US20060051963A1 - Devices containing zirconium-platinum-containing materials and methods for preparing such materials and devices - Google Patents
Devices containing zirconium-platinum-containing materials and methods for preparing such materials and devices Download PDFInfo
- Publication number
- US20060051963A1 US20060051963A1 US11/215,569 US21556905A US2006051963A1 US 20060051963 A1 US20060051963 A1 US 20060051963A1 US 21556905 A US21556905 A US 21556905A US 2006051963 A1 US2006051963 A1 US 2006051963A1
- Authority
- US
- United States
- Prior art keywords
- platinum
- zirconium
- film
- complexes
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Methods for forming materials containing both zirconium and platinum, such as platinum-zirconium films, and articles containing such materials. The resultant films can be used as electrodes in an integrated circuit structure, particularly in a memory device such as a ferroelectric memory device. The platinum-zirconium materials can also be used in catalyst materials.
Description
- This is a divisional of application Ser. No. 10/680,038, filed Oct. 7, 2003 (pending), which is a divisional of application Ser. No. 09/653,513, filed Aug. 31, 2000, (issued), which are incorporated herein by reference.
- This invention relates to the preparation of zirconium- and platinum-containing materials, particularly films on substrates such as semiconductor device structures.
- Films of metals and metal oxides, particularly the heavier elements of Group VIII, are becoming important for a variety of electronic and electrochemical applications. This is at least because many of the Group VIII metal films are generally unreactive, resistant to diffusion of oxygen and silicon, and are good conductors. Oxides of certain of these metals also possess these properties, although perhaps to a different extent.
- Thus, films of Group VIII metals and metal oxides, particularly the second and third row metals (e.g., Ru, Os, Rh, Ir, Pd, and Pt) have suitable properties for a variety of uses in integrated circuits. For example, they can be used in integrated circuits for electrical contacts. They are particularly suitable for use as the plate (i.e., electrode) itself in capacitors. In addition, Group VIII metals are useful in catalysts.
- Platinum is one of the candidates for use as an electrode for high dielectric capacitors. Capacitors are the basic charge storage devices in random access memory devices, such as dynamic random access memory (DRAM) devices, static random access memory (SRAM) devices, and now ferroelectric memory (FE RAM) devices. They consist of two conductors, such as parallel metal or polysilicon plates, which act as the electrodes (i.e., the storage node electrode and the cell plate capacitor electrode), insulated from each other by a dielectric material (a ferroelectric dielectric material for FE RAMs). It is important for device integrity that oxygen and/or silicon not diffuse into or out of the dielectric material. This is particularly true for ferroelectric RAMs because the stoichiometry and purity of the ferroelectric material greatly affect charge storage and fatigue properties. Also, oxidation of the underlying silicon will result in decreased series capacitance, thus degrading the cell capacitor.
- In order to function well in a bottom electrode, the electrode film or film stack must be able to withstand the high temperature anneals required to recrystallize the dielectric layer. As stated above, platinum is one of the candidates for use as an electrode material for high dielectric capacitors. Platinum, alone, however, in the form of films deposited by chemical vapor deposition techniques can be unstable when annealed at temperatures 650° C. and above. For example, as shown in
FIG. 1 , a platinum layer can form islands during the anneal process, which suggests high mobility of platinum at temperatures far below its melting temperature. One solution is to combine (e.g., alloy) the platinum with rhodium to enhance the barrier properties and stability of the layer; however, rhodium precursors can be very expensive. - Thus, there is a continuing need for methods and materials for the deposition of stable platinum-containing films, particularly those that can be subjected to relatively high annealing temperatures.
- The present invention is directed to methods for forming materials containing both zirconium and platinum. Preferably the materials are films deposited on substrates, such as those formed in the manufacture of a semiconductor device, such as a ferroelectric device. The substrates are preferably semiconductor substrates or substrate assemblies. Preferably, the films are formed by various vapor deposition techniques, preferably, chemical vapor deposition techniques.
- Significantly and preferably, the zirconium, which is typically in the form of an oxide (zirconia) stabilizes the platinum film, such that upon annealing at temperatures of at least about 650° C. there are substantially no signs of island formation. Thus, zirconium serves to mechanically stabilize platinum films against migration during annealing. Surprisingly, this occurs without substantially degrading the conductivity of the film.
- Typically and preferably, the films are electrically conductive. The resultant film can be used as an electrode in an integrated circuit structure, particularly in a memory device such as a ferroelectric memory device. The platinum-zirconium films (i.e., layers) overcome some of the problems associated with the use of platinum alone as an electrode material, without adversely affecting the properties of the platinum layer, such as its electrical conductivity.
- Other materials that can be formed using the present invention include catalyst materials. Such materials typically include a roughened surface (e.g., a surface that includes a plurality of columnar pedestals, preferably that are at least about 400 Angstroms tall).
- In the context of the present invention, the term “metal-containing film” includes, complexes of zirconium and platinum with other elements (e.g., O, N, and S), particularly oxygen, and/or other metals or metalloids. Zirconia (ZrO2) is a particularly desirable component of a metal-containing film because of its ability to stabilize platinum films against migration during annealing without substantially degrading the conductivity of the film, as described herein.
- One preferred method of the present invention involves forming a film on a substrate, such as a semiconductor substrate or substrate assembly during the manufacture of a semiconductor structure. The method includes: providing a substrate (preferably, a semiconductor substrate or substrate assembly); providing a precursor composition that includes one or more zirconium complexes; providing a precursor composition that includes one or more platinum complexes; and forming a platinum-zirconium-containing film from the precursor compositions on a surface of the substrate (preferably, the semiconductor substrate or substrate assembly). Preferably, the precursor composition that includes one or more zirconium complexes is the same as the precursor composition that includes one or more platinum complexes.
- In certain embodiments, the process is carried out in a nonhydrogen atmosphere (i.e., an atmosphere that does not include H2), and preferably in an oxidizing atmosphere. Using such methods, the precursor complexes of zirconium and platinum are converted in some manner (e.g., decomposed thermally while ligands are oxidized) and deposited on a surface to form a metal-containing film. Thus, the film is not simply a film of the complex of the precursors. Herein, “platinum-zirconium film” and “platinum-zirconium-containing film” are used interchangeably. Preferably, such films are in the form of a platinum-zirconia-containing film, also referred to herein as a platinum-zirconia (Pt—ZrO2) film.
