CA2427431A1 - Pmma moulding compositions with improved low-temperature impact resistance - Google Patents
Pmma moulding compositions with improved low-temperature impact resistance Download PDFInfo
- Publication number
- CA2427431A1 CA2427431A1 CA002427431A CA2427431A CA2427431A1 CA 2427431 A1 CA2427431 A1 CA 2427431A1 CA 002427431 A CA002427431 A CA 002427431A CA 2427431 A CA2427431 A CA 2427431A CA 2427431 A1 CA2427431 A1 CA 2427431A1
- Authority
- CA
- Canada
- Prior art keywords
- weight
- cndot
- impact
- pmma
- moulding composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a molding material, which is provided with impact resistance and which is characterized by exhibiting a particularly high impact resistance at low temperatures (-20 ~C, -40 ~C). This low-temperature impact resistance is achieved by using a silicon elastomer.
Claims (11)
1. Impact-resistant PMMA moulding composition com-posed of a) a matrix of .cndot. from 75 to 100% by weight of methyl meth-acrylate .cndot. from 0.1 to 15% by weight of acrylate and .cndot. from 0 to 15% by weight of other copolymer-izable compounds and b) another matrix of .cndot. from 70 to 92% by weight of styrene .cndot. from 8 to 30% by weight of acrylonitrile .cndot. from 0 to 22% by weight of other comonomers c) an impact modifier of silicone elastomer parti-cles with PMMA shell and d) an impact modifier based on acrylate rubber, where the contents of c) are from 5 to 95% by weight and of d) are from 95 to 5% by weight, based on the entirety of components c) and d), and where, based on the entirety a), b), c) and d), from 0 to 45% by weight of component b), from 5 to 30% by weight of component c), and from 1 to 30% by weight of component d) are added, and the moulding composition has the following properties:
.cndot. a Vicat softening point to ISO 306 (B50) of at least 95°C, .cndot. a notched impact strength NIS (Izod 180/leA, 1.8 MPa) to ISO 180 of at least 3.0 kJ/m2 at -20°C and of at least
.cndot. a Vicat softening point to ISO 306 (B50) of at least 95°C, .cndot. a notched impact strength NIS (Izod 180/leA, 1.8 MPa) to ISO 180 of at least 3.0 kJ/m2 at -20°C and of at least
2.5 kJ/m2 at -40°C, .cndot. a modulus of elasticity to ISO 527-2 of at least 2000 MPa.
2. Impact-resistant PMMA moulding composition accord-ing to Claim 1, characterized in that the matrix has an average molecular weight (weight average) from 90,000 to 250,000 daltons.
2. Impact-resistant PMMA moulding composition accord-ing to Claim 1, characterized in that the matrix has an average molecular weight (weight average) from 90,000 to 250,000 daltons.
3. Impact-resistant PMMA moulding composition accord-ing to Claim 1, characterized in that the impact-modifier c) has a silicone content of up to 95% by weight.
4. Impact-resistant PMMA moulding composition accord-ing to Claim 1, characterized in that]
the PMMA shell of the impact modifier c) is composed of the polymer of from 30 to 100% by weight of methyl methacrylate and from 0 to 30% by weight of other copolymerizable compounds.
the PMMA shell of the impact modifier c) is composed of the polymer of from 30 to 100% by weight of methyl methacrylate and from 0 to 30% by weight of other copolymerizable compounds.
5. Impact-resistant PMMA moulding composition accord-ing to Claim 1, characterized in that the primary particle size of the impact modifier c) is a diameter of from 10 to 300 nm and the distribution of the primary particle sizes is monomodal (polydispersity index not more than 0.2).
6. Impact-resistant PMMA moulding composition according to Claim 1, characterized in that the impact modifier d) is composed either .cndot. of core-shell particles (core composed of acryl-ate rubber, particle size from 100 to 1000 nm), or of core-shell-shell (C/S1/S2) particles (S1 com-posed of acrylate rubber, particle size from 100 to 1000 nm), or .cndot. of finely divided acrylate rubber in PMMA beads (particle size from 100 to 500 µm).
7. Use of the moulding composition according to any of the preceding claims for producing mouldings by injection moulding or extrusion, which even at temperatures extending to -40°C have a notched impact strength NIS (Izod 180/1eA, 1.8 MPa) to ISO
180 of at least 2.5 kJ/m2.
180 of at least 2.5 kJ/m2.
8. Use of the mouldings according to Claim 7 in applications with periods of exposure to temperatures below -10°C.
9. Use of the mouldings according to Claim 8 characterized in that the moulding is a mirror housing for a vehicle, or is a spoiler.
10. Use of the mouldings according to Claim 8 characterized in that the moulding is a tube or a protective covering.
11. Use of the mouldings according to Claim 8 characterized in that the moulding is a refrigerator component.