US20100119839A1 - System and Method for Forming a Thin-Film Phosphor Layer for Phosphor-Converted Light Emitting Devices - Google Patents
System and Method for Forming a Thin-Film Phosphor Layer for Phosphor-Converted Light Emitting Devices Download PDFInfo
- Publication number
- US20100119839A1 US20100119839A1 US12/617,673 US61767309A US2010119839A1 US 20100119839 A1 US20100119839 A1 US 20100119839A1 US 61767309 A US61767309 A US 61767309A US 2010119839 A1 US2010119839 A1 US 2010119839A1
- Authority
- US
- United States
- Prior art keywords
- phosphor
- layer
- phosphor powder
- polymer
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A thin-film phosphor layer can be formed by an improved deposition method involving: (1) forming a phosphor powder layer that is substantially uniformly deposited on a substrate surface; and (2) forming a polymer binder layer to fill gaps among loosely packed phosphor particles, thereby forming a substantially continuous layer of thin film.
Description
- This application claims the benefit of U.S. Provisional Application Ser. No. 61/114,198, filed on Nov. 13, 2008, the disclosure of which is incorporated herein by reference in its entirety.
- The invention relates generally to light emitting devices and more particularly to a thin-film phosphor deposition process for forming a thin-film phosphor layer adjacent to semiconductor light emitting devices.
- Solid-State Lighting through Light Emitting Diodes (SSL-LEDs) involves the use of solid-state, inorganic semiconductor light emitting diodes to produce white light for illumination. Like inorganic semiconductor transistors, which displaced vacuum tubes for computation, SSL-LED is a disruptive technology that has the potential to displace vacuum or gas tubes used in traditional incandescent or fluorescent lighting. Advantages of SSL-LEDs over conventional light sources include: (1) higher efficiency and associated energy savings; (2) better color rendering; (3) small form factor; (4) ruggedness; (5) longer operational lifetime and low maintenance; (6) environmentally friendly; and (7) low fabrication costs.
- Conventional LEDs typically generate monochromatic light with a narrow emission spectrum, and thus typically lack a broad emission spectrum to provide white light for illumination. In order to generate white light from an LED, a narrowband emission resulting from radiative recombination in the LED is transformed into broadband white light spectrum. Such broadband white light spectrum can be generated by three general approaches. A first approach is a wavelength-conversion approach by using an ultraviolet (“UV”) LED to excite multi-color phosphors that emit visible light at down-converted wavelengths. A second approach is a color-mixing approach by combining multiple LEDs, each of which generates light of a different color. A third approach is a hybrid between the two approaches described above. The current generation of commercially available white LEDs is primarily based on this hybrid approach. In particular, primary light emitted from a blue InGaN-based LED is mixed with a down-converted secondary light emitted from a pale-yellow YAG:Ce3+-based inorganic phosphor. The combination of partially transmitted blue and re-emitted yellow light gives the appearance of cool (green-blue) white light. Thus, phosphor coating technology is involved for white LEDs using either the wavelength-conversion approach or the hybrid approach.
- Current approaches for phosphor coating are described next. A first approach, as depicted in
FIG. 1A , is a slurry method involving the use of phosphor grains orparticles 1 blended in a liquid polymer system, such as polypropylene, polycarbonate, epoxy resin, or silicone resin. The mixed phosphor slurry is dispensed on or surrounding anLED chip 2, and then the liquid polymer system is dried or cured. TheLED chip 2 along with the phosphor slurry can be disposed in areflector cup 3, as depicted inFIG. 1A . While the slurry method is a convenient phosphor dispensing method, a resulting color uniformity of LEDs manufactured with this slurry method is typically unsatisfactory, and colored rings can be observed from different viewing angles. These deficiencies are the result of: (1) variations in the thickness of a phosphor-containing material surrounding an LED chip can lead to various lengths of optical paths before an emitted light escapes a package; and (2) non-uniform phosphor distribution within the phosphor-containing material (because of gravity and buoyancy effects) tends to move larger phosphor particles downward during a liquid polymer curing process. Moreover, due to variations in the quantity of phosphor powders dispensed surrounding the LED chip, a white color coordinate tends to vary from device to device. These color variations, in turn, result in a complicated white LED color sorting process, the so-called color binning, which attempts to manage the color variations by sorting each device according to its white color coordinate. - To measure the uniformity of emitted light, the variation in a Correlated Color Temperature (“CCT”) can be used. A color temperature of a light emitting device can be determined by comparing its hue with a theoretical, heated blackbody radiator. A temperature, expressed in terms of degrees Kelvin, at which the heated blackbody radiator matches the hue of the light emitting device is that device's color temperature. An incandescent light source can be close to being a blackbody radiator, but many other light emitting devices do not emit radiation in the form of a blackbody curve and are, therefore, assigned a CCT. A CCT of a light emitting device is a color temperature of a blackbody radiator that most closely matches the device's perceived color. The higher the Kelvin rating, the “cooler” or more blue the light. The lower the Kelvin rating, the “warmer” or more yellow the light. By measuring the CCT at different light emission angles and comparing this variation among different light emitting devices, the uniformity of the light produced can be quantified. A blue LED chip dispensed with a yellow phosphor by the slurry method can have a typical CCT that varies from about 5,800 K to about 7,200 K across a range of 1,400 K for light emission angles at ±70° from a center light-emitting axis of the LED. Because of the presence of colored rings, the CCT is typically higher at or near the center axis than in the periphery, where the emitted light tends to be more yellow.
- A second phosphor coating method is an Electrophoretic Deposition (“EPD”) method for the manufacture of phosphor-converted white LEDs, as depicted in
FIG. 1B . In the case of EPD, a phosphor is electrically charged by adding a proper amount of an electrolyte in a liquid solvent to form a liquid suspension, and is biased by an electrical field. Then, surface charged phosphor particles are moved to an electrode of counter-polarity and coated on the electrode. EPD of the phosphor particles creates aphosphor layer 4 of relatively uniform thickness that can produce white light of greater uniformity and reduced instances of colored rings. While achieving greater color uniformity, the EPD method is generally lacking in its ability to deposit phosphors directly over an electrically nonconductive surface. In commercial production, a phosphor layer is typically coated directly over aLED chip 5, according to the so-called proximate phosphor configuration. This configuration tends to be inefficient in terms of light scattering, since the proximate phosphor layer can direct about 60% of total white light emission back towards theLED chip 5, where high loss can occur. Another drawback of the EPD method is that certain phosphors are susceptible to degradation by the solvent, thereby limiting the general applicability of the EPD method. - More recently and as depicted in
FIG. 2 , another approach involves forming a luminescentceramic plate 6 by heating phosphor particles at high pressure until surfaces of the phosphor particles begin to soften and melt. The partially melted particles can stick together to form theceramic plate 6 including a rigid agglomerate of the particles. The luminescentceramic plate 6 is disposed in a path of light emitted by anLED chip 7, which is disposed over a set ofelectrodes 8. While providing benefits in terms of robustness, reduced sensitivity to temperature, and reduced color variations from chip to chip, a resulting package efficiency can be unsatisfactory due to the proximate phosphor configuration. - A scattering efficiency (also sometimes referred to as a package efficiency) is typically between 40% to 60% for commercially available white LEDs, with efficiency losses due to light absorption by internal package components such as an LED chip, a lead frame, or sub-mount.
