US20110259566A1 - Thermal conductive sheet - Google Patents
Thermal conductive sheet Download PDFInfo
- Publication number
- US20110259566A1 US20110259566A1 US13/016,507 US201113016507A US2011259566A1 US 20110259566 A1 US20110259566 A1 US 20110259566A1 US 201113016507 A US201113016507 A US 201113016507A US 2011259566 A1 US2011259566 A1 US 2011259566A1
- Authority
- US
- United States
- Prior art keywords
- thermal conductive
- conductive sheet
- epoxy resin
- good good
- boron nitride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A thermal conductive sheet contains a plate-like boron nitride particle. The thermal conductive sheet has a thermal conductivity in a direction perpendicular to the thickness direction of the thermal conductive sheet of 4 W/m·K or more. The thermal conductive sheet does not fall off from an adherend in the initial adhesion test (1) below:
Initial adhesion test (1):
The thermal conductive sheet is temporarily fixed on an adherend along the horizontal direction, and thereafter the adherend is turned over to be upside down. The maximum cutting resistance on the cutting blade at the time of cutting the thermal conductive sheet is 120 N/30 mm or less.
Description
- The present application claims priority from Japanese Patent Applications No. 2010-018256 filed on Jan. 29, 2010; No. 2010-090908 filed on Apr. 9, 2010; No. 2010-161850 filed on Jul. 16, 2010; and No. 2010-161854 filed on Jul. 16, 2010, the contents of which are hereby incorporated by reference into this application.
- 1. Field of the Invention
- The present invention relates to a thermal conductive sheet, to be specific, to a thermal conductive sheet for use in power electronics technology.
- 2. Description of Related Art
- In recent years, power electronics technology which uses semiconductor elements to convert and control electric power is applied in hybrid devices, high-brightness LED devices, and electromagnetic induction heating devices. In power electronics technology, a high current is converted to, for example, heat, and therefore materials that are disposed near the semiconductor element are required to have excellent heat dissipation characteristics (excellent heat conductivity).
- For example, Japanese Unexamined Patent Publication No. 2010-10469 has proposed covering a CPU with silicone resin, and then providing a heatsink so as to cover them.
- Also, for example, a thermal conductive sheet containing a plate-like boron nitride powder and an acrylic ester copolymer resin has been proposed (e.g., see Japanese Unexamined Patent Publication No. 2008-280496).
- In the thermal conductive sheet of Japanese Unexamined Patent Publication No. 2008-280496, the boron nitride powder is oriented so as to orient its major axis direction (direction perpendicular to the plate thickness of the boron nitride powder) in the thickness direction of the sheet, and thermal conductivity in the thickness direction of the thermal conductive sheet is improved in this way.
- However, the silicone adhesive of Japanese Unexamined Patent Publication No. 2010-10469 is disadvantageous in that heat generated from the CPU cannot be conducted to the heatsink efficiently.
- Another disadvantage of the silicone resin of Japanese Unexamined Patent Publication No. 2010-10469 is that when the silicone resin is applied to the CPU, positioning in relation to the CPU easily fails, failing to reliably fix the silicone resin to the CPU.
- However, there are cases where the thermal conductive sheet is required to have a high thermal conductivity in a direction (plane direction) perpendicular to the thickness direction depending on its use and purpose. In such a case, the thermal conductive sheet of
Patent Document 1 is disadvantageous in that the major axis direction of the boron nitride powder is perpendicular to (crossing) the plane direction, and therefore the thermal conductivity in the plane direction is insufficient. - Furthermore, such a thermal conductive sheet is usually processed into a predetermined shape by die cutting and the like, and therefore the thermal conductive sheet is required to have low brittleness, and required that no chipping or fracture is caused in the sheet at the time of die cutting.
- An object of the present invention is to provide a thermal conductive sheet that is excellent in thermal conductivity in the plane direction, and also excellent in initial adhesion.
- Another object of the present invention is to provide a thermal conductive sheet that is excellent in thermal conductivity in the plane direction, and also capable of achieving low brittleness.
- A thermal conductive sheet of the present invention contains a plate-like boron nitride particle, wherein the thermal conductivity in a direction perpendicular to the thickness direction of the thermal conductive sheet is 4 W/m·K or more, and the thermal conductive sheet does not fall off from an adherend in the initial adhesion test (1) below.
- Initial adhesion test (1): The thermal conductive sheet is temporarily fixed on an adherend along the horizontal direction, and thereafter the adherend is turned over to be upside down.
- The thermal conductive sheet of the present invention is excellent in thermal conductivity in the plane direction that is perpendicular to the thickness direction, and also excellent in adhesion (initial adhesion) to an adherend after being thermocompression bonded at a predetermined temperature.
- Therefore, by thermocompression bonding the thermal conductive sheet of the present invention to an adherend at a predetermined temperature, the thermal conductive sheet can be reliably fixed (temporarily fixed) on the adherend.
- Thus, the thermal conductive sheet allows the heat from the adherend to be reliably dissipated.
- The thermal conductive sheet of the present invention contains a plate-like boron nitride particle, wherein the thermal conductivity in a direction perpendicular to the thickness direction of the thermal conductive sheet is 4 W/m·K or more, and the maximum cutting resistance on the cutting blade is 120 N/30 mm or less at the time of cutting the thermal conductive sheet.
- The thermal conductive sheet of the present invention is excellent in thermal conductivity in the plane direction that is perpendicular to the thickness direction, and furthermore, the thermal conductive sheet of the present invention has a low maximum cutting resistance at the time of cutting, that is, brittleness is suppressed.
- Therefore, the thermal conductive sheet of the present invention can be applied in various heat dissipation uses as a thermal conductive sheet that can be easily processed, that is excellent in handleability, and that is excellent in thermal conductivity in the plane direction.
-
FIG. 1 shows a perspective view of an embodiment of a thermal conductive sheet of the present invention. -
FIG. 2 shows process drawings for describing a method for producing the thermal conductive sheet shown inFIG. 1 : - (a) illustrating a step of hot pressing a mixture or a laminated sheet,
- (b) illustrating a step of dividing the pressed sheet into a plurality of pieces, and
- (c) illustrating a step of laminating the divided sheets.
-
FIG. 3 shows a perspective view of a test device (Type I, before bend test) of a bend test. -
FIG. 4 shows a perspective view of a test device (Type I, during bend test) of a bend test. - A thermal conductive sheet of the present invention contains boron nitride particles.
- To be specific, the thermal conductive sheet contains boron nitride (BN) particles as an essential component, and further contains, for example, a resin component.
- The boron nitride particles are formed into a plate-like (or flake-like) shape, and are dispersed so as to be orientated in a predetermined direction (described later) in the thermal conductive sheet.
- The boron nitride particles have an average length in the longitudinal direction (maximum length in the direction perpendicular to the plate thickness direction) of, for example, 1 to 100 μm, or preferably 3 to 90 μm. The boron nitride particles have an average length in the longitudinal direction of, 5 μm or more, preferably 10 μm or more, more preferably 20 μm or more, even more preferably 30 μm or more, or most preferably 40 μm or more, and usually has an average length in the longitudinal direction of, for example, 100 μm or less, or preferably 90 μm or less.
- The average thickness (the length in the thickness direction of the plate, that is, the length in the short-side direction of the particles) of the boron nitride particles is, for example, 0.01 to 20 μm , or preferably 0.1 to 15 μm.
- The aspect ratio (length in the longitudinal direction/thickness) of the boron nitride particles is, for example, 2 to 10000, or preferably 10 to 5000.
- The average particle size of the boron nitride particles as measured by a light scattering method is, for example, 5 μm or more, preferably 10 μm or more, more preferably 20 μm or more, particularly preferably 30 μm or more, or most preferably 40 μm or more, and usually is 100 μm or less.
- The average particle size as measured by the light scattering method is a volume average particle size measured with a dynamic light scattering type particle size distribution analyzer.
- When the average particle size of the boron nitride particles as measured by the light scattering method is below the above-described range, the thermal conductive sheet may become fragile, and handleability may be reduced.