- Preferably, the precursor complexes are neutral complexes and may be liquids or solids at room temperature. Typically, however, they are liquids. If they are solids, they are preferably sufficiently soluble in an organic solvent or have melting points below their decomposition temperatures such that they can be used in flash vaporization, bubbling, microdroplet formation techniques, etc. However, they may also be sufficiently volatile that they can be vaporized or sublimed from the solid state using known vapor deposition techniques including chemical vapor deposition and atomic layer deposition techniques. Thus, the precursor compositions of the present invention can be in solid or liquid form. As used herein, “liquid” refers to a solution or a neat liquid (a liquid at room temperature or a solid at room temperature that melts at an elevated temperature). As used herein, a “solution” does not require complete solubility of the solid; rather, the solution may have some undissolved material, preferably, however, there is a sufficient amount of the material that can be carried by the organic solvent into the vapor phase for chemical vapor deposition processing.
- The methods described herein preferably involve the use of vapor deposition techniques such as chemical vapor deposition and atomic layer deposition, although this is not a requirement for all embodiments. That is, for certain embodiments, sputtering, spin-on coating, etc., can be used.
- The present invention also provides a capacitor. In one embodiment, the capacitor includes: a first conductive layer; a dielectric material on at least a portion of the first conductive layer; and a second conductive layer on the dielectric material; wherein at least one of the first and second layers includes a platinum-zirconium film (preferably, a vapor-deposited film, i.e., a film deposited by vapor deposition methods that includes platinum and zirconium, preferably in the form of platinum-zirconia (Pt—ZrO2)).
- The present invention also provides an integrated circuit that includes a capacitor. In one embodiment, the capacitor includes: a first conductive layer; a dielectric material on at least a portion of the first conductive layer; and a second conductive layer on the dielectric material; wherein at least one of the first and second conductive layers includes a (preferably, vapor-deposited) platinum-zirconium film.
- The present invention also provides a memory cell. In one embodiment, the memory cell includes: a transistor; and a capacitor that includes a (preferably, vapor-deposited) platinum-zirconium film. Preferably, the capacitors are as described above.
- The present invention also provides methods of fabricating capacitors. In one embodiment, a method involves: forming a first conductive layer; forming a dielectric layer on at least a portion of the first conductive layer; and forming a second conductive layer on the dielectric layer; wherein at least one of the first and second conductive layers includes a (preferably, vapor-deposited) platinum-zirconium film. Preferably, the conductive layer is formed by chemical vapor co-deposition of platinum and zirconium precursor compositions.
- In another embodiment of a method for fabricating a capacitor having a first and a second electrode, the method includes: providing a substrate; forming an insulative layer overlying a substrate; forming an opening in the insulative layer to expose the substrate; forming a conductive plug in the opening, the conductive plug forming a first portion of the first electrode of the capacitor, the conductive plug recessed below a surface of the insulative layer; forming a first conductive layer in the opening and overlying the conductive plug such that the first conductive layer is surrounded on sidewalls by the insulative layer, the first conductive layer forming a second portion of the first electrode, the first conductive layer being formed of a (preferably, vapor-deposited) platinum-zirconium film; and forming a second conductive layer overlying the first conductive layer, the second conductive layer forming a third portion of the first electrode. Preferably, the method further includes: creating a dielectric layer on the second conductive layer, the first conductive layer substantially preventing oxidation of the dielectric layer; and creating the second electrode overlying the dielectric layer, the first and the second electrode and the dielectric layer forming the capacitor. Preferably, forming the second electrode includes sputtering an electrically conductive material to overly the dielectric layer. Preferably, forming the first conductive layer includes: admitting a platinum precursor composition to a chemical vapor deposition reaction chamber; admitting a zirconium precursor composition to the chemical vapor deposition reaction chamber; and applying sufficient reaction gas to the chemical vapor deposition reaction chamber to cause co-deposition of platinum and zirconium. Preferably, the method further includes planarizing the insulative layer prior to forming the conductive plug. Preferably, forming the conductive plug includes depositing in-situ doped polysilicon in the opening.
- In another embodiment, there is a method of manufacturing a catalyst, the method includes: providing a substrate; providing a precursor composition including one or more zirconium complexes; providing a precursor composition including one or more platinum complexes; and forming a platinum-zirconium-containing material from the precursor compositions on a surface of the substrate to form a catalyst. Preferably, forming a platinum-zirconium-containing material occurs in the presence of an oxidizing gas.
- The present invention also provides a method of stabilizing a platinum film upon annealing the film at temperatures at least about 650° C., the method includes incorporating zirconium into the platinum film. Preferably, the zirconium is at least partially oxidized. As used herein, “stable” means that there are substantially no signs of island formation after annealing the platinum-zirconium film at a temperature of at least about 650° C. Significantly and advantageously, this zirconium incorporation preferably does not substantially degrade the conductivity of the platinum film.
- Preferably, in the methods and articles described herein, the platinum-zirconium films are platinum-zirconia films (Pt—ZrO2-containing films). Typically, whether partially or completely oxidized or including other elements, the films include platinum and zirconium in a ratio of platinum(x):zirconium(1−x), wherein x is in the range of about 0.99 to about 0.01. Preferably, the dielectric layer is selected from the group consisting of tantalum pentoxide (Ta2O5), Barium Strontium Titanate (BST), Strontium Titanate (ST), Lead Zirconium Titanate (PZT), Strontium Bismuth Tantalate (SBT) and Bismuth Zirconium Titanate (BZT).
- In the methods described herein, preferably, the platinum precursor composition includes a platinum complex selected from the group consisting of CpPt(Me)3, wherein Me is a methyl group and Cp is substituted or unsubstituted cyclopentadienyl, Pt(CO)2Cl2, cis-Pt(CH3)2[(CH3)NC]2, (COD)Pt(CH3)2, (COD)Pt(CH3)Cl, (C5H5)Pt(CH3)(CO), (acac)(Pt)(CH3)3, Pt(acac)2, Pt(PF 3)4, wherein COD=1,5-cycloctadiene and acac=acetylacetonate (CH3C(O)CH═C(O)CH3), and mixtures thereof. More preferably, the platinum precursor composition includes CpPt(Me)3, wherein Me is a methyl group and Cp is methyl cyclopentadienyl (also written as MeCp). Preferably, the platinum complexes do not include halogen atoms.
