WO1999033921A9 - Grafted poly(ethylene oxide) compositions - Google Patents
Grafted poly(ethylene oxide) compositionsInfo
- Publication number
- WO1999033921A9 WO1999033921A9 PCT/US1998/027703 US9827703W WO9933921A9 WO 1999033921 A9 WO1999033921 A9 WO 1999033921A9 US 9827703 W US9827703 W US 9827703W WO 9933921 A9 WO9933921 A9 WO 9933921A9
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- peo
- poly
- ethylene oxide
- modified
- melt
- Prior art date
Abstract
Description
Claims