- The bulk density (JIS K 5101, apparent density) of the boron nitride particles is, for example, 0.3 to 1.5 g/cm3, or preferably 0.5 to 1.0 g/cm3.
- As the boron nitride particles, a commercially available product or processed goods thereof can be used. Examples of commercially available products of the boron nitride particles include the “PT” series (for example, “PT-110”) manufactured by Momentive Performance Materials Inc., and the “SHOBN®UH1” series (for example, “SHOBN®UHP-1”) manufactured by Showa Denko K.K.
- The resin component is a component that is capable of dispersing the boron nitride particles, i.e., a dispersion medium (matrix) in which the boron nitride particles are dispersed, including, for example, resin components such as a thermosetting resin component and a thermoplastic resin component.
- Examples of the thermosetting resin component include epoxy resin, thermosetting polyimide, phenol resin, urea resin, melamine resin, unsaturated polyester resin, diallyl phthalate resin, silicone resin, and thermosetting urethane resin.
- Examples of the thermoplastic resin component include polyolefin (for example, polyethylene, polypropylene, and ethylene-propylene copolymer), acrylic resin (for example, polymethyl methacrylate), polyvinyl acetate, ethylene-vinyl acetate copolymer, polyvinyl chloride, polystyrene, polyacrylonitrile, polyamide, polycarbonate, polyacetal, polyethylene terephthalate, polyphenylene oxide, polyphenylene sulfide, polysulfone, polyether sulfone, poly ether ether ketone, polyallylsulfone, thermoplastic polyimide, thermoplastic urethane resin, polyamino-bismaleimide, polyamide-imide, polyether-imide, bismaleimide-triazine resin, polymethylpentene, fluorine resin, liquid crystal polymer, olefin-vinyl alcohol copolymer, ionomer, polyarylate, acrylonitrile-ethylene-styrene copolymer, acrylonitrile-butadiene-styrene copolymer, and acrylonitrile-styrene copolymer,
- These resin components can be used alone or in combination of two or more.
- Of the resin components, preferably, the epoxy resin is used.
- The epoxy resin is in a state of liquid, semi-solid, or solid under normal temperature.
- To be specific, examples of the epoxy resin include aromatic epoxy resins such as bisphenol epoxy resin (e.g., bisphenol A epoxy resin, bisphenol F epoxy resin, bisphenol S epoxy resin, hydrogenated bisphenol A epoxy resin, dimer acid-modified bisphenol epoxy resin, and the like), novolak epoxy resin (e.g., phenol novolak epoxy resin, cresol novolak epoxy resin, biphenyl epoxy resin, and the like), naphthalene epoxy resin, fluorene epoxy resin (e.g., bisaryl fluorene epoxy resin and the like), and triphenylmethane epoxy resin (e.g., trishydroxyphenylmethane epoxy resin and the like); nitrogen-containing-cyclic epoxy resins such as triepoxypropyl isocyanurate (triglycidyl isocyanurate) and hydantoin epoxy resin; aliphatic epoxy resin; alicyclic epoxy resin (e.g., dicyclo ring-type epoxy resin and the like); glycidylether epoxy resin; and glycidylamine epoxy resin.
- These epoxy resins can be used alone or in combination of two or more.
- Preferably, a combination of a liquid epoxy resin and a solid epoxy resin is used, or more preferably, a combination of a liquid aromatic epoxy resin and a solid aromatic epoxy resin is used. Examples of such a combination include, to be more specific, a combination of a liquid bisphenol epoxy resin and a solid triphenylmethane epoxy resin, and a combination of a liquid bisphenol epoxy resin and a solid bisphenol epoxy resin.
- Preferably, a semi-solid epoxy resin is used alone, or more preferably, a semi-solid aromatic epoxy resin is used alone. Examples of those epoxy resins include, in particular, a semi-solid fluorene epoxy resin.
- A combination of a liquid epoxy resin and a solid epoxy resin, or a semi-solid epoxy resin can improve conformability to irregularities (described later) of the thermal conductive sheet.
- The epoxy resin has an epoxy equivalent of, for example, 100 to 1000 g/eqiv., or preferably 180 to 700 g/eqiv., and has a softening temperature (ring and ball test) of, for example, 80° C. or less (to be specific, 20 to 80° C.), or preferably 70° C. or less (to be specific, 25 to 70° C.).
- The epoxy resin has a melt viscosity at 80° C. of, for example, 10 to 20,000 mPa·s, or preferably 50 to 15,000 mPa·s. When two or more epoxy resins are used in combination, the melt viscosity of the mixture of these epoxy resins is set within the above-described range.
- Furthermore, when an epoxy resin that is solid under normal temperature and an epoxy resin that is liquid under normal temperature are used in combination, a first epoxy resin having a softening temperature of, for example, below 45° C., or preferably 35° C. or less, and a second epoxy resin having a softening temperature of, for example, 45° C. or more, or preferably 55° C. or more are used in combination. In this way, the kinetic viscosity (in conformity with JIS K 7233, described later) of the resin component (mixture) can be set to a desired range, and also, conformability to irregularities of the thermal conductive sheet can be improved.
- The epoxy resin can also be prepared as an epoxy resin composition containing, for example, an epoxy resin, a curing agent, and a curing accelerator.
- The curing agent is a latent curing agent (epoxy resin curing agent) that can cure the epoxy resin by heating, and examples thereof include an imidazole compound, an amine compound, an acid anhydride compound, an amide compound, a hydrazide compound, and an imidazoline compound. In addition to the above-described compounds, a phenol compound, a urea compound, and a polysulfide compound can also he used.
- Examples of the imidazole compound include 2-phenyl imidazole, 2-methyl imidazole, 2-ethyl-4-methyl imidazole, and 2-phenyl-4-methyl-5-hydroxymethyl imidazole.
- Examples of the amine compound include aliphatic polyamines such as ethylene diamine, propylene diamine, diethylene triamine, and triethylene tetramine; and aromatic polyamines such as metha phenylenediamine, diaminodiphenyl methane, and diaminodiphenyl sulfone.
- Examples of the acid anhydride compound include phthalic anhydride, maleic anhydride, tetrahydrophthalic anhydride, hexahydrophthalic anhydride, 4-methyl-hexahydrophthalic anhydride, methyl nadic anhydride, pyromelletic anhydride, dodecenylsuccinic anhydride, dichloro succinic anhydride, benzophenone tetracarboxylic anhydride, and chlorendic anhydride.
- Examples of the amide compound include dicyanodiamide and polyamide.
- An example of the hydrazide compound includes adipic acid dihydrazide.
- Examples of the imidazoline compound include methylimidazoline, 2-ethyl-4-methylimidazoline, ethylimidazoline, isopropylimidazoline, 2,4-dimethylimidazoline, phenylimidazoline, undecylimidazoline, heptadecylimidazoline, and 2-phenyl-4-methylimidazoline.
- These curing agents can be used alone or in combination of two or more.
- A preferable example of the curing agent is an imidazole compound.
- Examples of the curing accelerator include tertiary amine compounds such as triethylenediamine and tri-2,4,6-dimethylaminomethylphenol; phosphorus compounds such as triphenylphosphine, tetraphenylphosphonium tetraphenylborate, and tetra-n-butylphosphonium-o,o-diethylphosphorodithioate; a quaternary ammonium salt compound; an organic metal salt compound; and derivatives thereof. These curing accelerators can be used alone or in combination of two or more.
- In the epoxy resin composition, the mixing ratio of the curing agent is, for example, 0.5 to 50 parts by mass, or preferably 1 to 10 parts by mass per 100 parts by mass of the epoxy resin, and the mixing ratio of the curing accelerator is, for example, 0.1 to 10 parts by mass, or preferably 0.2 to 5 parts by mass per 100 parts by mass of the epoxy resin.