- In the methods described herein, preferably the zirconium precursor composition includes one or more complexes of zirconium tert-butoxide (Zr(OC(CH3)3)4), zirconium butoxide (Zr(O(CH2)3CH3)4), zirconium propoxide (Zr(O(CH2)2CH3)4), and zirconium acetylacetonate (Zr(acac)4), and mixtures thereof.
- Methods of the present invention are particularly well suited for forming films on a surface of a semiconductor substrate or substrate assembly, such as a silicon wafer, with or without layers or structures formed thereon, used in forming integrated circuits. It is to be understood that methods of the present invention are not limited to deposition on silicon wafers; rather, other types of wafers (e.g., gallium arsenide wafer, etc.) and silicon on glass can be used as well. Also, the methods of the present invention can be used in silicon-on-insulator technology. Furthermore, substrates other than semiconductor substrates or substrate assemblies can be used in methods of the present invention. These include, for example, fibers, wires, etc., as well as substrates used in catalytic systems, such as catalytic converters in automobiles. If the substrate is a semiconductor substrate or substrate assembly, the films can be formed directly on the lowest semiconductor surface of the substrate, or they can be formed on any of a variety of the layers (i.e., surfaces) as in a patterned wafer, for example. Thus, the term “semiconductor substrate” refers to the base semiconductor layer, e.g., the lowest layer of silicon material in a wafer or a silicon layer deposited on another material such as silicon on sapphire. The term “semiconductor substrate assembly” refers to the semiconductor substrate having one or more layers or structures formed thereon.
-
FIG. 1 is a scanning electron micrograph of a platinum film deposited at a thickness of less than 500 Angstroms on silicon after rapid thermal oxidation at 700° C. and atmospheric pressure for 1 minute. -
FIG. 2 is a cross-sectional schematic of a thin layer ferroelectric memory device having a conductive platinum-zirconium-containing electrode. -
FIG. 3 is a schematic of a chemical vapor deposition system suitable for use in the method of the present invention. -
FIG. 4 is a schematic of an alternative chemical vapor deposition system suitable for use in the method of the present invention. -
FIG. 5 is a diagrammatic cross-sectional view taken along a portion of a semiconductor wafer at an early processing step according to one embodiment of the present invention. -
FIG. 6 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown inFIG. 5 . -
FIG. 7 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown inFIG. 6 . -
FIG. 8 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown inFIG. 7 . -
FIG. 9 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown inFIG. 8 . -
FIG. 10 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown inFIG. 9 . -
FIG. 11 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown inFIG. 10 . -
FIG. 12 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown inFIG. 11 . -
FIG. 13 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown inFIG. 12 . -
FIG. 14 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown inFIG. 13 . -
FIG. 15 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown inFIG. 14 . -
FIG. 16 is an Auger depth profile of a Pt—ZrO2 film deposited by CVD after anneal in oxygen at 700° C. for 60 seconds. -
FIG. 17 is a scanning electron micrograph of a Pt—ZrO2 film deposited by CVD conditions described in the Examples Section. -
FIG. 18 is a scanning electron micrograph of a cross-section of a Pt—ZrO2 film deposited by CVD after anneal in oxygen at 700° C. for 60 seconds. -
FIG. 19 is a scanning electron micrograph of a Pt—ZrO2 film deposited by CVD after anneal in oxygen at 700° C. for 60 seconds. The sheet resistance of this film was 2.0 ohm/square, corresponding to a resistivity of 10 microohms-centimeter. - The present invention provides structures and devices containing a platinum- and zirconium-containing material (e.g., film or layer), preferably an electrically conductive platinum- and zirconium-containing film, and methods of forming these materials. Specifically, the present invention is directed to methods of manufacturing a semiconductor device, particularly a ferroelectric device, having a platinum-zirconium-containing film. The platinum-zirconium-containing films formed are preferably conductive and can be used as the plate (i.e., electrode) in capacitors, in memory devices, such as ferroelectric memories, for example. They can be deposited in a wide variety of thicknesses and forms, depending on the desired use.
- The materials of the present invention are also suitable for use in the formation of catalyst materials as well or other materials that involve a roughened surface. Examples of platinum-containing materials having a roughened surface are disclosed in U.S. Pat. No. 5,990,559 (Marsh). Such materials typically include a roughened surface that includes a plurality of columnar pedestals, preferably that are at least about 400 Angstroms tall. The methods disclosed in U.S. Pat. No. 5,990,559 (Marsh) can be used to form roughened platinum-zirconium surfaces if both platinum and zirconium precursors are vapor deposited in the presence of an oxidizing gas, particularly one that is a strong oxidizer at elevated temperatures.
- Preferred platinum-zirconium materials (e.g., films or layers) are formed on a surface of a substrate, preferably, a semiconductor substrate or substrate assembly during the manufacture of semiconductor structures. More preferably, platinum-zirconium films are formed on a silicon-containing surface. Such materials may be used in the fabrication of semiconductor devices as an electrode or within a stack of layers forming an electrode. One skilled in the art will recognize that various semiconductor processes and structures for various devices (CMOS devices, memory devices, etc.), would benefit from the characteristics of the platinum-zirconium layers of the present invention. In no manner is the present invention limited to the illustrative embodiments described herein.
- A preferred platinum-zirconium film according to the present invention includes an atomic composition of platinum(x):zirconium(1−x), where preferably, x is in the range of about 0.01 to about 0.99. This atomic composition does not take into consideration the optional presence of oxygen and other elements. It is merely a representation of the relative ratio of platinum and zirconium. More preferably, x is in the range of about 0.3 to about 0.9, and most preferably, x is about 0.6. Preferably, the amount of zirconium desired in the platinum layer to accomplish stability is within a range of about 1 atom percent to about 30 atom percent, and more preferably, about 5 atom percent to about 20 atom percent zirconium. Preferably, at least a portion of the zirconium is oxidized. In other words, preferably, the atomic composition of the platinum-zirconium film is about 55% platinum, 15% zirconium, and about 30% oxygen. Preferably, a platinum-zirconium film (i.e., platinum-zirconium layer) will have a uniform composition throughout its thickness, although this is not a necessary requirement. For example, platinum could be deposited first and then a combination of zirconium and platinum could be deposited with increasing amounts of zirconium as the film is formed.