FIG. 3 depicts an example of a phosphor-converted white LED withyellow phosphor 31 powered by ablue LED chip 32, where a primaryblue light 34 undergoing color mixing with a secondary light 35 of yellow color to generate a white color. A main source of light loss results from absorption of light by theLED chip 32. Because theLED chip 32 is typically formed of high-refractive index materials, photons tend to be trapped within theLED chip 32 due to Total Internal Reflection (“TIR”) once the photons strike and enter theLED chip 32. Another potential source of light loss results from imperfections in amirror reflector 33 in the LED package. - Several scenarios depicted in
FIG. 3 can direct light to the highlyabsorbent LED chip 32. First, aprimary light 36 emitted by theLED chip 32 can be reflected back to thechip 32 by thephosphor powders 31 or by themirror reflector 33. Second, down-convertedsecondary light 37 emitted by thephosphor powders 31 can scatter backward towards theLED chip 32. Third, both primary light and secondary light 38 can be reflected back towards thechip 32 due to TIR at an air-LED package interface. To improve the probability of light escaping from the package, ahemispheric lens 39 can be used to reduce instances of TIR at the air-package interface. To reduce instances of backward scattered light striking theLED chip 32, thephosphor powders 31 desirably should not be placed directly over the chip surface, but rather should be placed at a certain distance from theLED chip 32. Furthermore, a thinner phosphor layer would reduce instances of backward scattering of secondary light by thephosphor powders 31. - It is against this background that a need arose to develop the thin-film phosphor deposition process and related devices and systems described herein.
- Certain embodiments of the invention relate to the formation of a thin-film phosphor layer of substantially uniform thickness that can be conformally disposed in an optical path of an LED, thereby producing substantially uniform white light with little or no colored rings. This thin-film phosphor layer can be prepared by an improved deposition method involving: (1) forming a phosphor powder layer that is substantially uniformly deposited on a substrate surface; and (2) forming a polymer binder layer to fill gaps among loosely packed phosphor particles, thereby forming a substantially continuous, thin-film phosphor layer. Phosphor conversion efficiency of the thin-film phosphor layer can be significantly improved because a thinner layer of a precisely controlled quantity of phosphor powders can be disposed in an optical path, thereby reducing light scattering losses. Also, color homogeneity of the thin-film phosphor layer can be significantly improved due to substantially uniform deposition of phosphor particles. One method of forming an uniform, thin-film phosphor layer is to introduce electrostatic charges among phosphor particles during deposition of the phosphor particles. The electrostatic charges among the phosphor particles can self-balance and adjust their distribution, thereby promoting a substantially uniform distribution of the phosphor particles. Another method of forming an uniform, thin-film phosphor layer is through a phosphor dispensing mechanism, such as a showerhead mechanism in a deposition chamber, or through a rotational substrate holding mechanism, such as a turn table that holds a substrate. In addition to improved efficiency and color homogeneity, temperature stability of the thin-film phosphor layer can be significantly improved because the polymer binder layer can be thermally stable up to at least about 300° C. or more.
- Advantageously, white color consistency can be maintained in a tight color coordinate by a coating process with precisely controlled quantities of deposited phosphor particles through a phosphor powder delivery mechanism. White color rendering can be precisely tuned with a layer-by-layer sequential deposition of multi-color phosphors, such as deposition of a red phosphor layer, deposition of a green phosphor layer, and then deposition of a blue phosphor layer. The ratio of multi-color phosphors can be precisely controlled in a resulting composite multi-color phosphor film stack. Thus, the color coordinate and CCT of a white LED fabricated by the phosphor thin-film process can be precisely controlled. This, in turn, can significantly simplify (or even avoid) a binning process.
- According to some embodiments of the invention, a consistent white color coordinate can be achieved from lightly varied blue LED chips by tuning the dosage of a multi-color phosphor film stack. This color compensation method can compensate for color variations of the blue LED chips using different compositions or amounts of phosphor contents. In such manner, white LED yield can be significantly increased for color sensitive applications, such as display backlighting using white LEDs.
- According to one embodiment of the invention, a thin-film phosphor coating method is a batch phosphor coating process. Multiple LED chips can be deposited with thin-film phosphor in one coating operation. According to another embodiment of the invention, multiple LED lenses can be deposited with thin-film phosphor in one coating operation. Similar to semiconductor chip manufacturing, a manufacturing cost per LED chip can be significantly reduced, and a manufacturing throughput can be significantly increased by a batch process.
- As contrasted to EPD, deposition of a thin-film phosphor layer can be used to form conformal thin-film phosphor layers directly over an electrically nonconductive surface. The conformal thin-film phosphor also can be deposited on a non-flat surface, such as a convex or concave surface of an LED lens.
- Some embodiments of the invention relate to a system for depositing a conformal thin-film phosphor layer on a substrate. The system can include a deposition chamber, a phosphor powder delivery subsystem, and a polymer precursor delivery subsystem configured to deliver a gas phase monomer to the deposition chamber. The system also can include a memory and a processor in electrical communication with the deposition chamber, the phosphor powder delivery subsystem, and the polymer precursor delivery subsystem, wherein the memory can include code or instructions stored therein and executable by the processor to form a thin-film phosphor layer.
- One specific embodiment of the invention relates to a method of forming a thin-film phosphor layer for use in a light emitting device. The method includes: (1) transporting, using a carrier gas, a phosphor powder from a source of the phosphor powder to a deposition chamber; and (2) depositing the phosphor powder adjacent to a substrate within the deposition chamber so as to substantially uniformly distribute the phosphor powder adjacent to a surface of the substrate.
- Another specific embodiment of the invention also relates to a method of forming a thin-film phosphor layer for use in a light emitting device. The method includes: (1) forming a first phosphor powder layer adjacent to a substrate, the first phosphor powder layer including first phosphor particles that are distributed adjacent to a surface of the substrate; and (2) forming, via vapor deposition, a first polymer layer adjacent to the first phosphor powder layer, the first polymer layer serving as a binder for the first phosphor particles.
- Another specific embodiment of the invention relates to a system to form a thin-film phosphor layer on a substrate. The system includes: (1) a deposition subsystem defining an enclosure to accommodate the substrate; (2) a phosphor powder delivery subsystem configured to deliver, using a carrier gas, a phosphor powder from a source of the phosphor powder to the deposition subsystem; (3) a polymer precursor delivery subsystem configured to deliver polymer precursors in a vapor phase to the deposition subsystem; and (4) a control subsystem connected to the deposition subsystem, the phosphor powder delivery subsystem, and the polymer precursor delivery subsystem, wherein the control subsystem is configured to control the phosphor powder delivery subsystem to deliver the phosphor powder to the deposition subsystem for a first time interval to form a phosphor powder layer adjacent to the substrate, and the control subsystem is configured to control the polymer precursor delivery subsystem to deliver the polymer precursors to the deposition subsystem for a second time interval to form a polymer layer adjacent to the phosphor powder layer.
- Another specific embodiment of the invention relates to a light emitting device, which includes: (1) a substrate; (2) a phosphor powder layer substantially uniformly distributed adjacent to the substrate; and (3) a parylene-based polymer layer conformally deposited adjacent to the phosphor powder layer as a binder material to form a substantially continuous thin film, wherein the phosphor powder layer includes a single-color phosphor.