- The above-described curing agent, and/or the curing accelerator can be prepared and used, as necessary, as a solution, i.e., the curing agent and/or the curing accelerator dissolved in a solvent; and/or as a dispersion liquid, i.e., the curing agent and/or the curing accelerator dispersed in a solvent.
- Examples of the solvent include organic solvents including ketones such as acetone and methyl ethyl ketone, ester such as ethyl acetate, and amide such as N,N-dimethylformamide; and water-based solvents including water, and alcohols such as methanol, ethanol, propanol, and isopropanol. A preferable example is an organic solvent, more preferable examples are ketones and amides.
- Of the thermoplastic resin components, preferably, polyolefin is used.
- Preferable examples of polyolefin are polyethylene and ethylene-propylene copolymer.
- Examples of polyethylene include a low density polyethylene and a high density polyethylene.
- Examples of ethylene-propylene copolymer include a random copolymer, a block copolymer, or a graft copolymer of ethylene and propylene.
- These polyolefins can be used alone or in combination of two or more.
- The polyolefins have a weight average molecular weight and/or a number average molecular weight of, for example, 1000 to 10000.
- The polyolefin can be used alone, or can be used in combination.
- The resin component has a kinetic viscosity as measured in conformity with the kinetic viscosity test of JIS K 7233 (bubble viscometer method) (temperature: 25° C.±0.5° C., solvent: butyl carbitol, resin component (solid content) concentration: 40 mass %) of, for example, 0.22×104 to 2.00×104 m2/s, preferably 0.3×104 to 1.9×104 m2/s, or more preferably 0.4×10−4 to 1.8×104 m2/s. The above-described kinetic viscosity can also be set to, for example, 0.22×104 to 1.00×104 m2/s, preferably 0.3×104 to 0.9×104 m2/s, or more preferably 0.4×10−4 to 0.8×10−4 m2/s.
- When the kinetic viscosity of the resin component exceeds the above-described range, excellent flexibility and conformability to irregularities (described later) may not be given to the thermal conductive sheet. On the other hand, when the kinetic viscosity of the resin component is below the above-described range, boron nitride particles may not be oriented in a predetermined direction.
- In the kinetic viscosity test in conformity with JIS K 7233 (bubble viscometer method), the kinetic viscosity of the resin component is measured by comparing the bubble rising speed of a resin component sample with the bubble rising speed of criterion samples (having a known kinetic viscosity), and determining the kinetic viscosity of the criterion sample having a matching rising speed to be the kinetic viscosity of the resin component.
- In the thermal conductive sheet, the proportion of the volume-based boron nitride particle content (solid content, that is, the volume percentage of boron nitride particles relative to a total volume of the resin component and the boron nitride particles) is, for example, 35 vol % or more, preferably 60 vol % or more, or more preferably 75 vol % or more, and usually, for example, 95 vol % or less, or preferably 90 vol % or less.
- When the proportion of the volume-based boron nitride particle content is below the above-described range, the boron nitride particles may not be oriented in a predetermined direction in the thermal conductive sheet. On the other hand, when the proportion of the volume-based boron nitride particle content exceeds the above-described range, the thermal conductive sheet may become fragile, and handleability and conformability to irregularities may be reduced.
- The mixing ratio by mass of the boron nitride particles relative to 100 parts by mass of the total amount of the components (boron nitride particles and resin component)(total solid content) forming the thermal conductive sheet is, for example, 40 to 95 parts by mass, or preferably 65 to 90 parts by mass, and the mixing ratio by mass of the resin component relative to 100 parts by mass of the total amount of the components forming the thermal conductive sheet is, for example, 5 to 60 parts by mass, or preferably 10 to 35 parts by mass. The mixing ratio by mass of the boron nitride particles relative to 100 parts by mass of the resin component is, for example, 60 to 1900 parts by mass, or preferably 185 to 900 parts by mass.
- When two epoxy resins (a first epoxy resin and a second epoxy resin) are used in combination, the mass ratio (mass of the first epoxy resin/mass of the second epoxy resin) of the first epoxy resin relative to the second epoxy resin can be set appropriately in accordance with the softening temperature and the like of the epoxy resins (the first epoxy resin and the second epoxy resin). For example, the mass ratio of the first epoxy resin relative to the second epoxy resin is 1/99 to 9911, or preferably 10/90 to 90/10.
- In the resin component, in addition to the above-described components (polymer), for example, a polymer precursor (for example, a low molecular weight polymer including oligomer), and/or a monomer are contained.
-
FIG. 1 shows a perspective view of an embodiment of a thermal conductive sheet of the present invention, andFIG. 2 shows process drawings for describing a method for producing the thermal conductive sheet shown inFIG. 1 . - Next, a method for producing a thermal conductive sheet as an embodiment of the present invention is described with reference to
FIG. 1 andFIG. 2 . - In this method, first, the above-described components are blended at the above-described mixing ratio and are stirred and mixed, thereby preparing a mixture.
- In the stirring and mixing, in order to mix the components efficiently, for example, the solvent may be blended therein with the above-described components, or, for example, the resin component (preferably, the thermoplastic resin component) can be melted by heating.
- Examples of the solvent include the above-described organic solvents. When the above-described curing agent and/or the curing accelerator are prepared as a solvent solution and/or a solvent dispersion liquid, the solvent of the solvent solution and/or the solvent dispersion liquid can also serve as a mixing solvent for the stirring and mixing without adding a solvent during the stirring and mixing. Alternatively, in the stirring and mixing, a solvent can be further added as a mixing solvent.
- In the case when the stirring and mixing is performed using a solvent, the solvent is removed after the stirring and mixing.
- To remove the solvent, for example, the mixture is allowed to stand at room temperature for 1 to 48 hours; heated at 40 to 100° C. for 0.5 to 3 hours; or heated under a reduced pressure atmosphere of, for example, 0.001 to 50 kPa, at 20 to 60° C., for 0.5 to 3 hours.
- When the resin component is to be melted by heating, the heating temperature is, for example, a temperature in the neighborhood of or exceeding the softening temperature of the resin component, to be specific, 40 to 150° C., or preferably 70 to 140° C.
- Next, in this method, the obtained mixture is hot-pressed.
- To be specific, as shown in
FIG. 2( a), as necessary, for example, the mixture is hot-pressed with two releasing films 4 sandwiching the mixture, thereby producing a pressed sheet 1A. Conditions for the hot-pressing are as follows: a temperature of, for example, 50 to 150° C., or preferably 60 to 140° C.; a pressure of, for example, 1 to 100 MPa, or preferably 5 to 50 MPa; and a duration of, for example, 0.1 to 100 minutes, or preferably 1 to 30 minutes. - More preferably, the mixture is hot-pressed under vacuum. The degree of vacuum in the vacuum hot-pressing is, for example, 1 to 100 Pa, or preferably 5 to 50 Pa, and the temperature, the pressure, and the duration are the same as those described above for the hot-pressing.
- When the temperature, the pressure, and/or the duration in the hot-pressing is outside the above-described range, there is a case where a porosity P (described later) of the thermal
conductive sheet 1 cannot be adjusted to a desired value. - The pressed sheet 1A obtained by the hot-pressing has a thickness of for example, 50 to 1000 μm, or preferably 100 to 800 μm.
