US20060151756A1 - Composite material and current collector for battery - Google Patents
Composite material and current collector for battery Download PDFInfo
- Publication number
- US20060151756A1 US20060151756A1 US11/367,331 US36733106A US2006151756A1 US 20060151756 A1 US20060151756 A1 US 20060151756A1 US 36733106 A US36733106 A US 36733106A US 2006151756 A1 US2006151756 A1 US 2006151756A1
- Authority
- US
- United States
- Prior art keywords
- carbon foam
- composite material
- pores
- battery
- bonding material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A composite material including a first carbon foam structure including a network of pores and a second carbon foam structure including a network of pores. An intermediate bonding structure is disposed at least in part between the first and second carbon foam structures.
Description
- This invention relates generally to a composite material and, more particularly, to a composite material current collector for an energy storage device.
- Lead acid batteries are known to include at least one positive current collector, at least one negative current collector, and an electrolytic solution including, for example, sulfuric acid (H2SO4) and distilled water. Ordinarily, both the positive and negative current collectors in a lead acid battery are constructed from lead. The role of these lead current collectors is to transfer electric current to and from the battery terminals during the discharge and charging processes. Storage and release of electrical energy in lead acid batteries is enabled by chemical reactions that occur in a paste disposed on the current collectors. The positive and negative current collectors, once coated with this paste, are referred to as positive and negative plates, respectively. A notable limitation on the durability of lead acid batteries is corrosion of the lead current collector of the positive plate.
- The rate of corrosion of the lead current collector is a major factor in determining the life of the lead acid battery. Once the sulfuric acid electrolyte is added to the battery and the battery is charged, the current collector of each positive plate is continually subjected to corrosion due to its exposure to sulfuric acid and to the anodic potentials of the positive plate. One of the most damaging effects of this corrosion of the positive plate current collector is volume expansion. Particularly, as the lead current collector corrodes, lead dioxide is formed from the lead source metal of the current collector. This lead dioxide corrosion product has a greater volume than the lead source material consumed to create the lead dioxide. Corrosion of the lead source material and the ensuing increase in volume of the lead dioxide corrosion product is known as volume expansion.
- Volume expansion induces mechanical stresses on the current collector that deform and stretch the current collector. At a total volume increase of the current collector of approximately 4% to 7%, the current collector may fracture. As a result, battery capacity drops, and eventually, the battery will reach the end of its service life. Additionally, at advanced stages of corrosion, internal shorting within the current collector and rupture of the cell case can occur. Both of these corrosion effects may lead to failure of one or more of the cells within the battery.
- One method of extending the service life of a lead acid battery is to increase the corrosion resistance of the current collector of the positive plate. Several methods have been proposed for inhibiting the corrosion process in lead acid batteries. Because carbon does not oxidize at the temperatures at which lead acid batteries generally operate, some of these methods have involved using carbon in various forms to slow or prevent the detrimental corrosion process in lead acid batteries. For example, U.S. Pat. No. 5,512,390 (hereinafter the '390 patent) discloses a lead acid battery that includes current collectors made from graphite plates instead of lead. The graphite plates have sufficient conductivity to function as current collectors, and they are more corrosion resistant than lead. Substituting graphite plates for the lead current collectors may, therefore, lengthen the life of a lead acid battery.
- While the battery of the '390 patent may potentially offer a lengthened service life as a result of reduced corrosion at the positive plate, the graphite plates of the '390 patent are problematic. For example, the graphite plates of the '390 patent are dense, flat sheets of material each having a relatively small amount of surface area. Unlike lead electrode plates of a conventional lead acid battery, which are generally patterned into a grid-like structure to increase the available surface area of the plates, the graphite plates of the '390 patent are smooth sheets with no patterning. In lead acid batteries, an increase in surface area of the current collector may increase the specific energy of the battery and, therefore, may translate into improved battery performance. More surface area on the current collectors may also lead to a reduction in the time required for charging and discharging of the battery. The relatively small surface area of the graphite plates of the '390 patent results in poorly performing batteries that have slow charging speeds.
