US20010001669A1

US20010001669A1 - Compound delivery using rapidly dissolving collagen film

Info

Publication number: US20010001669A1
Application number: US09/735,182
Authority: US
Inventors: Dale DeVore; Richard Eiferman; Edwin Keates
Original assignee: Devore Dale P.; Eiferman Richard A.; Keates Edwin U.
Current assignee: Euclid Systems Corp
Priority date: 1998-05-22
Filing date: 2000-12-12
Publication date: 2001-05-24
Anticipated expiration: 2018-05-22
Also published as: JP2002516289A; US6448378B2; WO1999061047A1; US6197934B1; EP1079850A1; EP1079850A4

Abstract

Disclosed herein are collagen films which rapidly dissolve at 35° C. Also disclosed are methods for the preparation of the collagen films and their use as a vehicle for delivering a dose of therapeutic compound to a specific tissue site.

Description

BACKGROUND OF THE INVENTION

In general, the invention relates to rapidly dissolving collagen films, methods of preparation, and the use of these films for rapid compound delivery.

The ability to specifically deliver a compound to a particular site in the human body is a desirable goal in many areas of medicine. For example, in cancer therapy, administration of chemotherapeutic agents to a tumor site with minimal exposure to surrounding tissues would dramatically reduce undesirable side effects to the surrounding tissues, or the body as a whole, while facilitating delivery of potent doses to malignant cells.

In addition, the inhibition of wound healing is beneficial in certain circumstances, for example, following glaucoma filtration surgery (otherwise known as trabeculectomy). The initial stage in the process of wound healing is characterized by the movement of intravascular components, such as plasma and blood proteins, to the extravascular area (Peacock, In: Wound Repair, 491-492, 1984, ed. EE Peacock, WB Saunders Co, Philadelphia, Pa.). Neutrophils and macrophages then migrate to the injury site, functioning to prevent infection and promote fibroblast migration. Subsequent phases of wound healing include fibroblast secretion of collagen, collagen stabilization, angiogenesis, and wound closure (Costa et al., Opth. Surgery 24: 152-170, 1993).

During surgery for the treatment of glaucoma, a fistula is frequently created to allow for post-operative drainage of intraopthalmic fluid from the eye. Accordingly, the inhibition of fistula healing is beneficial in order to extend the drainage time and reduce intraopthalmic pressure. Several therapies have been adopted to inhibit fistula healing, including beta irradiation, 5-fluorouracil treatment, and mitomycin (also known as mitomycin-C or mitomicin) treatment (Costa et al., Opth. Surgery 24: 152-170, 1993).

SUMMARY OF THE INVENTION

The present invention provides a method of preparing a rapidly dissolving collagen film which includes a therapeutic compound. The method involves (i) preparing a purified solution of monoreactive-amine modified collagen, e.g., a glutaric anhydride derivatized collagen, (ii) heating the collagen solution to about 35-45° C. for a time sufficient to reduce collagen viscosity, (iii) adding the compound to the heated collagen solution, and iv) casting the solution into thin layers, wherein the solution dries and forms the film.

The invention also includes a collagen film prepared by the above described method and a collagen film which rapidly dissolves upon exposure to about 35° C. Preferably, the collagen film dissolves within five to ten minutes upon exposure to about 35° C. More preferably, the collagen film dissolves within two minutes upon exposure to about 35° C. . Most preferably, the collagen film dissolves within one minute or 30 seconds upon exposure to about 35° C.

The therapeutic compound contained within the rapidly dissolving collagen film may be an inhibitor of cell proliferation, e.g., an anti-metabolic antibiotic, anti-metabolite, anti-fibrotic, anti-viral compound, or angiostatic compound. Preferably, the compound is an anti-metabolic antibiotic, e.g., mitomycin, daunorubicin, mithramycin, bleomycin, or doxorubicin.

Alternatively, the therapeutic compound may be an anti-metabolite. Examples of useful anti-metabolites include 5-fluorouracil, 5-fluorouridine-5′-monophosphate, 5-fluorodeoxyuridine, 5-fluorodeoxyuridine-5′-monophosphate, and 5-fluroorotate.

In yet other applications, the therapeutic compound contained within the rapidly dissolving collagen film is an anti-fibrotic. Examples of useful anti-fibrotics include inhibitors of prolyl nydroxylase and lysyl hydroxylase, e.g., iron chelators, α,α-dipyridyl, o-phenanthroline, proline analogs, lysine analogs, and free radical inhibitors and scavengers; inhibitors of collagen secretion, e.g., colchicine, vinblastin, cytochalasin B, copper, zinc, and EGTA; inhibitors of collagen secretion and maturation, e.g., BAPN, vincristine, and D-penicillamine; and stimulators of collagen degradation, e.g., EDTA and colchicine.