- Next, in this method, as shown in
FIG. 2( b), the pressed sheet 1A is divided into a plurality of pieces (for example, four pieces), thereby producing a dividedsheet 1B (dividing step). In the division of the pressed sheet 1A, the pressed sheet 1A is cut along the thickness direction so that the pressed sheet 1A is divided into a plurality of pieces when the pressed sheet 1A is projected in the thickness direction. The pressed sheet 1A is cut so that the respective dividedsheets 1B have the same shape when the dividedsheets 1B are projected in the thickness direction. - Next, in this method, as shown in
FIG. 2( c), the respective dividedsheets 1B are laminated in the thickness direction, thereby producing alaminated sheet 1C (laminating step). - Thereafter, in this method, as shown in
FIG. 2( a), thelaminated sheet 1C is hot-pressed (preferably hot-pressed under vacuum) (hot-pressing step). The conditions for the hot-pressing are the same as the conditions for the hot-pressing of the above-described mixture. - The thickness of the hot-pressed
laminated sheet 1C is, for example, 1 mm or less, or preferably 0.8 mm or less, and usually is, for example, 0.05 mm or more, or preferably 0.1 mm or more. - Thereafter, the series of the steps of the above-described dividing step (
FIG. 2( b)), laminating step (FIG. 2( c)), and hot-pressing step (FIG. 2( a)) are performed repeatedly, so as to allowboron nitride particles 2 to be efficiently oriented in a predetermined direction in theresin component 3 in the thermalconductive sheet 1. The number of the repetition is not particularly limited, and can be set appropriately according to the charging state of the boron nitride particles. The number of the repetition is, for example, 1 to 10 times, or preferably 2 to 7 times. - In the above-described hot-pressing step (
FIG. 2( a)), for example, a plurality of calendering rolls and the like can also be used for rolling the mixture and thelaminated sheet 1C. - The thermal
conductive sheet 1 can be obtained in this manner. - The thickness of the obtained thermal
conductive sheet 1 is, for example, 1 mm or less, or preferably 0.8 mm or less, and usually, for example, 0.05 mm or more, or preferably 0.1 mm or more. - In the thermal
conductive sheet 1, the proportion of the volume-based boron nitride particle content (solid content, that is, volume percentage of boron nitride particles relative to the total volume of the resin component and the boron nitride particles is, as described above, for example, 35 vol % or more (preferably 60 vol % or more, or more preferably 75 vol % or more), and usually 95 vol % or less (preferably 90 vol % or less). - When the proportion of the boron nitride particle content is below the above-described range, the
boron nitride particles 2 may not be oriented in a predetermined direction in the thermalconductive sheet 1. - When the
resin component 3 is the thermosetting resin component, for example, the series of the steps of the above-described dividing step (FIG. 2( b)), laminating step (FIG. 2( c)), and hot-pressing step (FIG. 2( a)) are performed repeatedly for an uncured thermalconductive sheet 1, thereby producing an uncured thermalconductive sheet 1 as is. - The thermal
conductive sheet 1 is in semi-cured (in B-stage) state when thermocompression bonded to the adherend to be described later, and the thermalconductive sheet 1 is cured by heat after the thermocompression bonding to the adherend. - To cure the thermal
conductive sheet 1 by heat, the above-described hot-press or a dryer is used. Preferably, a dryer is used. The conditions for the curing by heat are as follows: a temperature of, for example, 60 to 250° C., or preferably 80 to 200° C. - In the thus obtained thermal
conductive sheet 1, as shown inFIG. 1 and its partially enlarged schematic view, the longitudinal direction LD of theboron nitride particle 2 is oriented along a plane (surface) direction SD that crosses (is perpendicular to) the thickness direction TD of the thermalconductive sheet 1. - The calculated average of the angle formed between the longitudinal direction LD of the
boron nitride particle 2 and the plane direction SD of the thermal conductive sheet 1 (orientation angle a of theboron nitride particles 2 relative to the thermal conductive sheet 1) is, for example, 25 degrees or less, or preferably 20 degrees or less, and usually 0 degree or more. - The orientation angle a of the
boron nitride particle 2 relative to the thermalconductive sheet 1 is obtained as follows: the thermalconductive sheet 1 is cut along the thickness direction with a cross section polisher (CP); the cross section thus appeared is photographed with a scanning electron microscope (SEM) at a magnification that enables observation of 200 or moreboron nitride particles 2 in the field of view; a tilt angle α between the longitudinal direction LD of theboron nitride particle 2 and the plane direction SD (direction perpendicular to the thickness direction TD) of the thermalconductive sheet 1 is obtained from the obtained SEM photograph; and the average value of the tilt angles α is calculated. - The thus obtained thermal conductivity in the plane direction SD of the thermal
conductive sheet 1 is 4 W/m·K or more, preferably 5 Wm·K or more, more preferably 10 W/m·K or more, even more preferably 15 W/m·K or more, or particularly preferably 25 W/m·K or more, and usually 200 W/m·K or less. - The thermal conductivity in the plane direction SD of the thermal
conductive sheet 1 is substantially the same before and after the curing by heat when theresin component 3 is the thermosetting resin component. - When the thermal conductivity in the plane direction SD of the thermal
conductive sheet 1 is below the above-described range, thermal conductivity in the plane direction SD is insufficient, and therefore there is a case where the thermalconductive sheet 1 cannot be used for heat dissipation that requires thermal conductivity in such a plane direction SD. - The thermal conductivity in the plane direction SD of the thermal
conductive sheet 1 is measured by a pulse heating method. In the pulse heating method, the xenonflash analyzer “LFA-447” (manufactured by Erich NETZSCH GmbH & Co. Holding KG) is used. - The thermal conductivity in the thickness direction TD of the thermal
conductive sheet 1 is, for example, 0.5 to 15 W/m·K, or preferably 1 to 10 W/m·K. - The thermal conductivity in the thickness direction TD of the thermal
conductive sheet 1 is measured by a pulse heating method, a laser flash method, or a TWA method. In the pulse heating method, the above-described device is used, in the laser flash method, “TC-9000” (manufactured by Ulvac, Inc.) is used, and in the TWA method, “ai-Phase mobile” (manufactured by ai-Phase Co., Ltd) is used. - Thus, the ratio of the thermal conductivity in the plane direction SD of the thermal
conductive sheet 1 relative to the thermal conductivity in the thickness direction TD of the thermal conductive sheet 1 (thermal conductivity in the plane direction SD/thermal conductivity in the thickness direction TD) is, for example, 1.5 or more, preferably 3 or more, or more preferably 4 or more, and usually 20 or less. - Although not shown in
FIG. 1 , for example, pores (gaps) are formed in the thermalconductive sheet 1. - The proportion of the pores in the thermal
conductive sheet 1, that is, a porosity P, can he adjusted by setting the proportion of theboron nitride particle 2 content (volume-based), and further setting the temperature, the pressure, and/or the duration at the time of hot pressing the mixture of theboron nitride particle 2 and the resin component 3 (FIG. 2( a)). To be specific, the porosity P can be adjusted by setting the temperature, the pressure, and/or the duration of the hot pressing (FIG. 2( a)) within the above-described range. - The porosity P of the thermal
conductive sheet 1 is, for example, 30 vol % or less, or preferably 10 vol % or less. - The porosity P is measured by, for example, as follows: the thermal
conductive sheet 1 is cut along the thickness direction with a cross section polisher (CP); the cross section thus appeared is observed with a scanning electron microscope (SEM) at a magnification of 200 to obtain an image; the obtained image is binarized based on the pore portion and the non-pore portion; and the area ratio, i.e., the ratio of the pore portion area to the total area of the cross section of the thermalconductive sheet 1 is determined by calculation. - The thermal
conductive sheet 1 has a porosity P2 after curing of, relative to a porosity P1 before curing, for example, 100% or less, or preferably 50% or less. - For the measurement of the porosity P (P1), when the
resin component 3 is a thermosetting resin component, the thermalconductive sheet 1 before being cured by heat is used. - When the porosity P of the thermal
conductive sheet 1 is within the above-described range, the conformability to irregularities (described later) of the thermalconductive sheet 1 can be improved. - Meanwhile, the thermal
conductive sheet 1 does not fall off from the adherend in the initial adhesion test (1) below. That is, the temporarily fixed state between the thermalconductive sheet 1 and the adherend is kept. - Initial Adhesion Test (1): The thermal
conductive sheet 1 is thermocompression bonded on top of an adherend that is placed along a horizontal direction to be temporarily fixed thereon, allowed to stand for 10 minutes, and the adherend is turned over to be upside down. - Examples of the adherend include a substrate made of stainless steel (e.g., SUS 304 and the like), or a mounting substrate for notebook PC on which a plurality of electronic components such as IC (integrated circuit) chips, condensers, coils, and resistors are mounted. In the mounting substrate for notebook PC, the electronic components are usually disposed on the top face (one side) with a space provided therebetween in the plane direction (the plane direction of the mounting substrate for notebook PC).