- The thickness of the platinum-zirconium layer is dependent upon the application for which it is used. Preferably, the thickness is in the range of about 10 Angstroms to about 10,000 Angstroms. More preferably, the thickness is in the range of about 100 Angstroms to about 500 Angstroms. For example, this preferred thickness range of about 100 Angstroms to about 500 Angstroms is applicable to a single platinum-zirconium layer forming an electrode of a capacitor.
- The present invention also provides methods of forming a metal-containing film, preferably using one or more zirconium complexes and one or more platinum complexes. These zirconium and platinum complexes are typically mononuclear (i.e., monomers in that they contain one metal per molecule), although they can be in the form of weakly bound dimers (i.e., dimers containing two monomers weakly bonded together through hydrogen or dative bonds). Herein, such monomers and weakly bound dimers are shown as mononuclear complexes.
- A preferred platinum-zirconium film may be formed by vapor deposition from precursor compounds (typically, organometallic precursor compounds), as opposed to physical deposition (e.g., sputtering) techniques, because of the ability of these methods to form conformal layers. That is, vapor deposition techniques are desired because they are more suitable for deposition on semiconductor substrates or substrate assemblies, particularly in contact openings which are extremely small and require conformally filled layers of metal. Such methods typically involve various forms of chemical vapor deposition (CVD), for example, atmospheric pressure chemical vapor deposition, low pressure chemical vapor deposition (LPCVD), plasma enhanced chemical vapor deposition (PECVD), or any other chemical vapor deposition technique. Another vapor deposition technique called atomic layer deposition (ALD) can also be used. This method involves the formation of a monomolecular layer of a precursor compound, which is then contacted with a reaction gas, as disclosed in Pathangey et al., “Atomic Layer Deposition for Nanoscale Thin Film Coatings”, Vacuum Technology and Coating, pages 32-41, May 2000. A preferred deposition process includes the use of separate platinum and zirconium precursors, although one compound could be envisioned to provide both metals.
- A wide variety of platinum and zirconium complexes suitable for deposition via CVD or ALD can be used in the process of the invention. The zirconium precursor is preferably of Formula I shown below, which is shown as a monomer, although weakly bound dimers are also possible. The platinum precursor is preferably of Formula II shown below, which is shown as a monomer, although weakly bound dimers are also possible. Although these compounds are preferred, a wide variety of precursors can be used as long as they can be used in a vapor deposition process.
- The zirconium and platinum complexes, which are preferably of Formulae I and II below, are neutral complexes and may be liquids or solids at room temperature. Typically, they are liquids. If they are solids, they are sufficiently soluble in an organic solvent to allow for vaporization, they can be vaporized or sublimed from the solid state, or they have melting temperatures below their decomposition temperatures. Thus, many of the complexes described herein are suitable for use in vapor deposition techniques, preferably chemical vapor deposition (CVD) techniques, such as flash vaporization techniques, bubbler techniques, and/or microdroplet techniques. Preferred embodiments of the complexes described herein are particularly suitable for low temperature CVD, e.g., deposition techniques involving substrate temperatures of about 100° C. to about 400° C., preferably in an oxidizing atmosphere.
- The solvents that are suitable for this application can be one or more of the following: saturated or unsaturated linear, branched, or cyclic aliphatic (alicyclic) hydrocarbons (C3-C20, and preferably C5-C10), aromatic hydrocarbons (C5-C20, and preferably C5-C10), halogenated hydrocarbons, silylated hydrocarbons such as alkylsilanes, alkylsilicates, ethers, polyethers, thioethers, esters, lactones, ammonia, amides, amines (aliphatic or aromatic, primary, secondary, or tertiary), polyamines, nitrites, cyanates, isocyanates, thiocyanates, silicone oils, aldehydes, ketones, diketones, carboxylic acids, water, alcohols, thiols, or compounds containing combinations of any of the above or mixtures of one or more of the above. It should be noted that some precursor complexes are sensitive to reactions with protic solvents, and examples of these noted above may not be ideal, depending on the nature of the precursor complex. They are also generally compatible with each other, so that mixtures of variable quantities of the complexes will not interact to significantly change their physical properties.
- One preferred method of the present invention involves vaporizing a precursor composition that includes one or more zirconium complexes and preferably one or more platinum complexes. Also, the precursor composition can include complexes containing other metals or metalloids.
- The precursor composition can be vaporized in the presence of an inert carrier gas and/or a reaction gas to form a relatively pure platinum-zirconia film or other platinum-zirconium films including other Group VIII metals or oxides. The inert carrier gas is typically selected from the group consisting of nitrogen, helium, argon, and mixtures thereof. In the context of the present invention, an inert carrier gas is one that is generally unreactive with the complexes described herein and does not interfere with the formation of a platinum-zirconium-containing film. The reaction gas can be selected from a wide variety of gases reactive with the complexes described herein, at least at a surface under the conditions of chemical vapor deposition. Examples of reaction gases include hydrogen, oxidizing gases such as H2O, H2O2, O2, O3, N2O, SO3, as well as H2S, H2Se, SiH4, NH3, N2H4, Si2H6. Preferably, the reaction gas is a nonhydrogen gas (i.e., a gas that is not H2). Various combinations of carrier gases and/or reaction gases can be used in the methods of the present invention to form zirconium-containing films. Thus, the platinum-zirconium-containing film can include oxygen, sulfur, nitrogen, hydrogen, selenium, silicon, or combinations thereof. Preferably, the reaction gas is an oxidizing gas, particularly one that is a strong oxidizer at elevated temperatures if a roughened surface is desired.
- Such metal-containing films can be formed by subjecting a relatively pure metal-containing film to subsequent processing, such as annealing or rapid thermal oxidation, to form other metal-containing films, such as oxides or silicides, for example. For example, the rapid thermal oxidation (RTO) of a platinum-zirconium film deposited, for example, by physical vapor deposition, could form an oxide. Examplary RTO conditions include a temperature of about 650° C. to about 700° C. in an oxygen atmosphere for 1 minute.