- A further specific embodiment of the invention relates to a light emitting device, which includes: (1) a substrate; (2) multiple phosphor powder layers substantially uniformly distributed adjacent to the substrate, the phosphor powder layers being configured to emit light of different colors; and (3) multiple parylene-based polymer layers, each of the parylene-based polymer layers being conformally deposited adjacent to a respective one of the phosphor powder layers, each of the parylene-based polymer layers being a binder material for a respective one of the phosphor powder layers to fill voids among constituent phosphor particles.
- Other aspects and embodiments of the invention are also contemplated. The foregoing summary and the following detailed description are not meant to restrict the invention to any particular embodiment but are merely meant to describe some embodiments of the invention.
- For a better understanding of the nature and objects of some embodiments of the invention, reference should be made to the following detailed description taken in conjunction with the accompanying drawings.
-
FIG. 1A depicts a proximate phosphor-in-cup configuration of a conventional white LED formed using a slurry method. -
FIG. 1B depicts a proximate phosphor configuration of a conventional white LED formed using EPD. -
FIG. 2 depicts a proximate phosphor configuration of a conventional white LED formed by lamination with a luminescent ceramic plate. -
FIG. 3 depicts sources of light losses resulting from light scattering by phosphor powders, TIR at material interfaces, and light absorption at a surface of an LED. -
FIG. 4 is a flow diagram depicting a method of forming a conformal, thin-film phosphor layer, according to an embodiment of the invention. -
FIG. 5 is a flow diagram depicting a method of depositing a substantially uniformly distributed phosphor layer, according to an embodiment of the invention. -
FIG. 6A throughFIG. 6D depict examples of a family of polymers that can be used as binder materials to form thin-film phosphor layers, according to an embodiment of the invention. -
FIG. 7A depicts a single-color thin-film phosphor layer formed using a conformal, thin-film phosphor deposition process, according to an embodiment of the invention. -
FIG. 7B depicts a multi-color thin-film phosphor composite layer formed using a conformal thin-film phosphor deposition process, according to an embodiment of the invention. -
FIG. 8 depicts a system for depositing a conformal, thin-film phosphor layer on a substrate, according to an embodiment of the invention. - The following definitions apply to some of the aspects described with respect to sonic embodiments of the invention. These definitions may likewise be expanded upon herein.
- As used herein, the singular terms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to a layer can include multiple layers unless the context clearly dictates otherwise.
- As used herein, the term “set” refers to a collection of one or more components. Thus, for example, a set of layers can include a single layer or multiple layers. Components of a set also can be referred to as members of the set. Components of a set can be the same or different. In some instances, components of a set can share one or more common characteristics.
- As used herein, the term “adjacent” refers to being near or adjoining. Adjacent components can be spaced apart from one another or can be in actual or direct contact with one another. In some instances, adjacent components can be connected to one another or can be formed integrally with one another.
- As used herein, the terms “connect,” “connected,” and “connection” refer to an operational coupling or linking. Connected components can be directly coupled to one another or can be indirectly coupled to one another, such as via another set of components.
- As used herein, the terms “substantially” and “substantial” refer to a considerable degree or extent. When used in conjunction with an event or circumstance, the terms can refer to instances in which the event or circumstance occurs precisely as well as instances in which the event or circumstance occurs to a close approximation, such as accounting for typical tolerance levels of the manufacturing operations described herein.
- As used herein, the terms “electrically conductive” and “electrical conductivity” refer to an ability to transport an electric current, while the terms “electrically nonconductive” and “electrical nonconductivity” refer to a lack of ability to transport an electric current. Electrically conductive materials typically correspond to those materials that exhibit little or no opposition to flow of an electric current, while electrically nonconductive materials typically correspond to those materials within which an electric current has little or no tendency to flow. One measure of electrical conductivity (or electrical nonconductivity) is in terms of Siemens per meter (“S·m−1”). Typically, an electrically conductive material is one having a conductivity greater than about 104 S·m−1, such as at least about 105 S·m−1 or at least about 106 S·m−1, while an electrically nonconductive material is one having a conductivity less than about 104 S·m−1 such as less than or equal to about 103 S·m−1 or less than or equal to about 102 S·m−1. Electrical conductivity (or electrical nonconductivity) of a material can sometimes vary with temperature. Unless otherwise specified, electrical conductivity (or electrical nonconductivity) of a material is defined at room temperature.
- As used herein with respect to photoluminescence, the term “quantum efficiency” refers to a ratio of the number of output photons to the number of input photons.
- As used herein, the term “size” refers to a characteristic dimension. In the case of a particle that is spherical, a size of the particle can refer to a diameter of the particle. In the case of a particle that is non-spherical, a size of the particle can refer to an average of various orthogonal dimensions of the particle. Thus, for example, a size of a particle that is a spheroidal can refer to an average of a major axis and a minor axis of the particle. When referring to a set of particles as having a particular size, it is contemplated that the particles can have a distribution of sizes around that size. Thus, as used herein, a size of a set of particles can refer to a typical size of a distribution of sizes, such as an average size, a median size, or a peak size.
- As used herein, the term “alkane” refers to a saturated hydrocarbon molecule. For certain applications, an alkane can include from 1 to 100 carbon atoms. The term “lower alkane” refers to an alkane that includes from 1 to 20 carbon atoms, such as, for example, from 1 to 10 carbon atoms, while the term “upper alkane” refers to an alkane that includes more than 20 carbon atoms, such as, for example, from 21 to 100 carbon atoms. The term “branched alkane” refers to an alkane that includes one or more branches, while the term “unbranched alkane” refers to an alkane that is straight-chained. The term “cycloalkane” refers to an alkane that includes one or more ring structures. The term “heteroalkane” refers to an alkane that has one or more of its carbon atoms replaced by one or more heteroatoms, such as, for example, N, Si, S, O, and P. The term “substituted alkane” refers to an alkane that has one or more of its hydrogen atoms replaced by one or more substituent groups, such as, for example, halo groups, hydroxy groups, alkoxy groups, carboxy groups, thio groups, alkylthio groups, cyano groups, nitro groups, amino groups, alkylamino groups, dialkylamino groups, silyl groups, and siloxy groups, while the term “un-substituted alkane” refers to an alkane that lacks such substituent groups. Combinations of the above terms can be used to refer to an alkane having a combination of characteristics. For example, the term “branched lower alkane” can be used to refer to an alkane that includes from 1 to 20 carbon atoms and one or more branches. Examples of alkanes include methane, ethane, propane, cyclopropane, butane, 2-methylpropane, cyclobutane, and charged, hetero, or substituted forms thereof.
- As used herein, the term “alkyl group” refers to a monovalent form of an alkane. For example, an alkyl group can be envisioned as an alkane with one of its hydrogen atoms removed to allow bonding to another group of a molecule. The term “lower alkyl group” refers to a monovalent form of a lower alkane, while the term “upper alkyl group” refers to a monovalent form of an upper alkane. The term “branched alkyl group” refers to a monovalent form of a branched alkane, while the term “unbranched alkyl group” refers to a monovalent form of an unbranched alkane. The term “cycloalkyl group” refers to a monovalent form of a cycloalkane, and the term “heteroalkyl group” refers to a monovalent form of a heteroalkane. The term “substituted alkyl group” refers to a monovalent form of a substituted alkane, while the term “un-substituted alkyl group” refers to a monovalent form of an unsubstituted alkane. Examples of alkyl groups include methyl, ethyl, n-propyl, isopropyl, cyclopropyl, butyl, isobutyl, t-butyl, cyclobutyl, and charged, hetero, or substituted forms thereof.