- Additionally, the graphite plates of the '390 patent lack the toughness of lead current collectors. The dense graphite plates of the '390 patent are brittle and may fracture when subjected to physical shock or vibration. Such physical shock and vibration commonly occur in vehicular applications, for example. Any fracturing of the graphite plates would lead to the same problems caused by volume expansion of ordinary lead current collectors. Therefore, despite offering an increased resistance to corrosion compared to conventional lead current collectors, the brittle nature of the graphite plates of the '390 patent could actually result in battery service lives shorter than those possible through use of ordinary lead current collectors.
- One aspect of the present invention includes a composite material. The composite material includes a first carbon foam structure including a network of pores and a second carbon foam structure including a network of pores. An intermediate bonding structure is disposed at least in part between the first and second carbon foam structures.
- The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate exemplary embodiments of the invention and, together with the written description, serve to explain the principles of the invention. In the drawings:
-
FIG. 1 is a cross-sectional view of a composite material in accordance with an exemplary embodiment of the present invention; -
FIG. 2A is a plan view of a current collector in accordance with an exemplary embodiment of the present invention; -
FIG. 2B is a cross-sectional view of the current collector ofFIG. 2A taken along the line 2A; -
FIG. 3A is a plan view of another current collector in accordance with an exemplary embodiment of the present invention; -
FIG. 3B is a cross-sectional view of the current collector ofFIG. 3A taken along theline 3B; -
FIG. 4 is a diagrammatic cut-away representation of a battery in accordance with an exemplary embodiment of the present invention. - In the following description, reference is made to the accompanying drawings that form a part thereof, and in which is shown by way of illustration specific exemplary embodiments in which the invention may be practiced. These embodiments are described in sufficient detail to enable those skilled in the art to practice the invention, and it is to be understood that other embodiments may be utilized and that changes may be made without departing from the scope of the present invention. The following description is, therefore, not to be taken in a limited sense. Wherever possible, the same reference numbers are used throughout the drawings to refer to the same or like parts.
- As shown in
FIG. 1 , according to one embodiment of the invention,composite material 10 includes two layers ofporous carbon foam intermediate bonding material 12 is disposed betweencarbon foam layers material 12 attachescarbon foam layers composite material 10. - The carbon foam used to form carbon foam layers 11 and 13 of
composite material 10 is electrically conductive. In certain forms, the carbon foam may offer sheet resistivity values of less than about 1 ohm/cm. In still other forms, the carbon foam may have sheet resistivity values of less than about 0.75 ohm/cm. The electrical conductivity of carbon foam layers 11 and 13 allowscomposite material 10 to be used in a variety of applications such as, for example, current collectors in batteries. - The carbon foam used to form carbon foam layers 11 and 13 of
composite material 10 is also resistant to corrosion. In general, carbon oxidizes only at very high temperatures and will resist corrosion even in corrosive environments. The carbon foam used incomposite material 10 retains this corrosion resistance, and therefore,composite material 10 may be used, for example, in the corrosive environment of a lead acid battery. - Additionally, carbon foam layers 11 and 13 are lightweight due to the presence of a network of
pores 14. In one embodiment of the invention, for example, the carbon foam may include a total porosity value of at least about 60%. In other words, at least 60% of the volume of carbon foam layers 11 and 13 is included within pores 14. Moreover, the carbon foam may have an open porosity value of at least about 90%. In other words, at least 90% ofpores 14 are open to adjacent pores such that the network ofpores 14 forms a substantially open network. This open network ofpores 14 may result in a density of less than about 0.6 gm/cm3 for each of carbon foam layers 11 and 13. Further, the average pore size of the carbon foam may be between about 0.25 mm and about 2.0 mm, although other sizes may also be possible. - In addition to carbon foam, graphite foam may also be used to form
composite material 10. One such graphite foam, under the trade name PocoFoam™, is available from Poco Graphite, Inc. The density and pore structure of graphite foam may be similar to carbon foam. A primary difference between graphite foam and carbon foam is the orientation of the carbon atoms that make up the structural elements of the foam. For example, in carbon foam, the carbon may be primarily amorphous. In graphite foam, however, much of the carbon is ordered into a graphite, layered structure. Because of the ordered nature of the graphite structure, graphite foam offers higher conductivity than carbon foam. PocoFoam™ graphite foam exhibits electrical resistivity values of between about 100 μΩ/cm and about 400 μΩ/cm. - In