- In pressure bonding, for example, while a sponge roll made of a resin such as silicone resin is pressed against the thermal
conductive sheet 1, the sponge roll is rolled on the surface of the thermalconductive sheet 1. - The temperature of the thermocompression bonding is, when the
resin component 3 is a thermosetting resin component (e.g., epoxy resin), for example, 80° C. - On the other hand, when the
resin component 3 is a thermoplastic resin component (e.g., polyethylene), the temperature of the thermocompression bonding is a temperature higher by 10 to 30° C. than the softening point or the melting point of the thermoplastic resin component; preferably a temperature higher by 15 to 25° C. than the softening point or the melting point of the thermoplastic resin component; more preferably, a temperature higher by 20° C. than the softening point or the melting point of the thermoplastic resin component; or to be specific, a temperature of 120° C. (that is, the softening point or the melting point of the thermoplastic resin component is 100° C., and the temperature higher by 20° C. than 100° C. is 120° C.). - When the thermal
conductive sheet 1 falls off from the adherend in the above-described initial adhesion test (1), that is, when the temporarily fixed state between the thermalconductive sheet 1 and the adherend is not kept, the thermalconductive sheet 1 cannot be reliably temporarily fixed to the adherend. - When the
resin component 3 is a thermosetting resin component, the thermalconductive sheet 1 to be tested in the initial adhesion test (1) and the initial adhesion test (2) (described later) is a thermalconductive sheet 1 before being cured, and the thermalconductive sheet 1 will be in B-stage based on the thermocompression bonding in the initial adhesion test (1) and the initial adhesion test (2). - When the
resin component 3 is a thermoplastic resin component, the thermalconductive sheet 1 to be tested in the initial adhesion test (1) and the initial adhesion test (2) (described later) is a solid thermalconductive sheet 1, and the thermalconductive sheet 1 will be softened based on the thermocompression bonding in the initial adhesion test (1) and the initial adhesion test (2). - Preferably, the thermal
conductive sheet 1 does not fall off from the adherend in both of the above-described initial adhesion test (1) and the initial adhesion test (2) described below. That is, the temporarily fixed state between the thermalconductive sheet 1 and the adherend is kept. - Initial Adhesion Test (2): The thermal
conductive sheet 1 is thermocompression bonded on top of an adherend that is placed along a horizontal direction to be temporarily fixed thereon, and then allowed to stand for 10 minutes, and thereafter, the adherend is disposed along a vertical direction (up-down directions). - The temperature in the thermocompression bonding of the Initial Adhesion Test (2) is the same as the temperature of thermocompression bonding in the Initial Adhesion Test (1).
- When the thermal
conductive sheet 1 is evaluated in the bend test in conformity with the cylindrical mandrel method of JIS K 5600-5-1 under the test conditions shown below, preferably, no fracture is observed. - Test Device:
Type 1 - Mandrel:
diameter 10 mm - Bending Angle: 90 degrees or more
- Thickness of the thermal conductive sheet 1: 0.3 mm
-
FIGS. 3 and 4 show perspective views of the Type I test device. In the following, the Type I test device is described. - In
FIGS. 3 and 4 , a Type I testdevice 10 includes a firstflat plate 11; a secondflat plate 12 disposed in parallel with the firstflat plate 11; and a mandrel (rotation axis) 13 provided for allowing the firstflat plate 11 and the secondflat plate 12 to rotate relatively. - The first
flat plate 11 is formed into a generally rectangular flat plate. Astopper 14 is provided at one end portion (free end portion) of the firstflat plate 11. Thestopper 14 is formed on the surface of the secondflat plate 12 so as to extend along the one end portion of the secondflat plate 12. - The second
flat plate 12 is formed into a generally rectangular flat plate, and one side thereof is disposed so as to be adjacent to one side (the other end portion (proximal end portion) that is opposite to the one end portion where thestopper 14 is provided) of the firstflat plate 11. - The
mandrel 13 is formed so as to extend along one side of the firstflat plate 11 and one side of the secondflat plate 12 that are adjacent to each other. - In the Type I test
device 10, as shown inFIG. 3 , the surface of the firstflat plate 11 is flush with the surface of the secondflat plate 12 before the start of the bend test. - To perform the bend test, the thermal
conductive sheet 1 is placed on the surface of the firstflat plate 11 and the surface of the secondflat plate 12. The thermalconductive sheet 1 is placed so that one side of the thermalconductive sheet 1 is in contact with thestopper 14. - Then, as shown in
FIG. 4 , the firstflat plate 11 and the secondflat plate 12 are rotated relatively. In particular, the free end portion of the firstflat plate 11 and the free end portion of the secondflat plate 12 are rotated to a predetermined angle with themandrel 13 as the center. To he specific, the firstflat plate 11 and the secondflat plate 12 are rotated so as to bring the surface of the free end portions thereof closer (oppose each other). - In this way, the thermal
conductive sheet 1 is bent with themandrel 13 as the center, conforming to the rotation of the firstflat plate 11 and the secondflat plate 12. - More preferably, no fracture is observed in the thermal
conductive sheet 1 even when the bending angle is set to 180 degrees under the above-described test conditions. - When the
resin component 3 is the thermosetting resin component, a semi-cured (in B-stage) thermal conductive sheet 1 (that is, the thermalconductive sheet 1 before being cured by heat) is tested in the bend test. - When the fracture is observed in the bend test at the above bending angle in the thermal
conductive sheet 1, there is a case where excellent flexibility and conformability to irregularities (described later) cannot be given to the thermalconductive sheet 1. - In the thermal
conductive sheet 1, the maximum cutting resistance on the cutting blade at the time of cutting is 120 N/30 mm or less. - When the maximum cutting resistance exceeds the above upper limit, brittleness of the thermal
conductive sheet 1 increases, and problems such as chipping and fracture at the time of processing are caused. - For the method for measuring the maximum cutting resistance, the method described in Japanese Unexamined Patent Publication No. 2003-181967 is used.
- To be specific, first, the thermal conductive sheet 1 (length 30 mm×width 50 mm) is die cut with a cutting blade (Thomson blade: MIR (manufactured by Nakayama Co., Ltd., blade angle: 43°, blade length: 40 mm, blade thickness: 0.71 mm, blade height: 23.6 mm) attached to a hydraulic press at a stroke of 30 SPM (stroke per minute) up to 70 μm relative to the faceplate (so that the blade edge enters (reaches) up to the depth of 70 μm from the top face of the faceplate that supports the bottom face of the thermal
conductive sheet 1 to the lower side (inwardly)), and the cutting resistance applied on the faceplate is measured using a load cell (time resolution: 500 Hz, load resolution: 9 mN, maximum measurement load: 3.6 kN, load capacity: 27 kN) and a computer at 23° C. - When the
resin component 3 in the thermalconductive sheet 1 is a thermosetting resin component, the maximum cutting resistance is the maximum cutting resistance of a semi-cured (in B-stage) thermal conductive sheet 1 (that is, a thermalconductive sheet 1 before being cured by heat). - Furthermore, for example, when the thermal
conductive sheet 1 is evaluated in the 3-point bending test in conformity with JIS K 7171 (2008) under the test conditions shown below, no fracture is observed. - Test piece: size 20 mm×15 mm
- Distance between supporting points: 5 mm
- Testing speed: 20 mm/min (indenter depressing speed)
- Bending angle: 120 degrees
- Evaluation method: Presence or absence of fracture such as cracks at the center of the test piece is observed visually when tested under the above-described test conditions.