- As used herein, the term “arene” refers to an aromatic hydrocarbon molecule. For certain applications, an arene can include from 5 to 100 carbon atoms. The term “lower arene” refers to an arene that includes from 5 to 20 carbon atoms, such as, for example, from 5 to 14 carbon atoms, while the term “upper arene” refers to an arene that includes more than 20 carbon atoms, such as, for example, from 21 to 100 carbon atoms. The term “monocyclic arene” refers to an arene that includes a single aromatic ring structure, while the term “polycyclic arene” refers to an arene that includes more than one aromatic ring structure, such as, for example, two or more aromatic ring structures that are bonded via a carbon-carbon single bond or that are fused together. The term “heteroarene” refers to an arene that has one or more of its carbon atoms replaced by one or more heteroatoms, such as, for example, N, Si, S, O, and P. The term “substituted arene” refers to an arene that has one or more of its hydrogen atoms replaced by one or more substituent groups, such as, for example, alkyl groups, alkenyl groups, alkynyl groups, iminyl groups, halo groups, hydroxy groups, alkoxy groups, carboxy groups, thio groups, alkylthio groups, cyano groups, nitro groups, amino groups, alkylamino groups, dialkylamino groups, silyl groups, and siloxy groups, while the term “un-substituted arene” refers to an arene that lacks such substituent groups. Combinations of the above terms can be used to refer to an arene having a combination of characteristics. For example, the term “monocyclic lower alkene” can be used to refer to an arene that includes from 5 to 20 carbon atoms and a single aromatic ring structure. Examples of arenes include benzene, biphenyl, naphthalene, pyridine, pyridazine, pyrimidine, pyrazine, quinoline, isoquinoline, and charged, hetero, or substituted forms thereof.
- As used herein, the term “aryl group” refers to a monovalent form of an arene. For example, an aryl group can be envisioned as an arene with one of its hydrogen atoms removed to allow bonding to another group of a molecule. The term “lower aryl group” refers to a monovalent form of a lower arene, while the term “upper aryl group” refers to a monovalent form of an upper arene. The term “monocyclic aryl group” refers to a monovalent form of a monocyclic arene, while the term “polycyclic aryl group” refers to a monovalent form of a polycyclic arene. The term “heteroaryl group” refers to a monovalent form of a heteroarene. The term “substituted aryl group” refers to a monovalent form of a substituted arene, while the term “un-substituted arene group” refers to a monovalent form of an unsubstituted arene. Examples of aryl groups include phenyl, biphenylyl, naphthyl, pyridinyl, pyridazinyl, pyrimidinyl, pyrazinyl, quinolyl, isoquinolyl, and charged, hetero, or substituted forms thereof.
- As used herein, the term “arylene group” refers to a bivalent form of an arene. For example, an arylene group can be envisioned as an arene with two of its hydrogen atoms removed to allow bonding to one or more additional groups of a molecule. The term “lower arylene group” refers to a bivalent form of a lower arene, while the term “upper arylene group” refers to a bivalent form of an upper arene. The term “monocyclic arylene group” refers to a bivalent form of a monocyclic arene, while the term “polycyclic arylene group” refers to a bivalent form of a polycyclic arene. The term “heteroarylene group” refers to a bivalent form of a heteroarene. The term “substituted arylene group” refers to a bivalent form of a substituted arene, while the term “un-substituted arylene group” refers to a bivalent form of an unsubstituted arene. Examples of arylene groups include phenylene, biphenylylene, naphthylene, pyridinylene, pyridazinylene, pyrimidinylene, pyrazinylene, quinolylene, isoquinolylene, and charged, hetero, or substituted forms thereof.
- Certain embodiments of the invention relate to a thin-film conformal phosphor deposition process for phosphor-converted white LEDs. This process facilitates achieving the goal of increasing light scattering efficiency for white LEDs by providing a thin-film and remote phosphor layer configuration. According to the improved process as depicted in
FIG. 4 , a thin-film phosphor layer can be substantially uniformly and conformally deposited on a flat or non-flat and electrically conductive, semiconductive, or nonconductive surface by two operations: (1) forming a phosphor powder layer that is substantially uniformly deposited on the substrate surface (operation 42); and (2) forming a polymer binder layer to fill gaps among phosphor particles to form a substantially continuous layer of thin film (operation 44). The deposition process of forming the thin-film phosphor layer is desirably held in a vacuum chamber. However, it will be appreciated that the deposition process also can take place in a deposition chamber filled with an inert gas, such as nitrogen, or in an atmospheric environment. - In accordance with the process of
FIG. 4 , a variety of phosphors can be used. Typically, a phosphor is formed from a luminescent material, namely one that emits light in response to an energy excitation. Luminescence can occur based on relaxation from excited electronic states of atoms or molecules and, in general, can include, for example, chemiluminescence, electroluminescence, photoluminescence, thermoluminescence, triboluminescence, and combinations thereof. For example, in the case of photoluminescence, which can include fluorescence and phosphorescence, an excited electronic state can be produced based on a light excitation, such as absorption of light. Phosphors useful in accordance with the process ofFIG. 4 include a variety of inorganic host materials doped by activator ions such as Ce3+ and Eu2+, including garnets (e.g., (Y1-aGda)3(Al1-bGab)5O12:Ce3+ with a, b≦0.2 or YAG:Ce3+), silicates, orthosilicates, sulfides, and nitrides. Garnets and orthosilicates can be used as yellow-emitting phosphors, and nitrides can be used as red-emitting phosphors. However, it will be appreciated that various other types of wavelength-conversion materials can be used, including organic dyes. Desirably, phosphors and other types of wavelength-conversion materials can exhibit photoluminescence with a quantum efficiency that is greater than about 30 percent, such as at least about 40 percent, at least about 50 percent, at least about 60 percent, at least about 70 percent, or at least about 80 percent, and can be up to about 90 percent or more. - Typically, a phosphor used in accordance with
FIG. 4 is provided in a powder form, namely as a set of particles. To enhance color uniformity, the particles desirably have sizes in the range of about 1 nm to about 100 μm, such as from about 10 nm to about 30 μm, from about 100 nm to about 30 μm, from about 500 nm to about 30 μm, or from about 1 μm to about 30 μm. - Referring to