composite material 10,bonding material 12 is disposed between carbon foam layers 11 and 13.Bonding material 12 attaches carbon foam layers 11 and 13 together by permeating at least some ofpores 14 ofcarbon foam layer 11 and at least some ofpores 14 ofcarbon foam layer 13. In an exemplary embodiment,bonding material 12 permeates the pores ofcarbon foam layer 11 by a depth equal to or greater than an average pore size oflayer 11. Similarly, in the exemplary embodiment,bonding material 12 may permeate the pores ofcarbon foam layer 13 by a depth equal to or greater than an average pore size oflayer 13. The depth of permeation ofbonding material 12 into carbon foam layers 11 and 13 is not limited to depths of at least the average pore size oflayers bonding material 12 into carbon foam layers 11 and 13 is represented inFIG. 1 bypermeation zones - A variety of materials may be used as bonding
material 12.Bonding material 12 may include an electrically insulating material including a polymer. For example, in one embodiment,bonding material 12 may include polypropylene. In yet another embodiment,bonding material 12 may include any of a wide range of epoxies. In still another embodiment, an electrically conductive material may be used as bondingmaterial 12. Such electrically conductive materials may include, for example, various metals and electrically conductive polymers. - To make the composite material of one embodiment of the present invention, a bonding material may be applied to a sheet of carbon foam material. Next, a second sheet of carbon foam material may be placed on the bonding material to form a stacked structure. If the bonding material is applied as a solid, such as in the case of most polymers and metals, then heat may be applied to the stacked structure to soften and/or melt the bonding material. Softening and/or melting of the bonding material encourages permeation of the bonding material into the pores of the carbon foam. In addition to heat, pressure can also be applied to the stacked structure. The application of external pressure may aid in forcing the bonding material to permeate the pores of the carbon foam. In an exemplary embodiment of the present invention, heat and pressure are applied simultaneously. In certain situations, however, heat may be applied exclusive of pressure. In still other situations, the application of heat may occur separate from the application of pressure.
- In instances where the bonding material is applied as a liquid, such as an epoxy, for example, the bonding material may permeate the pores of each of the two sheets of carbon foam without the need for applying heat or pressure. Nevertheless, even in the case of bonding materials applied as a liquid, the application of heat and/or pressure, either together or individually, may facilitate permeation of the bonding material into the pores of the carbon foam by reducing the viscosity of the bonding material.
-
FIGS. 2A and 2B illustrate acurrent collector 20 that includes the composite material of one embodiment of the present invention. As shown inFIGS. 2A and 2B ,current collector 20 includes carbon foam layers 11 and 13 bonded together by aconductive bonding material 22.Bonding material 22 permeates at least some of the pores of the carbon foam layers 11 and 13. Further,bonding material 22 may permeate the pores of carbon foam layers 11 and 13 by a depth equal to or greater than an average pore size oflayers - An
electrical connection element 21 is disposed withinbonding material 22 and provides an external, electrical connection forcurrent collector 20.Electrical connection element 21 includes atab 31 that extends beyond an edge of either or both of carbon foam layers 11 and 13.Electrical connection element 21 also includes at least one electrically conductive portion (not shown) that extends withincurrent collector 20.Electrical connection element 21 may be formed using various different conductive materials, such as but not limited to metals, suitable for providing an electrical connection to either or both of carbon foam layers 11 and 13. - In the exemplary embodiment shown in
FIGS. 2A and 2B ,bonding material 22 ofcurrent collector 20 is an electrically conductive material. For example,bonding material 22 may include a metal or an electrically conductive polymer. Becausebonding material 22 is electrically conductive, an external electrical connection tocurrent collector 20 may be made using only oneelectrical connection element 21. Particularly,tab 31 can make electrical contact to both carbon foam layers 11 and 13 throughbonding material 22. -