- In the 3-point bending test, when the
resin component 3 is a thermosetting resin component, the thermalconductive sheet 1 before being cured by heat is used. - Therefore, the thermal
conductive sheet 1 is excellent in conformability to irregularities because no fracture is observed in the above-described 3-point bending test. The conformability to irregularities is, when the thermalconductive sheet 1 is provided on an object with irregularities (for example, on the above-described mounting substrate for notebook PC), a property of the thermalconductive sheet 1 that conforms to be in close contact with the irregularities (for example, irregularities formed by the above-described electronic components). - A mark such as, for example, letters and symbols can be given to the thermal
conductive sheet 1. That is, the thermalconductive sheet 1 is excellent in mark adhesion. The mark adhesion is a property of the thermalconductive sheet 1 that allows reliable adhesion of the above-described mark thereon. - The mark can be adhered (applied, fixed, or firmly fixed) to the thermal
conductive sheet 1, to be specific, by printing, engraving, or the like. - Examples of printing include, for example, inkjet printing, relief printing, intaglio printing, and laser printing.
- When the mark is to be printed by inkjet printing, relief printing, or intaglio printing, for example, an ink fixing layer for improving mark's fixed state can be provided on the surface (printing side) of the thermal
conductive sheet 1. - When the mark is to be printed by laser printing, for example, a toner fixing layer for improving marks fixed state can be provided on the surface (printing side) of the thermal
conductive sheet 1. - Examples of engraving include laser engraving and punching.
- Furthermore, the above-described thermal
conductive sheet 1 is excellent in thermal conductivity in the plane direction SD, and at the same time, excellent in adhesion (initial adhesion) to an adherend after thermocompression bonding at a predetermined temperature. - Thus, by thermocompression bonding the thermal
conductive sheet 1 to the adherend, the thermalconductive sheet 1 can be reliably fixed (temporarily fixed) to the adherend. - Thus, by temporarily fixing the thermal
conductive sheet 1 in B-stage to the adherend, and thereafter, curing the thermalconductive sheet 1 by heating, the thermal conductive sheet I can be reliably adhered to the adherend, and the thermalconductive sheet 1 allows the heat from the adherend to be conducted efficiently along the plane direction SD of the thermalconductive sheet 1. - The adherend is not particularly limited, and examples thereof also include, in addition to the above-described electronic components, light-emitting diodes.
- On the other hand, there is a case where it is desired to remove once the thermal
conductive sheet 1 for position adjustment as necessary after temporarily fixing the thermalconductive sheet 1 to the adherend, and bonded thereto again (reworking). In this case, the above-described thermalconductive sheet 1 is in B-stage, and reworkability is excellent. Thus, residue of the thermalconductive sheet 1 on the surface of the adherend can be prevented at the time of removing, and at the same time, reworking of the thermalconductive sheet 1 is easy. - Furthermore, even if the thermal
conductive sheet 1 remained on the surface of the adherend, because the thermalconductive sheet 1 is uncured (before being cured), the residue can be easily wiped off (removed). - Hereinafter, the present invention is described in further detail with reference to Examples. However, the present invention is not limited to those described in Examples.
- The components described below were blended, stirred, and allowed to stand at room temperature (23° C.) for one night, thereby allowing methyl ethyl ketone (dispersion medium for the curing agent) to volatilize and preparing a semi-solid mixture. The details of the components were as follows: 13.42 g of PT-110 (trade name, plate-like boron nitride particles, average particle size (light scattering method) 45 μm, manufactured by Momentive Performance Materials Inc.), 1.0 g of jER®828 (trade name, bisphenol A epoxy resin, first epoxy resin, liquid, epoxy equivalent 184 to 194 g/eqiv., softening temperature (ring and ball method) below 25° C., melt viscosity (80° C.) 70 mPa·s, manufactured by Japan Epoxy Resins Co., Ltd.), 2.0 g of EPPN-501HY (trade name, triphenylmethane epoxy resin, second epoxy resin, solid, epoxy equivalent 163 to 175 g/eqiv., softening temperature (ring and ball method) 57 to 63° C., manufactured by NIPPON KAYAKU Co., Ltd), and 3 g (solid content 0.15 g) (5 mass% per total amount of epoxy resins of jER®828 and EPPN-501HY) of a curing agent (a dispersion liquid of 5 mass% Curezol® 2P4MHZ-PW (trade name, manufactured by Shikoku Chemicals Corporation.) in methyl ethyl ketone).
- In the above-described blending, the volume percentage (vol %) of the boron nitride particles relative to the total volume of the solid content excluding the curing agent (that is, solid content of the boron nitride particle and epoxy resin) was 70 vol %.
- Then, the obtained mixture was sandwiched by two silicone-treated releasing films, and then these were hot-pressed with a vacuum hot-press at 80° C. under an atmosphere (vacuum atmosphere) of 10 Pa with a load of 5 tons (20 MPa) for 2 minutes. A pressed sheet having a thickness of 0.3 min was thus obtained (ref:
FIG. 2( a)). - Thereafter, the obtained pressed sheet was cut so as to be divided into a plurality of pieces when projected in the thickness direction of the pressed sheet. Divided sheets were thus obtained (ref:
FIG. 2( b)). Next, the divided sheets were laminated in the thickness direction, A laminated sheet was thus obtained (rcf:FIG. 2( c)). - Then, the obtained laminated sheet was hot-pressed under the same conditions as described above with the above-described vacuum hot-press (ref:
FIG. 2( a)). - Then, a series of the above-described operations of cutting, laminating, and hot-pressing (ref
FIG. 2 ) was repeated four times. A thermal conductive sheet (in uncured state) having a thickness of 0.3 mm was thus obtained. - A thermal conductive sheet was obtained in the same manner as in Example 1 in accordance with the mixing formulation and production conditions of Tables 1 to 3.
- The thermal conductivity of the thermal conductive sheets obtained in Examples 1 to 16 was measured.
- That is, the thermal conductivity in the plane direction (SD) was measured by a pulse heating method using a xenon flash analyzer “LFA-447” (manufactured by Erich NETZSCH GmbH & Co. Holding KG).
- The results are shown in Tables 1 to 3.
- Initial adhesion tests (1) and (2) were performed for adhesion of the thermal conductive sheets obtained in Examples 1 to 16 to a mounting substrate for notebook PC. On the mounting substrate, a plurality of electronic components are mounted.
- That is, the thermal conductive sheet was temporarily fixed to the surface (the side on which the electronic components are mounted) along the horizontal direction of the mounting substrate for notebook PC using a sponge roll made of silicone resin by thermocompression bonding at 80° C. (Examples 1 to 9 and Examples 11 to 16) or 120° C. (Example 10), and then allowed to stand for 10 minutes, and thereafter, the mounting substrate for notebook PC was disposed along the up-down directions (Initial Adhesion Test (2)).
- Afterwards, the mounting substrate for notebook PC was positioned so that the thermal conductive sheet faces downward (that is, turned over to be upside down from the position of the temporarily fixing) (Initial Adhesion Test (1)).
- Then, in the above-described Initial Adhesion Test (1) and Initial. Adhesion Test (2), the thermal conductive sheet was evaluated based on the criteria below. The results are shown in Tables 1 to 3.
- Good: It was confirmed that the thermal conductive sheet did not fall off from the mounting substrate for notebook PC.
- Bad: It was confirmed that the thermal conductive sheet fell off from the mounting substrate for notebook PC.
- Initial adhesion tests (1) and (2) were conducted in the same manner as described above for adhesion of the thermal conductive sheets obtained in Examples 1 to 16 to a stainless steel substrate (made of SUS 304).
- As a result, the thermal conductive sheets did not fall off from the stainless steel substrate in both of the initial adhesion tests (1) and (2).
- Then, in the above-described Initial Adhesion Test (1) and Initial Adhesion Test (2), the thermal conductive sheet was evaluated based on the criteria below. The results are shown in Tables 1 to 3.
- Good: It was confirmed that the thermal conductive sheet did not fall off from the stainless steel substrate.
- Bad: It was confirmed that the thermal conductive sheet fell off from the stainless steel substrate.
- The maximum cutting resistance on the cutting blade at the time of cutting the thermal conductive sheets obtained in Examples 1 to 16 was measured in accordance with the method described in Japanese Unexamined Patent Publication No.2003-181967.