operation 42 ofFIG. 4 , the phosphor powder can be transported and deposited over the substrate surface by inertia effects, Brownian movement, thermophoresis, or electrical fields if the phosphor powder is electrically charged. One approach to form a substantially uniformly distributed phosphor powder layer on the substrate surface is to entrain, carry, mobilize, or transport the phosphor powder from a phosphor canister by a set of carrier gases, such as clean, dry air or an inert gas such as nitrogen, and then spray the phosphor powder through a showerhead mechanism in a vacuum, inert gas, or atmospheric chamber. For some embodiments, it is desirable that the phosphor powder is ionized with the same positive or negative electrostatic charge during the phosphor transport process. When the charged phosphor powder is sprayed and deposited on the substrate surface, the constituent phosphor particles are substantially uniformly distributed to form a phosphor powder layer resulting from self-balancing of electrostatic forces among the phosphor particles. Specifically, electrostatic spraying of the phosphor powder involves: -
- 1) The phosphor powder is transported by an inert carrier gas from a phosphor powder canister or other phosphor powder source. Phosphor powder flow volume can be precisely controlled by a nozzle device or other flow control mechanism, as depicted in
operation 421 ofFIG. 5 . - 2) The phosphor powder is ionized with the same electrostatic charge, as depicted in
operation 422 ofFIG. 5 . The operation of ionizing the phosphor powder is desirable to substantially uniformly deposit the phosphor powder on the substrate surface. It will be appreciated, however, that this powder ionization operation is optional, and can be omitted for certain embodiments. - 3) As depicted in
operation 423 ofFIG. 5 , if the substrate surface is formed of an electrically nonconductive polymer material, the substrate surface is ionized with an opposite electrostatic charge on the substrate surface. If the substrate surface is formed of an electrically conductive material, the substrate surface is grounded, such as by electrically connecting the substrate surface to a ground potential. The operation of ionizing or grounding the substrate surface is desirable to substantially uniformly deposit the phosphor powder on the substrate surface. It will be appreciated, however, that this substrate surface ionizing or grounding operation is optional, and can be omitted for certain embodiments. - 4) The carrier gas entrains the charged phosphor powder to the deposition chamber through a showerhead mechanism, thereby evenly distributing the phosphor powder, as depicted in
operation 424 ofFIG. 5 . The showerhead mechanism is desirable to substantially uniformly deposit the phosphor powder on the substrate surface. Alternatively, or in conjunction, the substrate surface is rotated in the deposition chamber using a rotational mechanism so that the phosphor powder can be substantially uniformly deposited on the substrate surface. It will be appreciated, however, that these mechanisms are optional, and can be omitted for certain embodiments. - 5) The phosphor powder is conformally and substantially uniformly deposited onto the substrate surface, as depicted in
operation 425 ofFIG. 5 . In one embodiment, the substrate surface is a surface of an LED chip or surfaces of multiple LED chips. In another embodiment, the substrate surface is a surface of an LED lens or surfaces of multiple LED lenses. In another embodiment, the substrate surface is a surface of a glass or quartz substrate. In another embodiment, the substrate surface is a surface of a flexible transparent film, such as one formed of polyethylene terephthalate). - 6) The phosphor powder is discharged with ionizing (or de-ionizing) gas, as depicted in
operation 426 ofFIG. 5 . The ionizing gas neutralizes residual electrostatic charges on the phosphor power. It will be appreciated that this discharging operation is optional, and can be omitted for certain embodiments, such as those in which theionizing operation 422 is omitted.
- 1) The phosphor powder is transported by an inert carrier gas from a phosphor powder canister or other phosphor powder source. Phosphor powder flow volume can be precisely controlled by a nozzle device or other flow control mechanism, as depicted in
- In the case that the
operation 422 ofFIG. 5 is implemented, the phosphor powder is ionized with electrostatic charges by one, or a combination, of the following methods: -
- Corona charging where electric power is used to generate the electrostatic charges
- Triboelectric charging where the electrostatic charges are generated by friction between the powder and some conduit surface
- Induction charging where the powder is charged by induction from an electrical field
- In the case that the
operation 423 is implemented for an electrically conductive substrate, the substrate surface can be grounded to maintain an electric field potential for the deposition of the electrostatically charged phosphor powder. Electrostatic charges also can be created on the phosphor powder or an electrically nonconductive substrate surface by Tribo frictional charging. In particular, when two different materials are brought into contact, there can be a transfer of charge from one to the other to offset an imbalance of charges. The magnitude and direction of the charge transfer can depend on a number of factors, including a chemical and electronic structure of both materials. Table 1 sets forth certain materials ranging from those with the most positive charging effect to those with the most negative charging effect when brought into contact. -
TABLE 1 Materials ordered by Triboelectric Charging Effects Most Positive (+) Air Human Hands, Skin Asbestos Rabbit Fur +++ Glass Human Hair Mica Nylon Wool Lead Cat Fur + Silk Aluminum Paper Cotton Steel Wood Lucite Sealing Wax Amber Rubber Balloon Hard Rubber − Mylar Nickel Copper Silver UV Resist Brass Synthetic Rubber Gold, Platinum Sulfur Acetate, Rayon Polyester Celluloid Polystyrene Orlon, Acrylic Cellophane Tape Polyvinylidene chloride (Saran) Polyurethane −−− Polyethylene Polypropylene Polyvinylchloride (Vinyl) Kel-F (PCTFE) Silicon Teflon Silicone Rubber Most Negative (−) - An opposite electrostatic charge can be created on an electrically nonconductive substrate surface with the Tribo frictional charging method. For example, negative charges can be created on the nonconductive substrate surface by one, or a combination, of the following:
-
- Tribo frictional charging is carried out using a Teflon powder blown through a nonconductive epoxy or silicone resin surface. The Teflon powder can carry electrons away from the epoxy or silicone resin surface to render the surface negatively charged.
- An epoxy surface is rubbed with a Nylon brush or cloth.
- The phosphor deposition process provides a number of advantages, including:
-
- It can be applied to both a near phosphor configuration and a remote phosphor configuration for phosphor-converted white LEDs.
- It can be implemented as a layer-by-layer phosphor deposition process, and can be readily used to form a multi-color phosphor thin-film stack.
- The deposition process can be a dry and clean process, without any solvents.
- Controlled quantities of phosphors can be used during deposition, thereby significantly reducing color variations and binning issues of white LEDs.
- It can achieve a substantially uniform coating of phosphors by introducing electrostatic charges among phosphor particles.
- It can achieve a high phosphor utilization yield during deposition.