FIGS. 3A and 3B illustrate anothercurrent collector 40 including the composite material of the present invention. As shown inFIGS. 3A and 3B ,current collector 40 includes carbon foam layers 11 and 13 bonded together by abonding material 42. Similar to the bonding material ofcomposite material 10,bonding material 42 permeates at least some of the pores of the carbon foam layers 11 and 13. Further,bonding material 42 may permeate the pores of carbon foam layers 11 and 13 by a depth equal to or greater than an average pore size oflayers - In the exemplary embodiment shown in
FIGS. 3A and 3B ,bonding material 42 is an electrically insulating material. Becausebonding material 42 is electrically insulating, an external electrical connection tocurrent collector 40 may be made using twoelectrical connection elements 21. Particularly, when makingcurrent collector 40, a firstelectrical connection element 21 may be disposed on, for example,carbon foam layer 11. Then, bondingmaterial 42 is applied to both the first electrical connection element and tocarbon foam layer 11. Because electrically insulatingbonding material 42 coats the firstelectrical connection element 21, an additional electrical connection element may be required to make contact withcarbon foam layer 13, which is applied to thebonding material 42 to create a stacked structure. Therefore, prior to placingcarbon foam layer 13 onbonding material 42, a secondelectrical connection element 21 may be placed onbonding material 42. The secondelectrical connection element 21 provides an external electrical contact withcarbon foam layer 13. - Accordingly, two
electrical connection elements 21 are shown inFIG. 3B . Each resides at an interface betweenbonding material 42 and carbon foam layers 11 and 13, respectively.Electrical connection elements 21 may be configured with some open space or porosity so as not interfere with permeation ofbonding material 42 into the pores of the respective carbon foam layers. - While the exemplary embodiment of the present invention illustrated in
FIG. 3B includes twoelectrical connection elements 21, electrical connections to the carbon foam layers 11 and 13 may be accomplished through alternative configurations. For example, a singleelectrical connection element 21 may be configured such that electrically conductive portions 33 make electrical contact to both carbon foam layers 11 and 13. For example, conductive portions 33 may be arranged such that some of the conductive portions contactfoam layer 11 and other conductive portions contactfoam layer 13. Alternatively,electrical connection element 21 may be sized with a sufficient thickness relative to the thickness ofbonding material 42 such that asingle connection element 21 may contact both foam layers 11 and 13. In these exemplary instances, oneelectrical connection element 21 would be sufficient. -
FIG. 4 illustrates abattery 100 in accordance with an exemplary embodiment of the present invention.Battery 100 includes ahousing 110 andterminals 120, which are external tohousing 110. At least onecell 130 is disposed withinhousing 110. While only onecell 130 is necessary, multiple cells may be connected in series to provide a desired total potential ofbattery 100. - Each
cell 130 may be composed of alternating positive and negative plates immersed in an electrolytic solution including, for example, sulfuric acid and distilled water. Both the positive and negative plates include a current collector packed with a paste material, including, for example, an oxide of lead. As noted above,FIGS. 2A, 2B , 3A, and 3B illustratecurrent collectors battery 100. Chemical reactions in the paste disposed on the current collectors of the battery enable storage and release of energy. The composition of this paste, and not the material selected for the current collector, determines whether a given current collector functions as either a positive or a negative plate. - To create the positive and negative plates of
battery 100, a chemically active paste is applied tocurrent collectors current collectors pores 14 of thecurrent collectors - Once the paste has been deposited on
current collectors current collectors current collectors current collectors - When the positive and negative plates have been assembled together to form the cells of a battery 100 (shown in
FIG. 4 ),battery 100 is subjected to a charging (i.e., formation) process. During this charging process, the cured paste of the positive plate is electrically driven to lead dioxide (PbO2), and the paste of the negative plate is converted to sponge lead. Conversely, during subsequent discharge of thebattery 100, the pastes of both positive and negative plates convert toward lead sulfate. - The composite material of the present invention is useful in any of a wide variety of applications where materials with corrosion resistance, high surface area, electrical conductivity, or low weight would be desirable. In one possible application, the composite material of the present invention may serve as a current collector in a battery, such as a lead acid battery, for example. Current collectors may support the chemically active components of the battery and promote the flow of current between terminals of the battery.