- That is, the thermal conductive sheet (length 30 mm×width 50 mm) was die cut with a cutting blade (Thomson blade: MIR (manufactured by Nakayama Co., Ltd., blade angle: 43°, blade length: 40 mm, blade thickness: 0.71 mm, blade height: 23.6 mm) attached to a hydraulic press at a stroke of 30 SPM (stroke per minute), and up to 70 μm relative to the faceplate (so that the blade edge enters (reaches) up to the depth of 70 μm from the top face of the faceplate that supports the bottom face of the thermal conductive sheet to the lower side (inwardly)), and the cutting resistance applied on the faceplate was measured using a load cell (time resolution: 500 Hz, load resolution: 9 mN, maximum measurement load: 3.6 kN, load capacity: 27 kN) and a computer at 23° C.
- As a result, it was confirmed that the maximum cutting resistance on the cutting blade was 120 N/30 mm or less in any of the thermal conductive sheets obtained in Examples 1 to 16.
- Five types of Thomson die cut blades (manufactured by NISHIYAMA SEISAKUSHO CO., LTD.) shown below were prepared.
- (1) Rhombus (⋄): 10 ram square
- (2) Circular (◯): Diameter 23 mm
- (3) Circular (◯): Diameter 17 mm
- (4) Number Sign Shaped Rhombus (#): 6 mm square (3 columns×3 rows=9)
- (5) Number Sign Shaped Rhombus (#): 8 mm square (9 columns×9 rows=81)
- The thermal conductive sheets obtained in Examples 1 to 16 on a releasing film (polyethylene terephthalate film treated for release) were placed on rubber sheet, and were die cut using the above-described Thomson blades together with the releasing film as the support.
- As a result, no defect was caused in the thermal conductive sheets, and of the thermal conductive sheets obtained in Examples 1 to 16 and any of the blades used, no thermal conductive sheets stuck on the blades.
- After picking up the releasing film side by sucking and thermocompression bonding the thermal conductive sheet side on the mounting substrate, the releasing film was released and removed. At this time as well, no chipping or crumbling was caused in any of the thermal conductive sheets obtained in Examples 1 to 16.
- The thermal conductive sheets obtained in Examples 1 to 16 on a releasing film (polyethylene terephthalate film treated for release) were disposed on polystyrene sheet (Nippla sheet (product name), thickness: 0.3 mm, manufactured by Nihon Plastic), and allowed to be half-cut using the above-described Thomson die cut blades from the polystyrene sheet side so as not to cut the releasing film.
- As a result, no defect was caused in the thermal conductive sheets, and of the thermal conductive sheets obtained in Examples 1 to 16 and any of the blades used, no thermal conductive sheets stuck on the blades.
- In addition, because the releasing film was not cut, the sheet (the laminate of the releasing film that was not being die cut and the thermal conductive sheet thereon that was being die cut) was used as is and thermocompression bonded on the mounting substrate with the thermal conductive sheet side facing the mounting substrate, and thereafter, the releasing film was released and removed. At this time, in any of the thermal conductive sheets obtained in Examples 1 to 16, there was no problem of re-adhesion of cut pieces at the cutting end faces of the thermal conductive sheet, and transferring was easily performed.
- The porosity (P1) of the thermal conductive sheets before being cured by heat in Examples 1 to 16 was measured by the following measurement method.
- Measurement method of porosity: The thermal conductive sheet was cut along the thickness direction with a cross section polisher (CP); and the cross section thus appeared was observed with a scanning electron microscope (SEM) at a magnification of 200. The obtained image was binarized based on the pore portion and the non-pore portion; and the area ratio, i.e., the ratio of the pore portion area to the total area of the cross section of the thermal conductive sheet was calculated.
- The results are shown in Tables 1 to 3.
- The 3-point bending test in conformity with JIS K 7171 (2010) was carried out for the thermal conductive sheets obtained in Examples 1 to 16 with the following test conditions, thus evaluating conformability to irregularities with the following evaluation criteria. The results are shown in Tables 1 to 3.
- Test piece: size 20 mm×15 mm
- Distance between supporting points: 5 mm
- Testing speed: 20 mm/min (indenter depressing speed)
- Bending angle: 120 degrees
- (Evaluation Criteria)
- Excellent: No fracture was observed.
- Good: Almost no fracture was observed.
- Bad: Fracture was clearly observed.
- Marks were printed on the thermal conductive sheets of Examples 1 to 16 by inkjet printing and laser printing, and the mark was observed.
- As a result, it was confirmed that the mark was excellently visible in both cases of inkjet printing and laser printing, and that mark adhesion by printing was excellent in any of the thermal conductive sheets of Examples 1 to 16.
-
TABLE 1 Average Particle Size Example (μm) Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 Mixing Boron Nitride PT-110*1 45 13.42 3.83 5.75 12.22 23 — Formulation Particle/g*A/ [70] [40] [50] [68] [80] of [vol %]*B/ [69] [38.8] [48.8] [66.9] [79.2] Components [vol %]*C UHP-1*2 9 — — — — — 12.22 [68] [66.9] Polymer Thermosetting Epoxy Resin Epoxy Resin A*3 — 3 3 3 3 3 Resin Compositon (Semi-solid) Epoxy Resin B*4 1 — — — — — (Liquid) Epoxy Resin C*5 — — — — — — (Solid) Epoxy Resin D*6 2 — — — — — (Solid) Curing Agent*7 — 3 3 3 3 3 (Solid Content in Grams) (0.15) (0.15) (0.15) (0.15) (0.15) Curing Agent*8 3 — — — — — (Solid Content in Grams) (0.15) Thermoplastic Polyethylene*9 — — — — — — Resin Production Hot- Temperature (° C.) 80 80 80 80 80 80 Conditions pressing Number of Time (times)*D 5 5 5 5 5 5 Load (MPa)/(tons) 20/5 20/5 20/5 20/5 20/5 20/5 Evaluation Thermal Thermal Conductivity Plane Direction (SD) 30 4.5 6.0 30.0 32.5 17.0 Conductive (W/m · K) Thickness Direction (TD) 2.0 1.3 3.3 5.0 5.5 5.8 Sheet Ratio (SD/TD) 15.0 3.5 1.8 6.0 5.9 2.9 Initial Adhesion Test To Mounting Test Good Good Good Good Good Good Substrate for (1) Notebook PC Test Good Good Good Good Good Good (2) To Stainless Test Good Good Good Good Good Good Steel Substrate (1) Test Good Good Good Good Good Good (2) Maximum Cutting Resistance (N/30 mm) Good Good Good Good Good Good Workability in Die Cutting Test A Good Good Good Good Good Good Test B Good Good Good Good Good Good Porosity (vol %) 4 0 0 5 12 6 Conformability to Irregularities/3-point bending test Excellent Good Good Good Good Good JIS K 7171 (2008) Boron Nitride Orientation Angle (α)(degrees) 12 18 18 15 13 20 Particle g*A: Blended Weight [vol %]*B: Percentage relative to the total volume of the thermal conductive sheet (excluding curing agent) [vol %]*C: Percentage relative to the total volume of the thermal conductive sheet Number of Time*D: Number of times of hot-pressing of laminated sheet -