- In accordance with the thin-film phosphor deposition process of
FIG. 4 , the deposited phosphor layer is initially a loosely packed powder layer. Next, a polymer thin film is deposited to fill gaps among phosphor particles and to form a substantially continuous thin-film layer, as depicted inoperation 44 ofFIG. 4 . To preserve the substantially uniformly distributed phosphor layer structure, it is desirable to use a Chemical Vapor Deposition (“CVD”) process to form this polymer layer as a binder material for the phosphor particles. It will be appreciated that another suitable deposition process can be used in place of, or in conjunction with, CVD to form the polymer layer. Examples of other deposition processes include other vapor deposition processes, such as thermal evaporation, electron-beam evaporation, or physical vapor deposition, as well as spray coating, dip coating, web coating, wet coating, and spin coating. -
FIG. 6A throughFIG. 6D depict examples of a family of conformal coating polymers that can be used to form a binding matrix for a thin-film phosphor layer, according to an embodiment of the invention. In particular, the family of polymers corresponds to a family of parylene-based polymers. Generally, parylene-based polymers correspond to a variety of polyxylylene-based polymers, such as polyp-xylylene) and its derivatives, and include, for example, polymers having a general repeating unit of the formula —CZZ′—Ar—CZ″Z′″—, wherein Ar is an arylene group (e.g., un-substituted, partially substituted, or fully substituted arylene group, such as phenylene), and wherein Z, Z′, Z″, and Z′″ can be the same or different. In specific embodiments, Ar is C6H4-xXx, wherein X is a halogen such as Cl or F, x=0, 1, 2, 3, or 4, and Z, Z′, Z″, and Z′″ are independently selected from H, F, alkyl groups, and aryl groups (e.g., C6H5-xFx with x=0, 1, 2, 3, 4, or 5). In one specific embodiment, Parylene N depicted inFIG. 6A includes a repeating unit of the formula —CH2—C6H4—CH2—, and is used as a binder material to form a thin-film phosphor layer. In another embodiment, Parylene C depicted inFIG. 6B including a repeating unit of the formula —CH2—C6H3Cl—CH2— is used as a binder material to form a thin-film phosphor layer. Parylene C can be produced from the same monomer as Parylene N, but modified with the substitution of a chlorine atom for one of the aromatic hydrogens. In another embodiment, Parylene D depicted inFIG. 6C including a repeating unit of the formula —CH2—C6H2Cl2—CH2— is used as a binder material to form a thin-film phosphor layer. Parylene D can be produced from the same monomer as Parylene N, but modified with the substitution of two chlorine atoms for two of the aromatic hydrogens. In another embodiment, a partially fluorinated parylene-based polymer referred to as Parylene F can be used, as depicted inFIG. 6D . Parylene F includes a repeating unit of the formula —CF2—C6H4—CF2—, and can be formed from various precursors, such as BrCF2—C6H4—CF2Br. It will be appreciated that these parylene-based polymers are provided by way of example, and a variety of other conformal coating polymers can be used. Examples of other suitable polymers include polyimides, fluorocarbon-based polymers (e.g., poly(tetrafluoroethylene)), poly(p-phenylene vinylene), poly(pyrrole), poly(thiophene), poly(2,4-hexadiyn-1,6-diol), fluorocarbon/organosilicon copolymers, poly(ethylene glycol), and their derivatives. Thermal evaporation of acrylics also can be used to form a substantially continuous phosphor film. - Various parylene-based polymer films and other types of polymer films can be formed via a CVD technique of transport polymerization. Transport polymerization typically involves generating a vapor phase reactive intermediate from a precursor molecule at a location remote from a substrate surface, and then transporting the vapor phase reactive intermediate to the substrate surface. The substrate surface can be kept below a melting temperature of reactive intermediates for polymerization. For example, Parylene F can be formed from the precursor BrCF2—C6H4—CF2Br by the removal of the bromine atoms to form the reactive intermediate *CF2—C6H4—CF2*, wherein * denotes a free radical. This reactive intermediate can be formed at a location remote from a deposition chamber, and can be transported into the deposition chamber and condensed over the substrate surface, where polymerization takes place.
- More generally, parylene-based polymer films can be formed from a variety of precursors, such as those having the formula (CZZ′Y)m—Ar—(CZ″Z′″Y′)n, wherein Ar is an arylene group (e.g., un-substituted, partially substituted, or fully substituted arylene group, such as phenylene), Z, Z′, Z″, and Z′″ can be the same or different, Y and Y′ can be the same or different and are removable to generate free radicals, m and n are each equal to zero or a positive integer, and a sum of m and n is less than or equal to a total number of sp2-hybridized carbons on Ar available for substitution. In specific embodiments, Ar is C6H4-xXx, wherein X is a halogen such as Cl or F, x=0, 1, 2, 3, or 4, and Z, Z′, Z″, and Z′″ are independently selected from H, F, alkyl groups, and aryl groups (e.g., C6H5-xFx with x=0, 1, 2, 3, 4, or 5). Other suitable precursors include dimers having the formula {(CZZ′)—Ar—(CZ″Z′″)}2, wherein Ar is an arylene group (e.g., un-substituted, partially substituted, or fully substituted arylene group, such as phenylene), and Z, Z′, Z″, and Z′″ can be the same or different. In specific embodiments, Ar is C6H4-xXx, wherein X is a halogen such as Cl or F, x=0, 1, 2, 3, or 4, and Z, Z′, Z″, and Z′″ are independently selected from H, F, alkyl groups, and aryl groups (e.g., C6H5-xFx with x=0, 1, 2, 3, 4, or 5).
- One aspect of a parylene-based polymer film, or another type of polymer film, prepared by the CVD method is that it is a conformal coating with superior crevice penetration capability, thereby substantially filling gaps and voids within a phosphor powder layer. In some instances, Parylene F can achieve the best result for gap-filling, while Parylene N can achieve the second best result for gap-filling among the family of parylene-based polymers. Another aspect of a parylene-based polymer is that it has superior optical transparency in the visible light spectrum, rendering it a suitable filler material among a photoluminescent phosphor powder. Another aspect of a parylene-based polymer is that its refractive index can be adjusted based on chemical composition. In one embodiment, a multi-layer of parylene-based polymer films can be formed as a composite thin-film phosphor stack. This multi-layer structure can be formed by depositing a Parylene N film, with a refractive index of about 1.66, as a binder material among a phosphor powder, and then depositing a Parylene F film, with a refractive index of about 1.4, thereby enhancing light extraction due to index matching of the Parylene F film to ambient environment (e.g., air). It will be appreciated that, in general, this multi-layer structure can be formed by depositing a first polymer film, with a first refractive index, as a binder material among a first phosphor powder layer to form a first phosphor layer adjacent to the substrate surface, depositing a second polymer film, with a second refractive index, as a binder material among a second phosphor powder layer to form a second phosphor layer adjacent to the first phosphor layer, and so on, where the first refractive index is greater than or equal to the second refractive index.
- Using the CVD method, a parylene-based polymer, or another type of polymer, can be formed as a substantially continuous film having a thickness in the range of a few tens of angstroms to about 100 μm, such as from about 1 nm to about 100 μm, from about 10 nm to about 100 μm, from about 100 nm to about 100 μm, from about 1 μm to about 100 μm, from about 1 μm to about 75 μm, from about 1 μm to about 30 μm, or from about 1 μm to about 10 μm. In some instances, the thickness of the film can exhibit a standard deviation of less than about 20 percent with respect to an average thickness, such as less than about 10 percent or less than about 5 percent. A thickness of the initially deposited phosphor powder layer can be in the range of about 1 nm to about 60 μm, such as from about 10 nm to about 60 μm, from about 100 nm to about 40 μm, or from about 100 nm to about 20 μm. In some instances, the thickness of the phosphor powder layer can exhibit a standard deviation of less than about 20 percent with respect to an average thickness, such as less than about 10 percent or less than about 5 percent. A distribution of the phosphor powder within the resulting film can be substantially uniform across an extent of the film, such that a weight density (e.g., mass or weight of phosphor particles per unit volume) or a number density (e.g., number of phosphor particles per unit volume) can exhibit a standard deviation of less than about 20 percent with respect to an average density, such as less than about 10 percent or less than about 5 percent.