- The zirconium complex is preferably of the following formula, which is shown as a monomer, although weakly bound dimers are also possible:
Zr(OR)4 (Formula I)
wherein R is an organic group. Preferably, each R group in the complexes of Formula I is independently a (C1-C8) organic group. More preferably, each R group is a (C1-C5) organic group. Most preferably, each R group is a (C1-C4) alkyl moiety. Examples include zirconium tert-butoxide (Zr(OC(CH3)3)4), zirconium butoxide (Zr(O(CH2)3CH3)4), zirconium propoxide (Zr(O(CH2)2CH3)4), and zirconium acetylacetonate (Zr(acac)4), and mixtures thereof. Other zirconium complexes are also suitable, such as amines, for example, as long as the ligands are capable of being oxidized and removed from the metal during vapor deposition. - The platinum precursor is preferably a platinum complex as shown in Formula II:
CpPt(Me)3 (Formula II) -
- where Me is a methyl group and Cp is cyclopentadienyl, which may be substituted or unsubstituted (preferably, Cp is methylcyclopentadienyl, often written as MeCp). Other platinum complexes that can be used in addition or in place of the complex of Formula II include, for example, Pt(CO)2Cl2, cis-Pt(CH3)2[(CH3)NC]2, (COD)Pt(CH3)2, (COD)Pt(CH3)Cl, (C5H5)Pt(CH3)(CO),(acac)(Pt)(CH3)3, Pt(acac)2, and Pt(PF3)4, wherein COD=1,5-cycloctadiene and acac=acetylacetonate.
- For certain embodiments, the precursor compositions may be used in the range of from about 1 percent to about 99 percent of a zirconium precursor, more preferably about 5 percent to about 50 percent of a zirconium precursor, and most preferably, about 10 percent of Formula I (Zr precursor) and about 90 percent of Formula II (Pt precursor), wherein the percentages are based on mole percents.
- As used herein, the term “organic group” means a hydrocarbon group (with optional elements other than carbon and hydrogen, such as oxygen, nitrogen, sulfur, and silicon) that is classified as an aliphatic group, cyclic group, or combination of aliphatic and cyclic groups (e.g., alkaryl and aralkyl groups). In the context of the present invention, the organic groups are those that do not interfere with the formation of a metal-containing film. Preferably, they are of a type and size that do not interfere with the formation of a metal-containing film using chemical vapor deposition techniques. The term “aliphatic group” means a saturated or unsaturated linear or branched hydrocarbon group. This term is used to encompass alkyl, alkenyl, and alkynyl groups, for example. The term “alkyl group” means a saturated linear or branched hydrocarbon group including, for example, methyl, ethyl, isopropyl, t-butyl, heptyl, dodecyl, octadecyl, amyl, 2-ethylhexyl, and the like. The term “alkenyl group” means an unsaturated, linear or branched hydrocarbon group with one or more carbon-carbon double bonds, such as a vinyl group. The term “alkynyl group” means an unsaturated, linear or branched hydrocarbon group with one or more carbon-carbon triple bonds. The term “cyclic group” means a closed ring hydrocarbon group that is classified as an alicyclic group, aromatic group, or heterocyclic group. The term “alicyclic group” means a cyclic hydrocarbon group having properties resembling those of aliphatic groups. The term “aromatic group” or “aryl group” means a mono- or polynuclear aromatic hydrocarbon group. The term “heterocyclic group” means a closed ring hydrocarbon in which one or more of the atoms in the ring is an element other than carbon (e.g., nitrogen, oxygen, sulfur, etc.).
- Substitution is anticipated on the organic groups of the complexes of the present invention. As a means of simplifying the discussion and recitation of certain terminology used throughout this application, the terms “group” and “moiety” are used to differentiate between chemical species that allow for substitution or that may be substituted and those that do not allow or may not be so substituted. Thus, when the term “group” is used to describe a chemical substituent, the described chemical material includes the unsubstituted group and that group with O, N, Si, or S atoms, for example, in the chain (as in an alkoxy group) as well as carbonyl groups or other conventional substitution. Where the term “moiety” is used to describe a chemical compound or substituent, only an unsubstituted chemical material is intended to be included. For example, the phrase “alkyl group” is intended to include not only pure open chain saturated hydrocarbon alkyl substituents, such as methyl, ethyl, propyl, t-butyl, and the like, but also alkyl substituents bearing further substituents known in the art, such as hydroxy, alkoxy, alkylsulfonyl, halogen atoms, cyano, nitro, amino, carboxyl, etc. Thus, “alkyl group” includes ether groups, haloalkyls, nitroalkyls, carboxyalkyls, hydroxyalkyls, sulfoalkyls, etc. On the other hand, the phrase “alkyl moiety” is limited to the inclusion of only pure open chain saturated hydrocarbon alkyl substituents, such as methyl, ethyl, propyl, t-butyl, and the like.
- A preferred class of complexes of Formula I include those of the formula (Zr(OR)4, where ‘R’ represents one or more substituents such as methyl, ethyl, etc. This class of complexes of Formula I is particularly advantageous because they are liquids and can be delivered to the CVD chamber using simple bubbler techniques.
- Various combinations of the complexes described herein can be used in a precursor composition. Thus, as used herein, a “precursor composition” refers to a liquid or solid that includes one or more complexes of the formulas described herein optionally mixed with one or more complexes of formulas other than those described herein. The complexes of Formulae I and II can be provided in one precursor composition or in separate compositions. The precursor composition can also include one or more organic solvents suitable for use in a chemical vapor deposition system, as well as other additives, such as free ligands, that assist in the vaporization of the desired compounds.
- The complexes described herein can be used in precursor compositions for vapor deposition techniques, preferably, chemical vapor deposition (CVD) or atomic layer deposition (ALD). Alternatively, certain complexes described herein can be used in other deposition techniques, such as sputtering, spin-on coating, and the like. Typically, those complexes containing R groups with a low number of carbon atoms (e.g., 1-4 carbon atoms per R group) are suitable for use with vapor deposition techniques. Those complexes containing R groups with a higher number of carbon atoms (e.g., 5-12 carbon atoms per R group) are generally suitable for spin-on or dip coating. Preferably, however, vapor deposition techniques are desired because they are more suitable for deposition on semiconductor substrates or substrate assemblies, particularly in contact openings which are extremely small and require conformally filled layers of metal.
- For the preparation of zirconium-platinum films, at least one complex of Formula I can be combined with another complex in a precursor composition. For example, Zr(tert-butoxide)4 can be combined with MeCpPt(Me)3 to form an Pt/ZrO2 film. The precursor complexes used in the present invention can be prepared by a variety of methods known to one of skill in the art or are commercially available.
- As stated above, the use of the zirconium complexes and platinum complexes and methods of forming conductive platinum-zirconium-containing films of the present invention are beneficial for a wide variety of thin film applications in integrated circuit structures, particularly those using high dielectric materials or ferroelectric materials. For example, such applications include capacitors such as planar cells, trench cells (e.g., double sidewall trench capacitors), stacked cells (e.g., crown, V-cell, delta cell, multi-fingered, or cylindrical container stacked capacitors), as well as field effect transistor devices.