TABLE 2 Average Particle Size Example (μm) Ex. 7 Ex. 8 Ex. 9 Ex. 10 Ex. 11 Mixing Boron Nitride PT-110*1 45 12.22 12.22 12.22 3.83 13.42 Formulation Particle/g*A/ [68] [68] [68] [60] [70] of [vol %]*B/ [66.9] [66.9] [66.9] [60] [69] Components [vol %]*C UHP-1*2 9 — — — — — Polymer Thermosetting Epoxy Resin Epoxy Resin A*3 — — — — — Resin Compositon (Semi-solid) Epoxy Resin B*4 1.5 3 — — — (Liquid) Epoxy Resin C*5 1.5 — 3 — — (Solid) Epoxy Resin D*6 — — — — 3 (Solid) Curing Agent*7 3 3 3 — 3 (Solid Content in Grams) (0.15) (0.15) (0.15) (0.15) Curing Agent*8 — — — — — (Solid Content in Grams) Thermoplastic Polyethylene*9 — — — 1 — Resin Production Hot- Temperature (° C.) 80 80 80 120 80 Conditions pressing Number of Time (times)*D 5 5 5 5 5 Load (MPa)/(tons) 20/5 20/5 20/5 4/1 20/5 Evaluation Thermal Thermal Conductivity Plane Direction (SD) 30.0 30.0 30.0 20 24.5 Conductive (W/m · K) Thickness Direction (TD) 5.0 5.0 5.0 2.0 2.1 Sheet Ratio (SD/TD) 6.0 6.0 6.0 10.0 11.7 Initial Adhesion Test To Mounting Test Good Good Good Good Good Substrate for (1) Notebook PC Test Good Good Good Good Good (2) To Stainless Test Good Good Good Good Good Steel Substrate (1) Test Good Good Good Good Good (2) Maximum Cutting Resistance (N/30 mm) Good Good Good Good Good Workability in Die Cutting Test A Good Good Good Good Good Test B Good Good Good Good Good Porosity (vol %) 4 2 13 1 10 Conformability to Irregularities/3-point bending test Good Good Bad Bad Bad JIS K 7171 (2008) Boron Nitride Orientation Angle (α)(degrees) 15 16 16 15 16 Particle g*A: Blended Weight [vol %]*B: Percentage relative to the total volume of the thermal conductive sheet (excluding curing agent) [vol %]*C: Percentage relative to the total volume of the thermal conductive sheet Number of Time*D: Number of times of hot-pressing of laminated sheet -
TABLE 3 Average Particle Size Example (μm) Ex. 12 Ex. 13 Ex. 14 Ex. 15 Ex. 16 Mixing Boron Nitride PT-110*1 45 3.83 13.42 13.42 13.42 13.42 Formulation Particle/g*A/ [40] [70] [70] [70] [70] of [vol %]*B/ [37.7] [69] [69] [69] [69] Components [vol %]*C UHP-1*2 9 — — — — — Polymer Thermosetting Epoxy Resin Epoxy Resin A*3 3 3 3 3 3 Resin Compositon (Semi-solid) Epoxy Resin B*4 — — — — — (Liquid) Epoxy Resin C*5 — — — — — (Solid) Epoxy Resin D*6 — — — — — (Solid) Curing Agent*7 6 3 3 3 3 (Solid Content in Grams) (0.3) (0.15) (0.15) (0.15) (0.15) Curing Agent*8 — — — — — (Solid Content in Grams) Thermoplastic Polyethylene*9 — — — — — Resin Production Hot- Temperature (° C.) 80 60 70 80 80 Conditions pressing Number of Time (times)*D 5 5 5 5 5 Load (MPa)/(tons) 20/5 20/5 20/5 20/5 40/10 Evaluation Thermal Thermal Conductivity Plane Direction (SD) 4.1 10.5 11.2 32.5 50.7 Conductive (W/m · K) Thickness Direction (TD) 1.1 2.2 3.0 5.5 7.3 Sheet Ratio (SD/TD) 3.7 4.8 3.7 5.9 6.9 Initial Adhesion Test To Mounting Test Good Good Good Good Good Substrate for (1) Notebook PC Test Good Good Good Good Good (2) To Stainless Test Good Good Good Good Good Steel Substrate (1) Test Good Good Good Good Good (2) Maximum Cutting Resistance (N/30 mm) Good Good Good Good Good Workability in Die Cutting Test A Good Good Good Good Good Test B Good Good Good Good Good Porosity (vol %) 0 29 26 8 3 Conformability to Irregularities/3-point bending test Excellent Excellent Excellent Excellent Good JIS K 7171 (2008) Boron Nitride Orientation Angle (α)(degrees) 20 17 15 15 13 Particle g*A: Blended Weight [vol %]*B: Percentage relative to the total volume of the thermal conductive sheet (excluding curing agent) [vol %]*C: Percentage relative to the total volume of the thermal conductive sheet Number of Time*D: Number of times of hot-pressing of laminated sheet - In Tables 1 to 3, values for the components are in grams unless otherwise specified.
- In the rows of “boron nitride particles” in Tables 1 to 3, values on the top represent the Blended Weight (g) of the boron nitride particles; values in the middle represent the volume percentage (vol %) of the boron nitride particles relative to the total volume of the solid content excluding the curing agent in the thermal conductive sheet (that is, solid content of the boron nitride particles, and epoxy resin or polyethylene); and values at the bottom represent the volume percentage (vol %) of the boron nitride particles relative to the total volume of the solid content in the thermal conductive sheet (that is, solid content of boron nitride particles, epoxy resin, and curing agent).
- For the components with “*” added in Tables 1 to 3, details are given below.
- PT-110*1: trade name, plate-like boron nitride particles, average particle size (light scattering method) 45 μm, manufactured by Momentive Performance Materials Inc.
- IP-1*2: trade name: SHOBN®UHP-1, plate-like boron nitride particles, average particle size (light scattering method) 9 μm, manufactured by Showa Denko K.K.
- Epoxy Resin A*3: OGSOL EG (trade name), bisaryifluorene epoxy resin, semi-solid, epoxy equivalent 294 g/eqiv., softening temperature (ring and ball test) 47° C., melt viscosity (80° C.) 1360 mPa·s, manufactured by Osaka Gas Chemicals Co., Ltd.
- Epoxy Resin B*4: jER® 828 (trade name), bisphenol A epoxy resin, liquid, epoxy equivalent 184 to 194 g/eqiv., softening temperature (ring and ball test) below 25° C., melt viscosity (80° C.) 70 mPa·s, manufactured by Japan Epoxy Resins Co., Ltd.
- Epoxy Resin C*5: jER® 1002 (trade name), bisphenol A epoxy resin, solid, epoxy equivalent 600 to 700 g/eqiv., softening temperature (ring and ball test) 78° C., melt viscosity (80° C.) 10000 mPa·s or more (measurement limit or more), manufactured by Japan Epoxy Resins Co., Ltd.
- Epoxy Resin D*6: EPPN-501HY (trade name), triphenylmethane epoxy resin, solid, epoxy equivalent 163 to 175 g/eqiv., softening temperature (ring and ball test) 57 to 63° C., manufactured by NIPPON KAYAKU Co., Ltd.
- Curing Agent*7: a solution of 5 mass % Curezol® 2PZ (trade name, manufactured by Shikoku Chemicals Corporation) in methyl ethyl ketone.
- Curing Agent”: a dispersion of 5 mass % Curezol® 2P4MHZ-PW (trade name, manufactured by Shikoku Chemicals Corporation) in methyl ethyl ketone.
- Polyethylene*9: low density polyethylene, weight average molecular weight (Mw) 4000, number average molecular weight (Mn) 1700, melting point 100° C. to 105° C., manufactured by Sigma-Aldrich Co.
- While the illustrative embodiments of the present invention are provided in the above description, such is for illustrative purpose only and it is not to be construed as limiting the scope of the present invention. Modification and variation of the present invention that will be obvious to those skilled in the art is to be covered by the following claims.
Claims (2)
1. A thermal conductive sheet comprising a plate-like boron nitride particle, wherein
the thermal conductivity in a direction perpendicular to the thickness direction of the thermal conductive sheet is 4 W/m·K or more, and
the thermal conductive sheet does not fall off from an adherend in the initial adhesion test (1) below:
Initial Adhesion Test (1): The thermal conductive sheet is temporarily fixed on an adherend along a horizontal direction, and thereafter the adherend is turned over to be upside down.
2. A thermal conductive sheet comprising a plate-like boron nitride particle, wherein
the thermal conductivity in a direction perpendicular to the thickness direction of the thermal conductive sheet is 4 W/m·K or more, and
the maximum cutting resistance on a cutting blade at the time of cutting the thermal conductive sheet is 120 N/30 mm or less.