- Because
current collectors - The carbon foam includes a network of pores, which provides a large amount of surface area for each
current collector current collectors current collectors current collectors electrical connection element 21, for example. - As a result, batteries with carbon foam
current collectors - The increased specific power values offered by batteries of the present invention may also translate into reduced charging times. Therefore, the batteries may be suitable for applications in which charging energy is available for only a limited amount of time. For instance, in vehicles, a great deal of energy is lost during ordinary braking. This braking energy may be recaptured and used to charge a battery of, for example, a hybrid vehicle. The braking energy, however, is available only for a short period of time (i.e., while braking is occurring). In view of their reduced charging times, the batteries of the present invention may provide an efficient means for storing such braking energy.
- The porous nature of the carbon foam current collectors also creates an improved substrate for retaining the chemically active paste of the energy storage device. By impregnating the paste into pores of the carbon foam current collectors, the paste is less likely to separate from the current collectors. This property is important in vehicle and other applications where vibration is common.
- Further, by including carbon foam current collectors having a density of less than about 0.6 g/cm3, a battery may weigh substantially less that batteries including either lead current collectors or graphite plate current collectors. Other aspects and features of the present invention can be obtained from a study of the drawings, the disclosure, and the appended claims.
Claims (20)
1. A composite material, comprising:
a first carbon foam structure including a network of pores;
a second carbon foam structure including a network of pores; and
an intermediate bonding structure disposed at least in part between the first and second carbon foam structures.
2. The composite material of claim 1 , wherein the intermediate bonding structure permeates at least some of the pores of the first carbon foam structure and at least some of the pores of the second carbon foam structure.
3. The composite material of claim 2 , wherein the intermediate bonding structure permeates the pores of the first carbon foam structure by a depth equal to or greater than an average pore size of the first carbon foam structure.
4. The composite material of claim 2 , wherein the intermediate bonding structure permeates the pores of the second carbon foam structure by a depth equal to or greater than an average pore size of the second carbon foam structure.
5. The composite material of claim 1 , wherein the intermediate bonding structure comprises a polymer.
6. The composite material of claim 5 , wherein the intermediate bonding structure comprises polypropylene.
7. The composite material of claim 1 , wherein the intermediate bonding structure comprises a metal.
8. The composite material of claim 1 , wherein the intermediate bonding structure comprises an electrically conductive material.
9. The composite material of claim 1 , wherein at least one of the first and second carbon foam structures is graphite foam.
10. The composite material of claim 1 , wherein at least one of the first and second carbon foam structures has a total porosity value of at least about 60%.
11. The composite material of claim 1 , wherein at least one of the first and second carbon foam structures has an open porosity value of at least about 90%.
12. The composite material of claim 1 , wherein each of the first and second carbon foam structures has an average pore size of between about 0.25 mm and about 2.0 mm.
13. A method of making a composite material, comprising:
providing a first carbon foam element including a network of pores;
applying bonding material to the first carbon foam element; and
placing a second carbon foam element, which includes a network of pores, on the bonding material.
14. The method of claim 13 , wherein applying the bonding material and placing the second carbon foam element forms a stacked structure, and wherein the method further comprises applying heat to the stacked structure.
15. The method of claim 14 further comprising applying pressure to the stacked structure.
16. The method of claim 15 , wherein the steps of applying pressure and applying heat are at least in part performed substantially simultaneously.
17. The method of claim 13 , further including forming a current collector for a battery by coupling a first electrical connection element with the first carbon foam element.
18. The method of claim 17 , wherein the layer of bonding material comprises an insulating material.
19. The method of claim 18 , further comprising coupling a second electrical connection element with the bonding material.
20-40. (canceled)