- A specific example of where a film formed from the complexes of the present invention would be useful is the
ferroelectric memory cell 10 ofFIG. 2 . Thememory cell 10 includes aferroelectric material 11, such as a lead zirconate titanate (PZT) or lithium niobate film, between twoelectrodes bottom electrode 13 is typically in contact with a silicon-containinglayer 14, such as an n-type or p-type silicon substrate, silicon dioxide, glass, etc. Aconductive barrier layer 15 is positioned between thebottom electrode 13 and the silicon-containinglayer 14 to act as a barrier to diffusion of atoms such as silicon into the electrode and ferroelectric material. - Methods of the present invention can be used to deposit a metal-containing film on a variety of substrates, such as a semiconductor wafer (e.g., silicon wafer, gallium arsenide wafer, etc.), glass plate, etc., and on a variety of surfaces of the substrates, whether it be directly on the substrate itself or on a layer of material deposited on the substrate as in a semiconductor substrate assembly. The film is deposited upon decomposition (typically, thermal decomposition) of a zirconium complex of Formula I in combination with a platinum complex, preferably ones that are either volatile liquids, sublimable solids, or solids that are soluble in a suitable solvent that is not detrimental to the substrate, other layers thereon, etc. Preferably, however, solvents are not used; rather, the transition metal complexes are liquid and used neat. Methods of the present invention preferably utilize vapor deposition techniques, such as flash vaporization, bubbling, etc.
- A typical chemical vapor deposition (CVD) system that can be used to perform the process of the present invention is shown in
FIG. 3 . The system includes an enclosed chemicalvapor deposition chamber 10, which may be a cold wall-type CVD reactor. As is conventional, the CVD process may be carried out at pressures of from atmospheric pressure down to about 10−3 torr, and preferably from about 10 torr to about 0.1 torr. A vacuum may be created inchamber 10 usingturbo pump 12 andbacking pump 14. - One or more substrates 16 (e.g., semiconductor substrates or substrate assemblies) are positioned in
chamber 10. A constant nominal temperature is established for the substrate, preferably at a temperature of about 50° C. to about 600° C., and more preferably at a temperature of about 100° C. to about 400°C. Substrate 16 may be heated, for example, by anelectrical resistance heater 18 on whichsubstrate 16 is mounted. Other known methods of heating the substrate may also be utilized. - In this process, if only one precursor composition is used, the
precursor composition 40, which contains one or more zirconium complexes (and/or other metal or metalloid complexes), is stored in liquid form (a neat liquid at room temperature or at an elevated temperature if solid at room temperature) invessel 42. Asource 44 of a suitable inert gas is pumped intovessel 42 and bubbled through the neat liquid (i.e., without solvent) picking up the precursor composition and carrying it intochamber 10 throughline 45 andgas distributor 46. Additional inert carrier gas or reaction gas may be supplied fromsource 48 as needed to provide the desired concentration of precursor composition and regulate the uniformity of the deposition across the surface ofsubstrate 16. Valves 50-55 are opened and closed as required. - If two precursor compositions are used in this process, such as when a platinum-zirconium film is formed, the
precursor composition 240, which contains one or more platinum complexes (and/or other metal or metalloid complexes), is stored in liquid form (a neat liquid at room temperature or at an elevated temperature if solid at room temperature) invessel 242. Asource 244 of a suitable inert gas is pumped intovessel 242 and bubbled through the neat liquid (i.e., without solvent) picking up the precursor composition and carrying it intochamber 10 throughline 245 andgas distributor 46. Additional inert carrier gas or reaction gas may be supplied fromsource 248 as needed to provide the desired concentration of precursor composition and regulate the uniformity of the deposition across the surface ofsubstrate 16. Valves 250-253 and 255 are opened and closed as required. - Preferably, for the preparation of a platinum-zirconium film, within the reaction chamber, the partial pressure of zirconium precursor gas is kept sufficiently low such that the zirconium deposited is within the ranges described herein for forming the preferred composition of the film. This partial pressure may be controlled by controlling the flow of the carrier gas, e.g., helium, through the bubbler containing the zirconium precursor or through control of other parameters of the process, such as temperature and pressure of the bubbler.
- Generally, the precursor composition or compositions, and optional reaction gases, are pumped into the
CVD chamber 10 at a flow rate of about 1 sccm (standard cubic centimeters) to about 1000 sccm. The semiconductor substrate is exposed to the precursor composition at a pressure of about 0.001 torr to about 100 torr for a time of about 0.01 minute to about 100 minutes. Inchamber 10, the precursor composition will form an adsorbed layer on the surface of thesubstrate 16. As the deposition rate is temperature dependent in a certain temperature range, increasing the temperature of the substrate will increase the rate of deposition. Typical deposition rates are about 10 Angstroms/minute to about 1000 Angstroms/minute. The carrier gas containing the precursor composition(s) is terminated by closing valve 53 (and 253). - An alternative CVD system that can be used to perform the process of the present invention is shown in
FIG. 4 . The system includes an enclosed chemicalvapor deposition chamber 90, which may be a cold wall-type CVD reactor, in which a vacuum may be created usingturbo pump 92 andbacking pump 94. One or more substrates 96 (e.g., semiconductor substrates or substrate assemblies) are positioned inchamber 90. Substrate 96 may be heated as described with reference toFIG. 3 (for example, by an electrical resistance heater 98). - In this process, one or
more solutions 60 of one or more precursor zirconium and precursor platinum complexes (and/or other metal or metalloid complexes) are stored invessels 62. The solutions are transferred to a mixingmanifold 64 using pumps 66. The resultant precursor composition (or compositions) containing one or more precursor complexes and one or more organic solvents is then transferred alongline 68 tovaporizer 70, to volatilize the precursor composition. Asource 74 of a suitable inert gas is pumped intovaporizer 70 for carrying volatilized precursor composition intochamber 90 throughline 75 andgas distributor 76. Reaction gas may be supplied fromsource 78 as needed. As shown, a series of valves 80-85 are opened and closed as required. Similar pressures and temperatures to those described with reference toFIG. 3 can be used. - Alternatives to such methods include an approach wherein the precursor composition is heated and vapors are drawn off and controlled by a vapor mass flow controller, and a pulsed liquid injection method as described in “Metalorganic Chemical Vapor Deposition By Pulsed Liquid Injection Using An Ultrasonic Nozzle: Titanium Dioxide on Sapphire from Titanium (IV) Isopropoxide,” by Versteeg, et al., Journal of the American Ceramic Society, 78, 2763-2768 (1995). The complexes described herein are also particularly well suited for use with vapor deposition systems, as described in copending application U.S. Ser. No. 08/720,710 entitled “Method and Apparatus for Vaporizing Liquid Precursors and System for Using Same,” filed on Oct. 2, 1996. Generally, one method described therein involves the vaporization of a precursor composition in liquid form (neat or solution). In a first stage, the precursor composition is atomized or nebulized generating high surface area microdroplets or mist. In a second stage, the constituents of the microdroplets or mist are vaporized by intimate mixture of the heated carrier gas. This two stage vaporization approach provides a reproducible delivery for precursor compositions (either in the form of a neat liquid or solid dissolved in a liquid medium) and provides reasonable growth rates, particularly in device applications with small dimensions.
