WO2000076914A2 - Process for the recovery of chlorine from iron chlorides - Google Patents
Process for the recovery of chlorine from iron chlorides Download PDFInfo
- Publication number
- WO2000076914A2 WO2000076914A2 PCT/US2000/015091 US0015091W WO0076914A2 WO 2000076914 A2 WO2000076914 A2 WO 2000076914A2 US 0015091 W US0015091 W US 0015091W WO 0076914 A2 WO0076914 A2 WO 0076914A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- jet
- feed stream
- reactor
- oxygen
- particles
- Prior art date
Abstract
Description
Claims