As noted above, the therapeutic compound may also be an anti-viral drug. Examples of anti-viral drugs that can be used in the invention include vidarabine, acyclovir, AZT, and amantadine.

Finally, angiostatic drugs, e.g., angiostatin, as well as other miscellaneous anti-cell proliferative drugs, e.g., tissue plasminogen activator (TPA), heparin, cytosine arabinoside, and gamma-interferon, may also be used in the rapidly dissolving collagen films described herein.

In addition to methods of collagen film preparation, the invention also provides a method of rapidly delivering a compound dose to a specific tissue site in a mammal. The method involves administering a collagen film containing the compound dose to the tissue site, wherein the collagen film rapidly dissolves upon exposure to the mammalian tissue site. Using this method to deliver toxic compounds, the toxic side effects are essentially restricted to the specific tissue site of compound delivery.

In a related aspect, the invention also includes a method of treating a mammal to inhibit cellular proliferation, e.g., wound healing or tumor growth, at a specific tissue site. The method involves administering a collagen film comprising an inhibitor of cell proliferation, e.g., an anti-metabolic antibiotic, anti-metabolite, anti-fibrotic, anti-viral compound, or angiostatic compound, to the tissue site, wherein the collagen film rapidly dissolves upon exposure to the tissue and delivers a dose of the compound sufficient to inhibit cell proliferation at the tissue site.

In preferred embodiments, the cell proliferation inhibitor is mitomycin, 5-fluorouracil, or an anti-fibrotic. In addition, in other preferred embodiments, the collagen film dissolves within five to ten minutes upon exposure to the mammalian tissue site, more preferably, within two minutes, and, most preferably, within one minute or 30 seconds. In addition, the mammal is preferably a human.

This method can be used, for example, in treating a mammal undergoing surgery for glaucoma. In this application, the collagen film is administered to the trabeculectomy-created fistula in the mammal, wherein the dose of cell proliferation inhibitor is sufficient to inhibit closure of the fistula. Preferably, the cell proliferation inhibitor used is mitomycin at a dose of 200-400 μg and may be administered in a 4×4 mm collagen film patch. Most preferably, the mitomycin dose is 400 μg.

Use of this treatment results in reduced post-operative intraocular pressure. Preferably, post-operative intraocular pressure as a result of this method is less than 16 mmHg, more preferably, less than 12 mmHg, and, most preferably, less than 6 mmHg.

As used herein, by “mono-reactive amine-modified” is meant reacted with a monoreactive amine-modifying agent, also known as a monoacylating or sulfonating agent. Useful agents include, without limitation, anhydrides, acid halides, sulfonyl halides, and active esters. The modifying agent is preferably a compound or combination of compounds which contains an acidic, carboxylic, or sulfonide group, or generates an acidic, carboxylic, or sulfonic group during reaction.

By “inhibitor of cell proliferation” is meant an inhibitor of an increase in the number of cells located at a particular site. Such inhibition may occur by inhibition of cell migration or attachment, cell replication, cell survival, or angiogenesis.

By “specific tissue site” is meant the area of tissue directly in contact with the collagen film administered to the tissue.

By “rapidly dissolves” is meant dissolves, or melts, in approximately 30 minutes or less.

The present invention provides a number of advantages. For example, the present techniques and collagen film compositions facilitate an improved approach for delivering a compound in situations where both a precise dose and accurate placement are required. The dose can be adjusted to any desired amount, i.e., by modifying the concentration of compound in the film or the size of the film, and the solid nature of the film allows its placement at any site in the body which can be reached by surgical techniques. In addition, the invention provides for the rapid dissolution of the collagen film upon exposure to normal body temperature. Taken together, these features ensure that a delivered compound achieves a certain concentration at a specific site, reducing possible inaccuracy due to mistaken dose or improper placement.

For delivery of mitomycin or 5-fluorouracil to a post-trabeculectomy fistula, the present invention represents an improvement over current empirical techniques employed, which typically involve placing a sponge wetted with compound on the fistula site for 3-5 minutes.

The advantage of delivering essentially all compound to a specific site also provides for limited compound delivery to tissues surrounding the delivery site. This advantage is especially relevant when the compound to be delivered has toxic effects. By restricting delivery to the targeted tissues, any unintentional or unnecessary toxic damage to surrounding tissues is reduced.