- Various combinations of carrier gases and/or reaction gases can be used in certain methods of the present invention. They can be introduced into the chemical vapor deposition chamber in a variety of manners, such as directly into the vaporization chamber or in combination with the precursor composition.
- Although specific vapor deposition processes are described by reference to the figures, methods of the present invention are not limited to being used with the specific vapor deposition systems shown. Various CVD process chambers or reaction chambers can be used, including hot wall or cold wall reactors, atmospheric or reduced pressure reactors, as well as plasma enhanced reactors. Furthermore, methods of the present invention are not limited to any specific vapor deposition techniques.
- A specific example of a fabrication process for a capacitor according to one embodiment of the present invention is described below. It is to be understood, however, that this process is only one example of many possible configurations and processes utilizing the zirconium-containing layers (e.g., Pt—Zr electrodes) of the invention. For example, in the process described below, a Pt—Zr material is utilized as an electrode of a capacitor. In addition, in the process described below the bit line is formed over the capacitor. A buried bit-line process could also be used. As another example, the plugs under the capacitors formed by the following process could be eliminated. Also, dry or wet etching could be used rather than chemical mechanical polishing. The invention is not intended to be limited by the particular process described below.
- Referring to
FIG. 5 , a semiconductor wafer fragment at an early processing step is indicated generally byreference numeral 100. Thesemiconductor wafer 100 includes abulk silicon substrate 112 with fieldisolation oxide regions 114 andactive areas Word lines wafer 100 in a conventional manner. Each word line consists of alower gate oxide 130, alower poly layer 132, a higherconductivity silicide layer 134 and an insulatingsilicon nitride cap 136. Each word line has also been provided with insulatingspacers 138, also of silicon nitride. - Two FETs are depicted in
FIG. 5 . One FET is comprised of two active areas (source/drain) 116, 118 and one word line (gate) 124. The second FET is comprised of two active areas (source/drain) 118, 120 and a second word line (gate) 126. Theactive area 118 common to both FETs is the active area over which a bit line contact will be formed. - Referring to
FIG. 6 , athin film 140 of nitride or TEOS is provided atop thewafer 100. Next a layer of insulatingmaterial 142 is deposited. The insulating material preferably consists of borophosphosilicate glass (BPSG). The insulatinglayer 142 is subsequently planarized by chemical-mechanical polishing (CMP). - Referring to
FIG. 7 , a bitline contact opening 144 andcapacitor openings 146 have been formed through the insulatinglayer 142. Theopenings layer 142 by photomasking and dry chemical etching the BPSG relative to the thin nitride orTEOS layer 140. Referring now toFIG. 8 , alayer 150 of conductive material is deposited to provide conductive material within the bitline contact opening 144 andcapacitor openings 146. Theconductive layer 150 is in contact with theactive areas layer 150 is in situ arsenic or phosphorous doped poly. Referring now toFIG. 9 , theconductive layer 150 is etched away to the point that the only remaining material forms plugs 150 over theactive areas - Referring now to
FIG. 10 , athin barrier layer 151 is formed as a barrier layer atopconductive layer 150.Barrier layer 151 can be of a variety of conventional barrier materials in a conformal layer which protects the subsequently deposited capacitor dielectric against diffusion fromunderlying plug 150 and other surrounding materials. Perhaps more importantly for some applications of the invention,barrier layer 151 also protects theunderlying plug 150 from diffusion of oxygen from the capacitor dielectric. Such conformal layers are typically deposited using chemical vapor deposition techniques. - Following deposition of
barrier layer 151, alayer 152 of a conductive zirconium-platinum material (or other conventional electrode material if desired) that will eventually form one of the electrodes of the capacitor is deposited at a thickness such that thecapacitor openings 146 are not closed off. Referring toFIG. 11 , theconductive layer 152 is in electrical contact with the previously formed plugs 150. - Referring to
FIG. 12 , the portion of theconductive layer 152 above the top of theBPSG layer 142 is removed through a planarization process, thereby electrically isolating the portions oflayer 152 remaining in the bitline contact opening 144 andcapacitor openings 146. Referring now toFIG. 13 , acapacitor dielectric layer 154 is provided overconductive layer 152 andcapacitor openings 146. -
Dielectric layer 154 is deposited with a thickness such that theopenings 146 are again not completely filled.Dielectric layer 154 may comprise tantalum pentoxide (Ta2O5). Other suitable dielectric materials such as Strontium Titanate (ST), Barium Strontium Titanate (BST), Lead Zirconium Titanate (PZT), Strontium Bismuth Tantalate (SBT) and Bismuth Zirconium Titanate (BZT) may also be used.Dielectric layer 154 may be deposited by a low-pressure CVD process using Ta(OC2H5)5 and O2 at about 430° C., and may be subsequently annealed in order to reduce leakage current characteristics. - A second
conductive electrode layer 156 is then deposited by CVD over thedielectric layer 154, again at a thickness which less than completely fills thecapacitor openings 146. The secondconductive layer 156 includes a platinum-zirconium material (or other conventional electrode materials if desired). In addition to serving as the top electrode or second plate of the capacitor, the secondconductive layer 156 also forms the interconnection lines between the second plates of all capacitors. - Referring to
FIG. 14 , the secondconductive layer 156 and underlyingcapacitor dielectric layer 154 are patterned and etched such that the remaining portions of each group of the firstconductive layer 152,capacitor dielectric layer 154, and secondconductive layer 156 over the bitline contact opening 144 andcapacitor openings 146 are electrically isolated from each other. In this manner, each of theactive areas barrier layer 151 and the firstconductive layer 152 in contact with theplug 150 over the bit lineactive area 118 are outwardly exposed. - Referring now to
FIG. 15 , a bitline insulating layer 158 is provided over the secondconductive layer 156. The bit line insulatinglayer 158 is preferably comprised of BPSG. The BPSG is typically reflowed by conventional techniques, i.e., heating to about 800° C. Other insulating layers such as PSG, or other compositions of doped SiO2 may similarly be employed as the insulatinglayer 158. - A bit
line contact opening 160 is patterned through the bitline insulating layer 158 such that thebarrier layer 151 aboveconductive plug 150 is once again outwardly exposed. Then a bit line contact material is provided in the bitline contact opening 160 such that the bit line contact material is in electrical contact with the outwardly exposed portion of thebarrier layer 151 aboveconductive plug 150. Thus, theplug 150 over theactive area 118 common to both FETs acts as a bit line contact. The DRAM array and associated circuitry may then be completed by a variety of well established techniques, such as metalization, and attachment to peripheral circuitry. - The platinum-zirconium electrode materials according to the invention have excellent conductivity and therefor reduce depletion effects and enhance frequency response. In addition, the use of the platinum and zirconium precursor compositions and methods of forming co-deposited platinum-zirconium layers of the present invention are beneficial for a wide variety of thin film applications in integrated circuit structures, particularly those using high dielectric materials. For example, such applications include capacitors such as planar cells, trench cells (e.g., double sidewall trench capacitors), stacked cells (e.g., crown, V-cell, delta cell, multi-fingered, or cylindrical container stacked capacitors).
