WO2011077388A1 - Modification of enzymatic crosslinkers for controlling properties of crosslinked matrices - Google Patents
Modification of enzymatic crosslinkers for controlling properties of crosslinked matrices Download PDFInfo
- Publication number
- WO2011077388A1 WO2011077388A1 PCT/IB2010/056008 IB2010056008W WO2011077388A1 WO 2011077388 A1 WO2011077388 A1 WO 2011077388A1 IB 2010056008 W IB2010056008 W IB 2010056008W WO 2011077388 A1 WO2011077388 A1 WO 2011077388A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- matrix
- enzyme
- modified
- polymer
- peg
- Prior art date
Abstract
Description
Claims