WO2001080253A1 - Process for coating wire conductor - Google Patents
Process for coating wire conductor Download PDFInfo
- Publication number
- WO2001080253A1 WO2001080253A1 PCT/US2001/011856 US0111856W WO0180253A1 WO 2001080253 A1 WO2001080253 A1 WO 2001080253A1 US 0111856 W US0111856 W US 0111856W WO 0180253 A1 WO0180253 A1 WO 0180253A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- melt
- pigment
- fluoropolymer
- coating
- composition
- Prior art date
Abstract
Description
Claims