- The advantages of co-depositing Zr with Pt for electrode layers, for example, will now be discussed with references to
FIGS. 16-19 in the Examples below. - The following examples are offered to further illustrate the various specific and preferred embodiments and techniques. It should be understood, however, that many variations and modifications may be made while remaining within the scope of the present invention.
- A substrate of silicon that had been thermally oxidized was placed into a CVD chamber and heated to 350° C. A bubbler containing MeCpPt(Me)3, purchased from Technical Glass, was connected such that carrier gas would pass through the liquid precursor and take vapor of the compound into the chamber. The bubbler was heated to 33° C. and the lines connecting the bubbler to the chamber were heated to 50° C. to prevent condensation. A second bubbler containing Zr(OC(CH3)3)4, purchased from Technical Glass, was connected such that carrier gas would pass through the liquid precursor and take vapor of the compound into the chamber. The bubbler was heated to 48° C. and the lines connecting the bubbler to the chamber were heated to 60° C. to prevent condensation. Using a carrier gas flow of 30 sccm He for the platinum precursor and 10 sccm He for the zirconium precursor, and a reaction gas flow of 50 sccm N2O, with a platinum precursor bubbler pressure of about 5 torr and temperature of 33° C. and an zirconium precursor bubbler pressure of about 5 torr and temperature of 48° C., and a chamber pressure of 3 torr and deposition temperature of 350° C. at the wafer surface, a film was deposited for 6.5 minutes. A small lab scale reaction CVD chamber was built by MDC Vaccuum Products Corp. (Hayward, Calif.) and the glass research bubbler is from Technical Glass Service (Boise, Id.).
- A depth profile was attained by using an Auger spectrometer available under the trade designation of PhI (Φ) 670 from Physical Electronics (Eden Prairie, MN). The operating conditions for obtaining the profile include electron source of 10 keV. Sputtering was performed with a 4 keV Argon ion beam rastored over a 2×2 mm area. The sputter time for the depth profile of
FIG. 16 was 2.5 minutes. -
FIG. 16 shows an Auger depth profile of a Pt—ZrO2 film, produced by CVD co-deposition of Pt and Zr between a layer of Pt and SiO2. The zirconium concentration in the platinum-zirconium layer is about 15 atom percent. -
FIG. 17 is a scanning electron micrograph of a Pt—ZrO2 film deposited by CVD under the conditions listed above.FIG. 18 is a scanning electron micrograph of a cross-section of a Pt—ZrO2 film deposited by CVD under the conditions described above after annealing in oxygen at 700° C. for 60 seconds.FIG. 19 is a scanning electron micrograph of a Pt—ZrO2 film deposited by CVD after annealing in oxygen at 700° C. for 60 seconds. The sheet resistance of the film shown inFIG. 19 was 2.0 ohm/square, corresponding to a resistivity of about 10 microohms-centimeter. - The zirconia-stabilized platinum film shows no signs of island formation. Thus, zirconium serves to mechanically stabilize platinum films against migration during annealing without substantially degrading the conductivity of the film.
- The foregoing detailed description and examples have been given for clarity of understanding only. No unnecessary limitations are to be understood therefrom. The invention is not limited to the exact details shown and described, for variations obvious to one skilled in the art will be included within the invention defined by the claims. The complete disclosures of all patents, patent documents, and publications listed herein are incorporated by reference, as if each were individually incorporated by reference.
Claims (11)
1-37. (canceled)
38. A method of manufacturing a catalyst, the method comprising:
providing a substrate;
providing a precursor composition comprising one or more zirconium complexes;
providing a precursor composition comprising one or more platinum complexes; and
forming a platinum-zirconium-containing material from the precursor compositions on a surface of the substrate to form a catalyst.
39. The method of claim 38 wherein forming a platinum-zirconium-containing material occurs in the presence of an oxidizing gas.
40. A catalyst comprising a platinum-zirconium-containing material.
41. The catalyst of claim 40 wherein the platinum-zirconium-containing material comprises a roughened surface.
42. The catalyst of claim 41 wherein the roughened surface comprises a plurality of columnar pedestals.
43. The catalyst of claim 42 wherein the columnar pedestals are at least about 400 Angstroms tall.
44. A method of stabilizing a platinum film upon annealing the film at a temperature of at least about 650° C., the method comprising incorporating zirconium into the platinum film.
45. The method of claim 44 wherein the zirconium is at least partially oxidized.
46. The method of claim 44 wherein there are substantially no signs of island formation after annealing the platinum-zirconium film at a temperature of at least about 650° C.
47. The method of claim 44 wherein the zirconium incorporation does not substantially degrade the conductivity of the platinum film.