- An embodiment of a thin-film phosphor layer prepared by the CVD method is depicted in
FIG. 7A . InFIG. 7A , a single-colorphosphor powder layer 71, such as a YAG:Ce3+-based yellow phosphor, is initially deposited on asubstrate surface 72. Thesubstrate surface 72 can be an electrically nonconductive surface, such as a surface of a flexible plastic substrate. A parylene-basedpolymer layer 73 is deposited, and another parylene-basedpolymer layer 74 is next deposited. The parylene-basedpolymer layer 73 serves as a binder or a matrix that at least partially penetrates or surrounds thephosphor powder layer 71, such that phosphor particles of thephosphor powder layer 71 are dispersed within the parylene-basedpolymer layer 73. It will be appreciated that the parylene-based polymer layers 73 and 74 can be formed from the same material or different materials. In some instances, a refractive index of the parylene-basedpolymer layer 73 is greater than a refractive index of the parylene-basedpolymer layer 74. - In accordance with a layer-by-layer deposition of phosphor powders, the CVD method can be used to form a substantially uniformly distributed multi-color phosphor stack. In an embodiment depicted in
FIG. 7B , a multi-color phosphor thin-film stack 75 is formed by sequential deposition of a blue phosphor powder, a parylene-based polymer as a binder material for the blue phosphor powder, a green phosphor powder, a parylene-based polymer as a binder material for the green phosphor powder, a red phosphor power, and a parylene-based polymer as a binder material for the red phosphor powder. A resulting phosphor-converted white LED can emit three down-converted secondary lights of respective colors by the phosphors. Thus, a Color Rendering Index (“CRI”) of the phosphor-converted white LED can be readily tuned, for example, when used in an indoor general illumination application with a warmer white light and an improved color uniformity. Another application of the phosphor-converted white LED incorporating the multi-color thin-film phosphor stack 75 is for backlighting of Liquid Crystal Displays (“LCDs”). - It will be appreciated that the phosphor powder deposition in
operation 42 and the polymer deposition inoperation 44 need not take place sequentially. Alternatively, these operations can take place substantially simultaneously to form a conformal phosphor thin-film layer. -
FIG. 8 depicts a thin-filmphosphor deposition system 80, according to an embodiment of the invention. The thin-filmphosphor deposition system 80 can be used to form a conformally coated thin-film phosphor layer by depositing a substantially uniformly distributed phosphor powder layer and then depositing a conformally coated CVD polymer to form a substantially continuous phosphor thin film. The thin-filmphosphor deposition system 80 includes: (1) a deposition subsystem orunit 81; (2) a phosphor powder delivery subsystem orunit 82 connected to thedeposition subsystem 81; and (3) a parylene-based polymer precursor delivery subsystem orunit 83 connected to thedeposition subsystem 81. - The
deposition subsystem 81 includes: (1) a deposition chamber 81 a, which defines an enclosure within which a substrate is disposed and, for example, is a vacuum chamber with an associated vacuum pump to maintain vacuum conditions, is filled with an inert gas, or is an atmospheric chamber; (2) asubstrate holder 81 b within the chamber 81 a and, for example, is capable of rotating the substrate during the formation of the phosphor film; (3) ashowerhead mechanism 81 c; and (4) aphosphor powder ionizer 81 d, which introduces electrostatic charges among phosphor particles during phosphor powder deposition. - The phosphor
powder delivery subsystem 82 includes: (1) aphosphor powder canister 82 a or other phosphor powder source; (2) aphosphor flow controller 82 b, which regulates a specified quantity of phosphors for each deposition of phosphors; (3) anionizer 82 c, which introduces electrostatic charges among phosphor particles during phosphor powder deposition; and (4) a set ofvalves 82 d. - The parylene-based polymer
precursor delivery subsystem 83 includes: (1) aprecursor canister 83 a or other precursor source; (2) aprecursor flow controller 83 b, which regulates a specified quantity of precursors for each polymer deposition; (3) agas reactor 83 c, which induces the generation of vapor phase reactive intermediates from precursors; and (4) a set ofvalves 83 d. - In order to deposit parylene-based films, solid or liquid precursors are heated in the
stainless canister 83 a to a consistent temperature to generate vapor phase precursors. The vapor phase precursors are fed into thegas reactor 83 c, which is regulated by theflow controller 83 b, as depicted inFIG. 8 . Thegas reactor 83 c splits the precursors into reactive intermediates that bear two unpaired electrons, or diradicals. The diradicals are transported to the deposition chamber 81 a shortly after thegas reactor 83 c activates the precursors. Because the diradicals can be very reactive, the diradicals can quickly polymerize to form a polymer thin film once the diradicals collide with each other on a substrate surface held inside the deposition chamber 81 a. - The thin-film
phosphor deposition system 80 also includes a control subsystem or unit, which includes aprocessor 84 and an associatedmemory 85 that are connected to other components of thesystem 80 and serve to direct operation of those components. Thememory 85 can include a computer-readable storage medium having computer code stored thereon for performing various computer-implemented operations. The media and computer code can be those specially designed and constructed for the purposes of embodiments of the invention, or they may be of the kind well known and available to those having skill in the computer software arts. Examples of computer-readable media include, but are not limited to: magnetic storage media such as hard disks, floppy disks, and magnetic tape; optical storage media such as Compact Disc/Digital Video Discs (“CD/DVDs”), Compact Disc-Read Only Memories (“CD-ROMs”), and holographic devices; magneto-optical storage media such as floptical disks; and hardware devices that are specially configured to store and execute program code, such as Application-Specific Integrated Circuits (“ASICs”), Programmable Logic Devices (“PLDs”), and ROM and RAM devices. Examples of computer code include, but are not limited to, machine code, such as produced by a compiler, and files containing higher-level code that are executed by a computer using an interpreter. For example, an embodiment of the invention may be implemented using Java, C++, or other object-oriented programming language and development tools. Additional examples of computer code include, but are not limited to, encrypted code and compressed code. Other embodiments of the invention can be implemented using hardwired circuitry in place of, or in conjunction with, computer code. - Table 2 sets forth certain advantages of the conformal thin-film phosphor deposition method of some embodiments of the invention, relative to other phosphor coating methods.
-
TABLE 2 Comparison of Phosphor Coating Methods Conformal Thin- Slurry Method EPD Ceramic Plate Film Phosphor Spatial proximate proximate proximate remote conformal Phosphor phosphor-in-cup conformal phosphor phosphor Distribution phosphor Scattering ~50% ~40% Slightly better ≧about 90% (e.g., Efficiency than EPD ≧about 92% or ≧about 95% and up to about 99% or more) Homogeneity Poor Good Good Good Color Poor Good Good Good Consistency Color Possible for Single Possible for Possible for layer- Rendering multi-color phosphor multi-layer by-layer phosphor phosphor ceramic plate deposition Temperature Medium Poor Good Best Stability Cost Die-level Batch process Die-level Batch process process process - In conjunction with the advantages set forth above, a light emitting device formed in accordance with the conformal thin-film phosphor deposition method can emit white light of greater uniformity. In particular, a CCT variation of a white light LED can be no greater than about 1,000 K over a 140° (±70° from a center light-emitting axis) range of light emission angles, such as no greater than about 800 K, no greater than about 500 K, or no greater than about 300 K, and down to about 200 K or less.
- While the invention has been described with reference to the specific embodiments thereof, it should be understood by those skilled in the art that various changes may be made and equivalents may be substituted without departing from the true spirit and scope of the invention as defined by the appended claims. In addition, many modifications may be made to adapt a particular situation, material, composition of matter, method, or process to the objective, spirit and scope of the invention. All such modifications are intended to be within the scope of the claims appended hereto. In particular, while the methods disclosed herein have been described with reference to particular operations performed in a particular order, it will be understood that these operations may be combined, sub-divided, or re-ordered to form an equivalent method without departing from the teachings of the invention. Accordingly, unless specifically indicated herein, the order and grouping of the operations are not limitations of the invention.
Claims (26)
1. A method of forming a thin-film phosphor layer for use in a light emitting device, the method comprising:
transporting, using a carrier gas, a phosphor powder from a source of the phosphor powder to a deposition chamber; and
depositing the phosphor powder adjacent to a substrate within the deposition chamber so as to substantially uniformly distribute the phosphor powder adjacent to a surface of the substrate.