Furthermore, compounds, such as mitomycin, exhibit increased stability in the collagen film as compared to stability in solution. Thus, one collagen film sample preparation can be subdivided and used for several applications over the course of several weeks. This feature provides the advantages of reducing experimental variation when administered over several days and eliminating the need for daily pre-surgical sample preparation.

Other features and advantages of the invention will be apparent from the following detailed description thereof, and from the claims.

DETAILED DESCRIPTION OF THE INVENTION

Described herein are methods of preparing collagen films containing therapeutic compounds that readily dissolve upon exposure to normal human body temperature (35-37° C.). These collagen films can be used for the rapid and accurate delivery of compounds to specific tissue sites. [0026]
For the purposes of this invention, collagen can be collected, solubilized, subjected to modification by mono-reactive, amine-modifying agents, and re-precipitated by any standard technique, e.g., those provided in DeVore et al. (U.S. Pat. No. 4,713,446), herein incorporated by reference. The following example is provided as an illustration and is in no way intended to limit the scope of the invention. [0027]
Preparation of Collagen [0028]
As a first step toward producing rapidly dissolving films, soluble collagen was prepared by standard procedures. Young calf hide was washed thoroughly with reagent alcohol and with deionized, pyrogen-free water, cut into approximately 1 cm[0029] ²sections, and stirred overnight in 40 volumes of 0.5 M acetic acid. The mixture was then supplemented with pepsin (3% hide wet weight) and stirred for 72 hours. The digested, solubilized collagen was filtered through cheesecloth and precipitated by increasing the NaCl concentration to 0.8 M. The collagen was then cycled twice through steps of redissolution, in 0.5 M acetic acid, and reprecipitated. The collagen precipitate was then redissolved in 0.1 N acetic acid, dialyzed against 0.1 M acetic acid, filtered (0.45 μm), and refiltered (0.22 μm).
The purified, telopeptide-poor collagen was derivatized with glutaric anhydride as previously described (U.S. Pat. Nos. 5,631,243 and 5,492,135). Briefly, the collagen solution (approximately 3 mg/ml) was adjusted to pH 9.0 with 10 N and 1 N NaOH. While stirring the solution, glutaric anhydride was added at 10% (weight of collagen). For twenty minutes, the stirring continued, and the pH was maintained. [0030]
The pH of the solution was adjusted to 4.3 with 6 N and 1 N HCl to precipitate the derivatized collagen. The precipitate was centrifuged at 3500 rpm for 30 minutes. The pellet was washed three times in pyrogen-free deionized water and then redissolved in phosphate buffered glycerol (2% glycerol in 0.004 M phosphate buffer, pH 7.4) to achieve a final concentration of approximately 10 mg/ml. [0031]
Preparation of Collagen Films Containing Mitomycin [0032]
To prepare collagen films containing mitomycin, the collagen solution, described above, was heated in a 35° C. water bath for 30 minutes to reduce viscosity. Mitomycin (e.g., Mutamycin®, Bristol Myers Squibb, Princeton, N.J.), also known as mitomicin C, was added to the heated collagen. The collagen solution was then poured into petri dishes in a thin layer and allowed to air dry under a laminar-flow hood. [0033]
Collagen film melting time at 35° C. was measured after placing the films in 0.8% saline in a 35° C. water bath. Pre-heated collagen films melted in approximately one minute. In contrast, collagen films poured into petri dishes without pre-heating melted at 35° C. in approximately 30 minutes. [0034]
Mitomycin-containing collagen films had a final mitomycin concentration of 400 μg per 16 mm[0035] ². 6 mm diameter discs were cut from the film and applied to human subconjunctival fibroblasts derived from Tenon's membrane layered in 96 well plates (CSM supplemented with 10% fetal bovine serum). After 72 hours, mitomycin-induced inhibition of cell division was assessed by measuring the reduction in fluorescence intensity (RFU) using a fluorogenic CalceinAM assay (see, for example, Decherchi et al., J. Neurosci. Meth. 71: 205 (1997); Sugita, Pflitgers Arch. 429: 555 (1995); Padanilam et al., Ann. NY Acad. Sci. 720: 111 (1994); Lichtenfels et al., J. Immunol. Meth. 172: 227 (1994); and Wang et al., Human Immunol. 37: 264 (1993)). The mitomycin-containing collagen films inhibited approximately 91% of the cell division demonstrated in control cells.
Mitomycin-containing films may be stored for later use. For example, mitomycin activity in the collagen films described above was maintained for at least 6 weeks after preparation of the films (stored at 4° C.). Administration of mitomycin-collagen films, 2, 4, and 6 weeks old, demonstrated 91%, 90%, and 92% inhibition of cell division, respectively, compared to mitomycin-free controls. These values were comparable to the % cell death inhibition elicited by administration of a freshly prepared mitomycin solution (0.4 mg/ml solution, dissolved in USP sterile water). [0036]
In contrast to the stability of mitomycin in the collagen film, HPLC analysis of the mitomycin solution determined that stability was maintained for only 4 days following storage at ambient temperature and 4° C. in the dark. Dissolution and storage in 0.9% saline or phosphate buffer (pH 7.4) is not recommended due to degradation and precipitation. [0037]
Use [0038]
Rapidly dissolving collagen films containing therapeutic compounds are useful for various treatments. For example, the collagen-mitomycin film may be administered to the external opening of the fistula created during glaucoma filtering surgery (trabeculectomy). Immediately following surgery, a collagen film, e.g., a 4×4 mm patch, containing 100-1000 μg mitomycin (preferably 400 μg), is directly applied to the external opening of the fistula prior to replacing the scleral flap. Administration of the mitomycin increases the duration of fistula patency, increasing filtration from the eye and reducing intraocular pressure. [0039]
Other compounds may also be administered to the trabeculectomy-created fistula to increase filtration during recovery. For example, 5-fluorouracil-containing films may be administered in the same fashion to deliver a 5-fluorouracil dose of 25-250 μg (preferably 100 μg). Other alternative compounds that are effective for this treatment are anti-fibrotic, angiostatic, and anti-viral compounds. [0040]
Administration of the rapidly dissolving collagen films containing inhibitors of cell proliferation are also useful for treatment during recovery from other surgical procedures where prevention of wound healing is beneficial. [0041]
In addition, the collagen films of the invention may be administered to reduce cellular proliferation in specific tissue sites, such as for the localized inhibition of neoplastic or non-neoplastic cell growth. For this application, any chemotherapeutic compound may be dissolved in the collagen matrix in concentrations appropriate for inhibiting cell growth. [0042]