2. The method of claim 1 , further comprising inducing electrostatic charges in the phosphor powder.
3. The method of claim 2 , wherein the substrate is electrically nonconductive, and further comprising:
inducing opposite electrostatic charges adjacent to the surface of the substrate; and
subsequent to depositing the phosphor powder, discharging the phosphor powder using an ionizing gas.
4. The method of claim 2 , wherein the substrate is electrically conductive, and further comprising:
electrically connecting the substrate to a ground potential; and
subsequent to depositing the phosphor powder, discharging the phosphor powder using an ionizing gas.
5. The method of claim 1 , wherein depositing the phosphor powder includes dispensing the phosphor powder through a showerhead mechanism.
6. The method of claim 1 , wherein depositing the phosphor powder includes rotating the substrate using a rotating substrate holder.
7. The method of claim 1 , wherein a thickness of the deposited phosphor powder is in the range of 10 nm to 60 μm.
8. The method of claim 1 , further comprising depositing a polymer adjacent to the deposited phosphor powder so as to form a thin-film phosphor layer adjacent to the surface of the substrate.
9. The method of claim 8 , wherein a thickness of the thin-film phosphor layer is in the range of 10 nm to 100 μm.
10. The method of claim 8 , wherein the polymer includes a polyxylylene-based polymer, and depositing the polymer is carried out using chemical vapor deposition.
11. A method of forming a thin-film phosphor layer for use in a light emitting device, the method comprising:
forming a first phosphor powder layer adjacent to a substrate, the first phosphor powder layer including first phosphor particles that are distributed adjacent to a surface of the substrate; and
forming, via vapor deposition, a first polymer layer adjacent to the first phosphor powder layer, the first polymer layer serving as a binder for the first phosphor particles.
12. The method of claim 11 , further comprising forming, via vapor deposition, a second polymer layer adjacent to the first polymer layer.
13. The method of claim 12 , wherein a refractive index of the first polymer layer is greater than a refractive index of the second polymer layer.
14. The method of claim 12 , wherein at least one of the first polymer layer and the second polymer layer includes a polymer including a repeating unit of the formula: —CZZ′—Ar—CZ″Z′″—, wherein Ar is selected from (1) an un-substituted phenylene group, (2) a chlorine-substituted phenylene group of the formula: C6H4-xClx, with x being an integer in the range of 1 to 4, and (3) a fluorine-substituted phenylene group of the formula: C6H4- x′Fx′, with x′ being an integer in the range of 1 to 4, and Z, Z′, Z″, and Z′″ are independently selected from H, F, alkyl groups, and aryl groups.
15. The method of claim 11 , further comprising:
forming a second phosphor powder layer adjacent to the first polymer layer, the second phosphor powder layer including second phosphor particles that are distributed adjacent to a surface of the first polymer layer; and
forming, via vapor deposition, a second polymer layer adjacent to the second phosphor powder layer, the second polymer layer serving as a hinder for the second phosphor particles,
wherein the first phosphor particles and the second phosphor particles are configured to emit light of different colors.
16. The method of claim 15 , further comprising:
forming a third phosphor powder layer adjacent to the second polymer layer, the third phosphor powder layer including third phosphor particles that are distributed adjacent to a surface of the second polymer layer; and
forming, via vapor deposition, a third polymer layer adjacent to the third phosphor powder layer, the third polymer layer serving as a binder for the third phosphor particles,
wherein the first phosphor particles, the second phosphor particles, and the third phosphor particles are configured to emit light of different colors.
17. A system to form a thin-film phosphor layer on a substrate, the system comprising:
a deposition subsystem defining an enclosure to accommodate the substrate;
a phosphor powder delivery subsystem configured to deliver, using a carrier gas, a phosphor powder from a source of the phosphor powder to the deposition subsystem;
a polymer precursor delivery subsystem configured to deliver polymer precursors in a vapor phase to the deposition subsystem; and
a control subsystem connected to the deposition subsystem, the phosphor powder delivery subsystem, and the polymer precursor delivery subsystem, wherein the control subsystem is configured to control the phosphor powder delivery subsystem to deliver the phosphor powder to the deposition subsystem for a first time interval to form a phosphor powder layer adjacent to the substrate, and the control subsystem is configured to control the polymer precursor delivery subsystem to deliver the polymer precursors to the deposition subsystem for a second time interval to form a polymer layer adjacent to the phosphor powder layer.
18. The system of claim 17 , wherein the deposition subsystem includes a vacuum chamber defining the enclosure, a substrate holder configured to support the substrate within the vacuum chamber, and a showerhead mechanism configured to deposit the phosphor powder over the substrate.
19. The system of claim 18 , wherein the substrate holder is configured to rotate the substrate.
20. The system of claim 18 , wherein the deposition subsystem further includes an ionizer configured to induce electrostatic charges in the phosphor powder.
21. The system of claim 17 , wherein the phosphor powder delivery subsystem includes an ionizer configured to induce electrostatic charges in the phosphor powder.
22. The system of claim 17 , wherein the polymer precursor delivery subsystem includes a gas reactor configured to generate reactive intermediates in a vapor phase from the polymer precursors.
23. The system of claim 22 , wherein the gas reactor is configured to generate free radicals from the polymer precursors, and the polymer precursors have the formula: (CZZ′Y)m—Ar—(CZ″Z′″Y′)n, wherein Ar is selected from (1) an un-substituted phenylene group, (2) a chlorine-substituted phenylene group of the formula: C6H4-xClx, with x being an integer in the range of 1 to 4, and (3) a fluorine-substituted phenylene group of the formula: C6H4- x′Fx′, with x′ being an integer in the range of 1 to 4, Z, Z′, Z″, and Z′″ are independently selected from H, F, alkyl groups, and aryl groups, Y and Y′ being removable to generate the free radicals, m and n are each equal to zero or a positive integer, and a sum of m and n is less than or equal to a total number of sp2-hybridized carbons on Ar available for substitution.
24. The system of claim 22 , wherein the gas reactor is configured to generate free radicals from the polymer precursors, and the polymer precursors include dimers having the formula: {(CZZ′)—Ar—(CZ″Z′″)}2, wherein Ar is selected from (1) an un-substituted phenylene group, (2) a chlorine-substituted phenylene group of the formula: C6H4-xClx, with x being an integer in the range of 1 to 4, and (3) a fluorine-substituted phenylene group of the formula: C6H4- x′Fx′, with x′ being an integer in the range of 1 to 4, and Z, Z′, Z″, and Z′ are independently selected from H, F, alkyl groups, and aryl groups.
25. A thin-film phosphor layer, comprising:
at least one phosphor layer; and
at least one parylene-based polymer layer disposed adjacent to the at least one phosphor layer, the at least one parylene-based polymer layer serving as a binder for the at least one phosphor layer.
26. The thin-film phosphor layer of claim 25 , wherein the at one parylene-based polymer layer includes a polymer including a repeating unit of the formula: —CZZ′—Ar—CZ″Z′″—, wherein Ar is selected from (1) an un-substituted phenylene group, (2) a chlorine-substituted phenylene group of the formula: C6H4-xClx, with x being an integer in the range of 1 to 4, and (3) a fluorine-substituted phenylene group of the formula: C6H4- x′Fx′, with x′ being an integer in the range of 1 to 4, and Z, Z′, Z″, and Z′″ are independently selected from H, F, alkyl groups, and aryl groups.