OTHER EMBODIMENTS

While the treatment regimens described herein are preferably applied to human patients, they also find use in the treatment of other animals, such as domestic pets or livestock. [0043]
Moreover, while the invention has been described in connection with specific embodiments thereof, it will be understood that it is capable of further modifications and this application is intended to cover any variations, uses, or adaptations of the invention following, in general, the principles of the invention and including such departures from the present disclosure come within known or customary practice within the art to which the invention pertains and may be applied to the essential features hereinbefore set forth, and follows in the scope of the appended claims. [0044]

Claims

What is claimed is:

1. A method of preparing a rapidly dissolving collagen film which includes a therapeutic compound, said method comprising:

a) preparing a purified solution of monoreactive-amine modified collagen;

b) heating said collagen solution to about 35-45° C. for a time sufficient to reduce collagen viscosity;

c) adding said compound to the heated collagen solution; and

d) casting said solution into thin layers, wherein said solution dries and forms said film.

2. The method of

claim 1

, wherein said collagen is modified by glutaric anhydride derivatization.

3. A collagen film prepared by the method of

claim 1

.

4. A collagen film, wherein said film rapidly dissolves upon exposure to about 35° C.

5. The collagen film of

claim 4

, wherein said collagen film dissolves within ten minutes upon exposure to about 35° C.

6. The collagen film of

claim 4

, wherein said collagen film dissolves within five minutes upon exposure to about 35° C.

7. The collagen film of

claim 4

, wherein said collagen film dissolves within two minutes upon exposure to about 35° C.

8. The collagen film of

claim 4

, wherein said collagen film dissolves within one minute upon exposure to about 35° C.

9. The collagen film of

claim 4

, wherein said collagen film dissolves within thirty seconds upon exposure to about 35° C.

10. The collagen film of

claim 4

, wherein said film includes a compound which is an inhibitor of cell proliferation.

11. The collagen film of

claim 10

, wherein said compound is an anti-metabolic antibiotic.

12. The collagen film of

claim 11

, wherein said compound is mitomycin.

13. The collagen film of

claim 4

, wherein said film includes a compound which is an anti-metabolite.

14. The collagen film of

claim 13

, wherein said compound is 5-fluorouracil.

15. The collagen film of

claim 4

, wherein said film includes a compound which is an anti-fibrotic.